Patent US4238316A successfully refreshed from Google Patents.
US4238316A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Two-stage catalytic process to produce lubricating oils
Assignee: Atlantic Richfield Co
•
Filing: 1978-07-06
•
Granted: 1980-12-09
•
Expires: 1998-07-06
Abstract
Abstract A high viscosity index mineral lubricating oil is produced by processing a heavy hydrocarbon feedstock, e.g., a deasphalted residiuum in two (2) catalytic steps. The feedstock is first catalytically hydrocracked, hydrotreated then catalytically hydrogenated and can be fractionated and dewaxed to provide a finished product. Improved step (1) catalysts comprise at least one Group VIB metal, Group VIII metal and mixtures thereof on a support involving both silica-alumina and alumina.
Inventors
- 👤 John Mooi
- 👤 James P. Gallagher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 22:33
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/70; B01J23/76; B01J23/84; B01J23/85; C; C10; C10G; C10G2400/00; C10G2400/10
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
298 words
A process for preparing a mineral hydrocarbon lubricating oil having an increased viscosity index, on a dewaxed basis, which comprises 1) contacting a mineral hydrocarbon oil feedstock of lubricating viscosity, at least about 90% by weight of which boils above about 600° F. and having a viscosity index of about 50 to about 85, with molecular hydrogen at hydrocarbon hydrocracking conditions in the presence of a catalyst which is boria-free and comprises a major amount of a catalytically active support derived by the calcination of a material comprising about 30% to about 70% by weight of silica and about 30% to about 70% by weight of alumina, based on the total silica and alumina in said support, said silica and alumina being supplied by a mixture comprising about 40% to about 90% by weight of amorphous silica-alumina and about 10% to about 60% by weight of alumina derived from hydrous alumina selected from the group consisting of boehmite, and mixtures thereof with amorphous hydrous alumina, and a minor, catalytically effective amount of each of at least one metal selected from the group consisting of Group VIb metals and at least one metal selected from the group consisting of Group VIII metals; and (2) contacting hydrocarbon oil of lubricating viscosity from step (1) with molecular hydrogen under hydrocarbon hydrogenation conditions in the presence of a solid hydrogenation catalyst at a hydrotreating severity such that not more than about 5 volume percent of the hydrocarbon feed to step (2) boiling above about 600° F. is cracked to material boiling below about 600° F. to produce oil of lubricating viscosity having a viscosity index of at least about 90 and at least about 20 viscosity index numbers greater than the hydrocarbon oil feedstock contacted in step (1), on a dewaxed basis.
Claim 2
Dependent Claim
298 words
A process for preparing a mineral hydrocarbon lubricating oil having an increased viscosity index, on a dewaxed basis, which comprises 1) contacting a mineral hydrocarbon oil feedstock of lubricating viscosity, at least about 90% by weight of which boils above about 600° F. and having a viscosity index of about 50 to about 85, with molecular hydrogen at hydrocarbon hydrocracking conditions in the presence of a catalyst which is boria-free and comprises a major amount of a catalytically active support derived by the calcination of a material comprising about 30% to about 70% by weight of silica and about 30% to about 70% by weight of alumina, based on the total silica and alumina in said support, said silica and alumina being supplied by a mixture comprising about 40% to about 90% by weight of amorphous silica-alumina and about 10% to about 60% by weight of alumina derived from hydrous alumina selected from the group consisting of boehmite, and mixtures thereof with amorphous hydrous alumina, and a minor, catalytically effective amount of each of at least one metal selected from the group consisting of Group VIb metals and at least one metal selected from the group consisting of Group VIII metals; and (2) contacting hydrocarbon oil of lubricating viscosity from step (1) with molecular hydrogen under hydrocarbon hydrogenation conditions in the presence of a solid hydrogenation catalyst at a hydrotreating severity such that not more than about 5 volume percent of the hydrocarbon feed to step (2) boiling above about 600° F. is cracked to material boiling below about 600° F. to produce oil of lubricating viscosity having a viscosity index of at least about 90 and at least about 20 viscosity index numbers greater than the hydrocarbon oil feedstock contacted in step (1), on a dewaxed basis.
Claim 3
Dependent Claim
30 words
The process of claim 1 wherein said amorphous silica alumina contains about 40% to about 92% by weight of silica and about 8% to about 60% by weight of alumina.
Claim 4
Dependent Claim
120 words
The process of claim 2 wherein the Group VIb metal is present in the step (1) catalyst in an amount of about 5% to about 40% by weight of the total calalyst, calculated as the Group VIb metal oxide and the Group VIII metal in said step (1) catalyst is selected from the group consisting of an iron group metal, a platinum group metal and mixtures thereof, said iron group metal being present in an amount of about 2% to about 15% by weight of the total catalyst, calculated as the elemental metal, and said platinum group metal being present in an amount of about 0.1% to about 3% by weight of the total catalyst, calculated as the elemental metal.
Claim 5
Dependent Claim
115 words
The process of claim 3 wherein said catalytically-active support of the step (1) catalyst is derived by the calcination of material comprising about 35% to about 65% by weight of silica and about 35% to about 65% by weight of alumina, based on the total silica and alumina in the support and supplied by a mixture comprising about 40% to about 85% by weight of amorphous silica-alumina and about 15% to about 60% by weight of alumina derived from hydrous alumina selected from the group consisting of boehmite, and mixtures thereof with amorphous hydrous alumina, and said Group VIII metal in the step 1) catalyst is selected from the group consisting of iron group metals.
Claim 6
Dependent Claim
32 words
The process of claim 4 wherein said mineral hydrocarbon oil feedstock is a residual oil and said step (1) catalyst has a surface area of at least about 140 m. 2 /gm.
Claim 7
Dependent Claim
81 words
The process of claim 4 wherein said Group VIb metal in the step (1) catalyst is selected from the group consisting of molybdenum, tungsten and mixtures thereof, and is present in an amount of about 10% to about 30% by weight of the total step (1) catalyst, calculated as the metal oxide, and said Group VIII, iron group metal is present in an amount of about 2% to about 10% by weight of the total catalyst, calculated as the elemental metal.
Claim 8
Dependent Claim
17 words
The process of claim 6 wherein said Group VIII metal in the step (1) catalyst is nickel.
Claim 9
Dependent Claim
105 words
The process of claim 7 wherein said hydrocarbon hydrocracking conditions include a temperature of about 725° F. to about 875° F., a hydrogen partial pressure of about 1,000 psig. to about 5,000 psig., a ratio of hydrogen-to-hydrocarbon feed of about 1,000 s.c.f./b. to about 8,000 s.c.f./b. and a WHSV in the range of about 0.3 to about 3; and the hydrocarbon hydrogenation conditions include a temperature of about 550° F. to about 825° F., a pressure of about 1,000 psig. to about 5,000 psig., a hydrogen-to-hydrocarbon feed ratio of about 500 s.c.f./b. to about 3,500 s.c.f./b. and a WHSV of about 0.3 to about 5.
Claim 10
Dependent Claim
32 words
The process of claim 8 wherein said mineral hydrocarbon oil feedstock is a residual oil and said step (1) catalyst has a surface area of at least about 140 m. 2 /gm.
Claim 11
Dependent Claim
104 words
The process of claim 7 wherein said hydrocarbon hydrocracking conditions include a temperature of about 750° F. to about 850° F., a hydrogen partial pressure of about 1500 psig. to 3,000 psig., a ratio of hydrogen-to-hydrocarbon feed of about 1500 s.c.f./b. to about 3,000 s.c.f./b. and a WHSV in the range of about 0.5 to about 2; and the hydrocarbon hydrogenation conditions include a temperature of about 600° F. to about 800° F., a pressure of about 1500 psig. to about 3,000 psig., a hydrogen-to-hydrocarbon feed ratio of about 1500 s.c.f./b. to about 3,000 s.c.f./b. and a WHSV of about 0.5 to about 3.
Claim 12
Dependent Claim
32 words
The process of claim 10 wherein said mineral hydrocarbon oil feedstock is a residual oil and said step (1) catalyst has a surface area of at least about 140 m. 2 /gm.
References Cited (Backward Citations)
US3642610A
Cited
US3726790A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-09 | 1984-06-09 | 1984-12-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-09 | 1988-06-09 | 1988-12-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-09 | 1992-06-09 | 1992-12-09 | $7700.00 | Window Closed / Lapsed |