Polymerizable premix composition for preparation of polyurethane surfaces
Assignee: Chevron USA Inc
•
Filing: 1979-06-06
•
Granted: 1980-12-02
•
Expires: 1999-06-06
Abstract
Abstract A method is provided for stabilizing a polymerizable premix composition for use in preparing a polyurethane surface and the resulting composition. An aliphatic polyamide is used to achieve the stabilization.
Inventors
- 👤 Judson E. Goodrich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:31
CPC Classifications
C; C08; C08L; C08L75/00; C08L75/04; C08L95/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
152 words
A method for improving the storage stability of a polymerizable mixture comprising a high molecular weight diol component, a low molecular weight chain stiffener component and an asphalt component which comprises at least substantially increasing said stability by admixing into said mixture an effective amount to improve storage stability of at least one aliphatic polyamide resin having a molecular weight in the range of from about 3000 to 9000 and a softening point below 150° C., said resin being the condensation product of (1) at least one aliphatic polycarboxylic acid having a carboxyl group content in the range 2 to 8 and a carbon atom content in the range 10 to 72 and (2) at least one polyamine of the formula (H(HN--R--NH) x H, wherein R is an alkylene radical having a carbon atom content in the range 2 to 5 and x is an integer in the range 1 to 5.
Claim 2
Independent Claim
152 words
A method for improving the storage stability of a polymerizable mixture comprising a high molecular weight diol component, a low molecular weight chain stiffener component and an asphalt component which comprises at least substantially increasing said stability by admixing into said mixture an effective amount to improve storage stability of at least one aliphatic polyamide resin having a molecular weight in the range of from about 3000 to 9000 and a softening point below 150° C., said resin being the condensation product of (1) at least one aliphatic polycarboxylic acid having a carboxyl group content in the range 2 to 8 and a carbon atom content in the range 10 to 72 and (2) at least one polyamine of the formula (H(HN--R--NH) x H, wherein R is an alkylene radical having a carbon atom content in the range 2 to 5 and x is an integer in the range 1 to 5.
Claim 3
Dependent Claim
29 words
A method as in claim 1 wherein said amount of resin, based by weight upon said asphalt component, is in the range of from about 5 to 30 percent.
Claim 4
Dependent Claim
153 words
In a polymerizable mixture comprising a high molecular weight diol component, a low molecular weight chain stiffener component and an asphalt component, wherein said asphalt is present in the form of an unstabilized dispersion, solute or sol, the improvement comprising said mixture containing an effective amount to improve storage stability of at least one aliphatic polyamide resin having a molecular weight in the range of from about 3000 to 9000 and a softening point below 150° C., said resin being the condensation product of (1) at least one aliphatic polycarboxylic acid having a carboxyl group content in the range 2 to 8 and a carbon atom content in the range 10 to 72 and (2) at least one polyamine of the formula (H(HN--R--NH) x H, wherein R is an alkylene radical having a carbon atom content in the range 2 to 5 and x is an integer in the range 1 to 5.
Claim 5
Dependent Claim
153 words
In a polymerizable mixture comprising a high molecular weight diol component, a low molecular weight chain stiffener component and an asphalt component, wherein said asphalt is present in the form of an unstabilized dispersion, solute or sol, the improvement comprising said mixture containing an effective amount to improve storage stability of at least one aliphatic polyamide resin having a molecular weight in the range of from about 3000 to 9000 and a softening point below 150° C., said resin being the condensation product of (1) at least one aliphatic polycarboxylic acid having a carboxyl group content in the range 2 to 8 and a carbon atom content in the range 10 to 72 and (2) at least one polyamine of the formula (H(HN--R--NH) x H, wherein R is an alkylene radical having a carbon atom content in the range 2 to 5 and x is an integer in the range 1 to 5.
Claim 6
Dependent Claim
31 words
A mixture as in claim 3 wherein said polyamide, based by weight upon said asphalt component, is present in an amount in the range of from about 5 to 30 percent.
Claim 7
Dependent Claim
52 words
In a process for producing an asphalt-extended polyurethane surface by admixing an effective amount of a polyisocyanate component with a polymerizable mixture comprising a high molecular weight diol component, a low molecular weight chain stiffener component and an asphalt component, the improvement comprising using as said mixture the composition of claim 4.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-02 | 1984-06-02 | 1984-12-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-02 | 1988-06-02 | 1988-12-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-02 | 1992-06-02 | 1992-12-02 | $7700.00 | Window Closed / Lapsed |