Process for the production of a basic carbonate of aluminum and an alkali or alkali earth metal
Assignee: Rio Tinto Switzerland AG
•
Filing: 1978-02-01
•
Granted: 1980-12-09
•
Expires: 1998-02-01
Abstract
Abstract The process of the present invention resides in the production of an extremely pure basic aluminum-sodium carbonate of the dawsonite type. In the process of the present invention, aluminum hydroxide is reacted with an aqueous sodium bi-carbonate solution at a temperature between 160 DEG and 240 DEG C. and at a pressure of 5-50 atm. The reagents from an aqueous suspension which is stirred throughout the duration of the reaction and the temperature of the reaction is chosen in accordance with the length of crystalline fiber which is to be produced.
Inventors
- 👤 Chanakya Misra
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:00
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/18; C01; C01F; C01F7/00; C01F7/78; C01F7/782; G; G03; G03C; G03C1/00; G03C1/76; G03C1/775; C01P; C01P2004/00; C01P2004/10
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
91 words
A process for the production of a basic pure aluminum-sodium carbonate of the dawsonite type by reacting aluminum tri-hydroxide obtained from the Bayer process with an aqueous sodium bi-carbonate solution wherein the conversion to dawsonite is in the order of 98.5 to 99.5% comprising carrying out the reaction at a temperature between 160° and 240° C. and under a pressure of between 5 and 50 atm. in an aqueous suspension which is agitated by stirring whereby the length of the crystalline fibers increase with a corresponding increase in the reaction temperature.
Claim 2
Dependent Claim
91 words
A process for the production of a basic pure aluminum-sodium carbonate of the dawsonite type by reacting aluminum tri-hydroxide obtained from the Bayer process with an aqueous sodium bi-carbonate solution wherein the conversion to dawsonite is in the order of 98.5 to 99.5% comprising carrying out the reaction at a temperature between 160° and 240° C. and under a pressure of between 5 and 50 atm. in an aqueous suspension which is agitated by stirring whereby the length of the crystalline fibers increase with a corresponding increase in the reaction temperature.
Claim 3
Dependent Claim
18 words
A process according to claim 1 wherein a sodium carbonate solution containing 40-250 g/l NaHCO 3 is employed.
Claim 4
Dependent Claim
25 words
A process according to claim 1 wherein a suspension containing a molar ratio of reagents (Na 2 O/Al 2 O 3 )of 2-6 is employed.
Claim 5
Dependent Claim
15 words
A process according to claim 1 wherein the duration of the reaction is 20-40 minutes.
Claim 6
Dependent Claim
15 words
A process according to claim 4 wherein the duration of the reaction is 20-180 minutes.
Claim 7
Dependent Claim
22 words
A process according to claim 1 wherein before the start of the reaction, dawsonite seed crystals are added to the aqueous suspension.
Claim 8
Dependent Claim
23 words
A process according to claim 6 wherein the quantity of seed crystals is between 5 and 50 wt. % of the resultant product.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-09 | 1984-06-09 | 1984-12-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-09 | 1988-06-09 | 1988-12-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-09 | 1992-06-09 | 1992-12-09 | $7700.00 | Window Closed / Lapsed |