Method of producing hydrogenated amorphous silicon film
Assignee: United States Department of Energy
•
Filing: 1979-04-18
•
Granted: 1980-12-02
•
Expires: 1999-04-18
Abstract
Abstract This invention relates to hydrogenated amorphous silicon produced by thermally decomposing silane (SiH4) or other gases comprising H and Si, from a tungsten or carbon foil heated to a temperature of about 1400 DEG -1600 DEG C., in a vacuum of about 10-6 to 19-4 torr, to form a gaseous mixture of atomic hydrogen and atomic silicon, and depositing said gaseos mixture onto a substrate independent of and outside said source of thermal decomposition, to form hydrogenated amorphous silicon. The presence of an ammonia atmosphere in the vacuum chamber enhances the photoconductivity of the hydrogenated amorphous silicon film.
Inventors
- 👤 Harold J. Wiesmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 08:51
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/24; H; H10; H10F; H10F71/00; H10F71/10; H10F71/103; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
91 words
A method of producing hydrogenated amorphous silicon which comprises thermally decomposing a silicohydride gas by directing a stream of said silicohydride gas against a tungsten or carbon foil heated to a temperature of about 1400°-1600° C. and in a vacuum of about 10 -6 to 10 -4 torr, to form a gaseous mixture of atomic hydrogen and atomic silicon, and depositing said gaseous mixture onto a substrate independent of and situated a distance from said heated tungsten or carbon foil, to form a film of hydrogenated amorphous silicon on said substrate.
Claim 2
Independent Claim
91 words
A method of producing hydrogenated amorphous silicon which comprises thermally decomposing a silicohydride gas by directing a stream of said silicohydride gas against a tungsten or carbon foil heated to a temperature of about 1400°-1600° C. and in a vacuum of about 10 -6 to 10 -4 torr, to form a gaseous mixture of atomic hydrogen and atomic silicon, and depositing said gaseous mixture onto a substrate independent of and situated a distance from said heated tungsten or carbon foil, to form a film of hydrogenated amorphous silicon on said substrate.
Claim 3
Dependent Claim
12 words
A method in accordance with claim 1, wherein the silicohydride is silane.
Claim 4
Dependent Claim
19 words
A method in accordance with claim 1, wherein the substrate is heated to a temperature less than 500° C.
Claim 5
Dependent Claim
20 words
A method in accordance with claim 1, wherein ammonia is introduced in the vacuum chamber to create an ammonia atmosphere.
Claim 6
Dependent Claim
19 words
A method in accordance with claim 1, wherein the substrate is heated to a temperature of about 225°-325° C.
Claim 7
Dependent Claim
25 words
A method in accordance with claim 1, wherein the substrate is a material selected from the group consisting of sapphire, fused quartz and crystal silicon.
Claim 8
Dependent Claim
42 words
A method in accordance with claim 1, wherein the film of deposited hydrogenated amorphous silicon is vacuum annealed to about 175°-200° C. and then exposed to air at room temperature to increase the photoconductivity and dark conductivity over a period of time.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-02 | 1984-06-02 | 1984-12-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-02 | 1988-06-02 | 1988-12-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-02 | 1992-06-02 | 1992-12-02 | $7700.00 | Window Closed / Lapsed |