Cross-linked polyurethane elastomers and microcellular foams
Assignee: Stamicarbon BV
•
Filing: 1979-03-05
•
Granted: 1980-11-25
•
Expires: 1999-03-05
Abstract
Abstract Cross-linked polyurethanes such as solid elastomeric polyurethanes or microcellular polyurethanes are prepared by reacting a polyisocyanate, one or more polyols and at least one trihydroxy compound in the presence of a catalyst using, as the hydroxyl compounds a low molecular weight diol, optionally a polymeric polyol and tris-( beta -hydroxypropyl)-isocyanaurate or ethoxylated tris-( beta -hydroxypropyl)-isocyanurate all present in specific ranges of proportions. Use of the specific isocyanurates provides for better utilization and smaller quantities of the blowing agent used to make microcellular polyurethane foams.
Inventors
- 👤 Kurt C. Frisch
- 👤 Daniel M. J. Tummers
- 👤 Anne Te Nijenhuis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 14:32
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/65; C08G18/66; C08G18/30; C08G18/38; C08G18/3819; C08G18/3842; C08G18/3851; C08G18/3853; C08G2120/00; Y; Y10; Y10S; Y10S528/00; Y10S528/906
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
155 words
In a process for preparing a cross-linked polyurethane elastomer by reacting a polyisocyanate, at least one polyol, and at least one trihydroxy compound, optionally in the presence of a catalyst, the improvement wherein the hydroxyl compounds employed are: A-1. a polymeric polyol compound having a molecular weight of between about 500 and about 10,000 and an average of 2 to 3 hydroxy groups per molecule; A-2. a dihydroxy compound having a molecular weight of between about 60 and about 200, in a quantity such that the ratio between the hydroxyl groups derived from the low molecular weight diol (A-2) and the hydroxyl groups derived from the polymeric polyol (A-1) is between about 0:1 and about 5:1; and B. tris-(β-hydroxypropyl)-isocyanurate or ethoxylated tris(β-hydroxypropyl)-isocyanurate such that the ratio between the hydroxyl groups derived from the isocyanurate and the hydroxyl groups derived from the sum of the polyols (A-1) and (A-2) is between about 0.5:1 and about 5:1.
Claim 2
Dependent Claim
155 words
In a process for preparing a cross-linked polyurethane elastomer by reacting a polyisocyanate, at least one polyol, and at least one trihydroxy compound, optionally in the presence of a catalyst, the improvement wherein the hydroxyl compounds employed are: A-1. a polymeric polyol compound having a molecular weight of between about 500 and about 10,000 and an average of 2 to 3 hydroxy groups per molecule; A-2. a dihydroxy compound having a molecular weight of between about 60 and about 200, in a quantity such that the ratio between the hydroxyl groups derived from the low molecular weight diol (A-2) and the hydroxyl groups derived from the polymeric polyol (A-1) is between about 0:1 and about 5:1; and B. tris-(β-hydroxypropyl)-isocyanurate or ethoxylated tris(β-hydroxypropyl)-isocyanurate such that the ratio between the hydroxyl groups derived from the isocyanurate and the hydroxyl groups derived from the sum of the polyols (A-1) and (A-2) is between about 0.5:1 and about 5:1.
Claim 3
Dependent Claim
42 words
The process according to claim 1, wherein the ratio between the hydroxyl groups derived from the tris-(β-hydroxypropyl)-isocyanurate or its ethoxylated derivative and the hydroxyl groups derived from the sum of the polyols (A-1 and A-2) is between about 0.8:1 and about 3.5:1.
Claim 4
Dependent Claim
95 words
The process according to claim 1 or 2 wherein the polymeric polyol (A-1) is selected from the group consisting of polyoxyalkylene glycols composed of C 2 to C 4 oxyalkylene units, the addition products of a C 2 to C 3 alkene oxide of a trihydroxy compound, polyactone diols derived from C 5 to C 12 lactones, polylactone triols derived from C 5 to C 12 lactones, hydroxylterminated polyesters, polyacrylates containing hydroxyl groups and graft polymers containing hydroxyl groups having chains based on acrylonitrile and graft polymers containing hydroxyl groups having chains based on styrene.
Claim 5
Dependent Claim
29 words
The process according to claim 1 or 3 wherein an elastomeric polyurethane is prepared using a polymeric polyol (A-1) having a molecular weight between about 500 and about 2,500.
Claim 6
Dependent Claim
91 words
The process according to claim 4 wherein an elastomeric polyurethane is produced using an amount of tris-(β-hydroxypropyl)-isocyanurate or the ethoxylated derivative thereof such that the ratio of the hydroxyl groups derived from said isocyanurate triol and the hydroxyl groups derived from the other polyols is between about 1.0 and about 3.5, and the quantity of low molecular weight diol (A-2) used is such that the ratio between the hydroxyl groups derived from the (A-2) diol and the hydroxyl groups derived from the polymeric polyol (A-1) is about 0:1 to about 0.5:1.
Claim 7
Dependent Claim
67 words
The process according to claim 1 or 3 wherein said polyol (A-1) is a polymeric trihydroxyl compound having a molecular weight of between about 2,500 and about 10,000, and the quantity of said isocyanurate triol is such that the ratio between the hydroxyl groups derived from the polymeric trihydroxyl compound and the hydroxyl groups deriving from said isocyanurate triol (B) is between about 0.1:1 and about 1.0:1.
Claim 8
Dependent Claim
22 words
The process according to claim 6 wherein said polymeric trihydroxyl compound has a molecular weight of between about 4,000 and about 8,000.
Claim 9
Dependent Claim
10 words
A cross-linked polyurethane produced by the process of claim 1.
Claim 10
Dependent Claim
10 words
An elastomeric polyurethane produced by the process of claim 3.
Claim 11
Dependent Claim
153 words
In a process for preparing a microcellular polyurethane foam by reacting a polyisocyanate, at least one polyol, and at least one trihydroxy compound, optionally in the presence of a catalyst, the improvement wherein the hydroxyl compounds employed are: A-1. a polymeric polyol compound having a molecular weight of between about 500 and about 10,000 and an average of 2 to 3 hydroxy groups per molecule; A-2. a dihydroxy compound having a molecular weight of between 60 and about 200, and present in an amount such that the ratio between the hydroxyl groups derived from the diol (A-2) and the hydroxyl groups derived from the polymeric polyol (A-1) is between about 0.5:1 and about 3:1; and B. tris-(β-hydroxypropyl)-isocyanurate or ethoxylated tris(β-hydroxypropyl)-isocyanurate such that the ratio between the hydroxyl groups derived from the isocyanurate and the hydroxyl groups derived from the sum of the polyols (A-1 and A-2) is between about 0.5:1 and about 5:1.
Claim 12
Dependent Claim
153 words
In a process for preparing a microcellular polyurethane foam by reacting a polyisocyanate, at least one polyol, and at least one trihydroxy compound, optionally in the presence of a catalyst, the improvement wherein the hydroxyl compounds employed are: A-1. a polymeric polyol compound having a molecular weight of between about 500 and about 10,000 and an average of 2 to 3 hydroxy groups per molecule; A-2. a dihydroxy compound having a molecular weight of between 60 and about 200, and present in an amount such that the ratio between the hydroxyl groups derived from the diol (A-2) and the hydroxyl groups derived from the polymeric polyol (A-1) is between about 0.5:1 and about 3:1; and B. tris-(β-hydroxypropyl)-isocyanurate or ethoxylated tris(β-hydroxypropyl)-isocyanurate such that the ratio between the hydroxyl groups derived from the isocyanurate and the hydroxyl groups derived from the sum of the polyols (A-1 and A-2) is between about 0.5:1 and about 5:1.
Claim 13
Dependent Claim
40 words
The process for preparing a microcellular polyurethane foam according to claim 10 wherein the ratio between the hydroxyl groups derived from the diol (A-2) and the hydroxyl groups derived from the polymeric polyol (A-1) is between about 1.0:1 and 2.0:1.
Claim 14
Dependent Claim
101 words
The process for preparing a microcellular polyurethane foam according to claim 10 or 11 wherein the polymeric polyol (A-1) is selected from the group consisting of polyoxyalkylene glycols composed of C 2 to C 4 oxyalkylene units, the addition products of a C 2 to C 3 alkene oxide of a trihydroxy compound, polylactone diols derived from C 5 to C 12 lactones, polylactone triols derived from C 5 to C 12 lactones, hydroxylterminated polyesters, polyacrylates containing hydroxyl groups and graft polymers containing hydroxyl groups having chains based on acrylonitrile and graft polymers containing hydroxyl groups having chains based on styrene.
Claim 15
Dependent Claim
72 words
The process for preparing a microcellular polyurethane foam according to claim 10 wherein a cross-linked microcellular polyurethane having a density of at least 200 kg/m 3 is produced by conducting said reaction in the presence of a blowing agent, and the ratio of the hydroxyl groups derived from said isocyanurate triol and the hydroxyl groups derived from the sum of the polyols A-1 and A-2 is between about 0.8:1 and about 2.5:1.
Claim 16
Dependent Claim
27 words
The process for preparing a microcellular polyurethane foam according to claim 13 wherein said cross-linked microcellular polyurethane has a density of at least 200 kg/cm 3 .
Claim 17
Dependent Claim
27 words
The process for preparing a microcellular polyurethane foam according to claim 14 wherein said cross-linked microcellular polyurethane has a density of at least 400 kg/cm 3 .
Claim 18
Dependent Claim
76 words
The process for preparing a microcellular polyurethane foam according to claim 13 wherein the ratio of the hydroxyl groups derived from the low molecular weight diol and the hydroxyl groups derived from the polymeric polyol are both between about 1:1 and about 2:1, and the ratio between the hydroxyl groups derived from said isocyanurate and the hydroxyl groups derived from the sum of the polyols (A-1 and A-2) are both between about 1:1 and about 2:1.
Claim 19
Dependent Claim
71 words
The process for preparing a microcellular polyurethane foam according to claim 10 wherein said polyol (A-1) is a polymeric trihydroxyl compound having a molecular weight of between about 2,500 and about 10,000, and the quantity of said isocyanurate triol is such that the ratio between the hydroxyl groups derived from the polymeric trihydroxyl compound and the hydroxyl groups deriving from said isocyanurate triol (B) is between about 0.1:1 and about 1.0:1.
Claim 20
Dependent Claim
28 words
The process for preparing a microcellular polyurethane foam according to claim 17 wherein said polymeric trihydroxyl compound has a molecular weight of between about 4,000 and about 8,000.
Claim 21
Dependent Claim
20 words
A cross-linked microcellular polyurethane having a density of at least 200 kg/cm 3 produced by the process of claim 13.
References Cited (Backward Citations)
US2052490A
Cited
US3174950A
Cited
GB1080487A
Cited
US3730923A
Cited
US4031040A
Cited
US4063020A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-25 | 1984-05-26 | 1984-11-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-25 | 1988-05-26 | 1988-11-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-25 | 1992-05-26 | 1992-11-25 | $7700.00 | Window Closed / Lapsed |