US4238266A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process of forming a glass fiber reinforced, stampable thermoplastic laminate
Assignee: Honeywell International Inc
•
Filing: 1979-01-08
•
Granted: 1980-12-09
•
Expires: 1999-01-08
Abstract
Abstract Glass fiber reinforced thermoplastic laminate is formed by extruding first and second sheets of thermoplastic resin containing glass fibers. A layer of glass fibers is applied to one side of the first sheet. The second sheet is laminated to the first sheet and the layer of glass fiber at a temperature ranging from the melting point of the thermoplastic resin to about 650° F.
Inventors
- 👤 Albert H. Steinberg
- 👤 Lowell G. Ward
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:47
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/50; B29C70/504; B29C70/506; B29K; B29K2309/00; B29K2309/08
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
212 words
A continuous process of forming a glass-fiber reinforced, stampable thermoplastic laminate consisting essentially of the steps of: (a) extruding a first sheet of thermoplastic resin containing about 5 to 35% by weight of glass fibers on an extruded basis; (b) embedding a layer of glass fibers into one side of said first sheet; (c) extruding a second sheet of thermoplastic resin containing about 5 to 35% by weight of glass fibers on an extruded basis; and (d) laminating, in a lamination zone, said second sheet to said first sheet and said layer of glass fibers without substantially impairing the integrity of or rearranging said glass fibers of said first and second sheets, wherein said lamination zone comprises a set of three heated rolls, said first sheet and said layer of glass fibers being in the form of a prelaminate and being passed serially around the first and second of said heated rolls and thence between the second and third rolls, advancing said second sheet to the nip formed by the second and third rolls and onto said prelaminate and laminating said prelaminate and said second sheet between the second and third rolls and wherein the lamination occurs at a temperature ranging from the melting point of the resin to about 650° F.
Claim 2
Dependent Claim
212 words
A continuous process of forming a glass-fiber reinforced, stampable thermoplastic laminate consisting essentially of the steps of: (a) extruding a first sheet of thermoplastic resin containing about 5 to 35% by weight of glass fibers on an extruded basis; (b) embedding a layer of glass fibers into one side of said first sheet; (c) extruding a second sheet of thermoplastic resin containing about 5 to 35% by weight of glass fibers on an extruded basis; and (d) laminating, in a lamination zone, said second sheet to said first sheet and said layer of glass fibers without substantially impairing the integrity of or rearranging said glass fibers of said first and second sheets, wherein said lamination zone comprises a set of three heated rolls, said first sheet and said layer of glass fibers being in the form of a prelaminate and being passed serially around the first and second of said heated rolls and thence between the second and third rolls, advancing said second sheet to the nip formed by the second and third rolls and onto said prelaminate and laminating said prelaminate and said second sheet between the second and third rolls and wherein the lamination occurs at a temperature ranging from the melting point of the resin to about 650° F.
Claim 3
Dependent Claim
35 words
The process of claim 1 wherein said prelaminate is additionally heated during contact with said first and second rolls by means of an infrared heater before reaching said nip and said second and third rolls.
Claim 4
Dependent Claim
15 words
The process of claim 1 wherein said first sheet further comprises a particulate mineral filler.
Claim 5
Dependent Claim
14 words
The process of claim 3 wherein said second sheet further comprises a particulate filler.
Claim 6
Dependent Claim
61 words
The process of claim 1 wherein said thermoplastic resin is nylon 6 resin, said first sheet comprises by weight basis of the extruded sheet, 20 to 30% glass fiber, 5 to 35% mineral filler and 0.5 to 1.5% talc as a nucleating agent and said laminating step is conducted at a temperature in the range of about 450° to 550° F.
Claim 7
Dependent Claim
12 words
The process of claim 5 wherein said mineral filler comprises glass beads.
Claim 8
Dependent Claim
29 words
The process of claim 1 wherein the thermoplastic resin is nylon 6 and said second and third rolls are maintained at a maximum surface temperature of about 350° F.
Claim 9
Dependent Claim
22 words
The process of claim 7 wherein the first roll is maintained at a surface temperature below the melting point of the resin.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-09 | 1984-06-09 | 1984-12-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-09 | 1988-06-09 | 1988-12-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-09 | 1992-06-09 | 1992-12-09 | $7700.00 | Window Closed / Lapsed |