Method and apparatus for the degassing of molten metal
Assignee: Rio Tinto Switzerland AG
•
Filing: 1979-05-23
•
Granted: 1980-11-25
•
Expires: 1999-05-23
Abstract
Abstract An improved method and apparatus for degassing molten metal is disclosed in which the molten metal is passed in countercurrent relationship with a fluxing gas which is introduced through a sparger plate provided with a plurality of orifices of controlled size and spacing so as to minimize fluxing gas bubble size while maximizing fluxing gas bubble density thereby optimizing the degassing of the molten metal.
Inventors
- 👤 Jonathan A. Dantzig
- 👤 Derek E. Tyler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:23
CPC Classifications
C; C21; C21C; C21C7/00; C21C7/04; C21C7/072; C22; C22B; C22B21/00; C22B21/06; C22B21/066; C22B9/00; C22B9/05; C22B9/055
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
168 words
An apparatus for degassing molten metal by purging said molten metal with a fluxing gas which comprises a fluxing box having a floor, inlet means for delivering said molten metal to said fluxing box, outlet means for removing said molten metal from said fluxing box, the improvement which comprises means located within said fluxing box for purging said molten metal with said fluxing gas while said molten metal is within said fluxing box, said means comprising a sparger plate means being provided with a plurality of orifices of controlled size and spacing so as to minimize fluxing gas bubble size maximizing fluxing gas bubble dispersion thereby optimizing the degassing of said molten metal wherein said spacing of said orifices is no smaller than twice d b so as to prevent bubble coalescence where d b is the bubble diameter defined by the equation ##EQU10## where θ=contact angle of the bubble on the sparger plate σ=surface tension g=gravity ρ liq =density of liquid ρ gas =density of fluxing gas.
Claim 2
Independent Claim
168 words
An apparatus for degassing molten metal by purging said molten metal with a fluxing gas which comprises a fluxing box having a floor, inlet means for delivering said molten metal to said fluxing box, outlet means for removing said molten metal from said fluxing box, the improvement which comprises means located within said fluxing box for purging said molten metal with said fluxing gas while said molten metal is within said fluxing box, said means comprising a sparger plate means being provided with a plurality of orifices of controlled size and spacing so as to minimize fluxing gas bubble size maximizing fluxing gas bubble dispersion thereby optimizing the degassing of said molten metal wherein said spacing of said orifices is no smaller than twice d b so as to prevent bubble coalescence where d b is the bubble diameter defined by the equation ##EQU10## where θ=contact angle of the bubble on the sparger plate σ=surface tension g=gravity ρ liq =density of liquid ρ gas =density of fluxing gas.
Claim 3
Dependent Claim
18 words
An apparatus according to claim 1 wherein said sparger plate means constitutes the floor of said fluxing box.
Claim 4
Dependent Claim
18 words
An apparatus according to claim 1 wherein said mixture comprises from about 5 to 15% by volume dichlorodifluoromethane.
Claim 5
Dependent Claim
39 words
An apparatus according to claim 2 wherein said orifice size is defined by the equation ##EQU11## where F=flow rate of fluxing gas per hole ν=kinematic viscosity ρ=density of fluxing gas L=thickness of sparger plate ΔP=pressure drop across the holes.
Claim 6
Dependent Claim
61 words
An apparatus according to claim 4 wherein said spacing of said orifices is no smaller than twice d b so as to prevent bubble coalescence where d b is the bubble diameter defined by the equation ##EQU12## where θ=contact angle of the bubble on the sparger plate σ=surface tension g=gravity ρ liq =density of liquid ρ gas =density of fluxing gas.
Claim 7
Dependent Claim
33 words
An apparatus according to claim 1 wherein said fluxing gas comprises a mixture of an element taken from the group of nitrogen or argon with from about 2 to 20% by volume dichlorodifluoromethane.
Claim 8
Dependent Claim
106 words
An improved sparger plate for use in the degassing of molten metal wherein said sparger plate is provided with a plurality of orifices of controlled size and spacing so as to minimize fluxing gas bubble size while maximizing fluxing gas bubble dispersion thereby optimizing the degassing of said molten metal wherein said spacing of said orifices is no smaller than twice of d b so as to prevent bubble coalescence where d b is the bubble diameter defined by the equation ##EQU13## where θ=contact angle of the bubble on the sparger plate σ=surface tension g=gravity ρ liq =density of liquid ρ gas =density of fluxing gas.
Claim 9
Dependent Claim
106 words
An improved sparger plate for use in the degassing of molten metal wherein said sparger plate is provided with a plurality of orifices of controlled size and spacing so as to minimize fluxing gas bubble size while maximizing fluxing gas bubble dispersion thereby optimizing the degassing of said molten metal wherein said spacing of said orifices is no smaller than twice of d b so as to prevent bubble coalescence where d b is the bubble diameter defined by the equation ##EQU13## where θ=contact angle of the bubble on the sparger plate σ=surface tension g=gravity ρ liq =density of liquid ρ gas =density of fluxing gas.
Claim 10
Dependent Claim
40 words
A sparger plate according to claim 7 wherein said orifice size is defined by the equation ##EQU14## where F=flow rate of fluxing gas per hole ν=kinematic viscosity ρ=density of fluxing gas L=thickness of sparger plate ΔP=pressure drop across the holes.
Claim 11
Independent Claim
134 words
A method for degassing molten metal by purging said molten metal with a fluxing gas which comprises passing said fluxing gas through said molten metal in countercurrent flow therewith, the improvement comprising feeding said fluxing gas to said molten metal through a sparger plate characterized by having a plurality of discrete orifices of controlled size and spacing so as to minimize fluxing gas bubble size while maximizing fluxing gas bubble dispersion thereby optimizing the degassing of said molten metal wherein said spacing of said orifices is no smaller than twice d b so as to prevent bubble coalescence where d b is the bubble diameter defined by the equation ##EQU15## where θ=contact angle of the bubble on the sparger plate σ=surface tension g=gravity ρ liq =density of liquid ρ gas =density of fluxing gas.
Claim 12
Independent Claim
134 words
A method for degassing molten metal by purging said molten metal with a fluxing gas which comprises passing said fluxing gas through said molten metal in countercurrent flow therewith, the improvement comprising feeding said fluxing gas to said molten metal through a sparger plate characterized by having a plurality of discrete orifices of controlled size and spacing so as to minimize fluxing gas bubble size while maximizing fluxing gas bubble dispersion thereby optimizing the degassing of said molten metal wherein said spacing of said orifices is no smaller than twice d b so as to prevent bubble coalescence where d b is the bubble diameter defined by the equation ##EQU15## where θ=contact angle of the bubble on the sparger plate σ=surface tension g=gravity ρ liq =density of liquid ρ gas =density of fluxing gas.
Claim 13
Dependent Claim
39 words
A method according to claim 9 wherein said orifice size is defined by the equation ##EQU16## where F=flow rate of fluxing gas per hole ν=kinematic viscosity ρ=density of fluxing gas L=thickness of sparger plate ΔP=pressure drop across the holes.
Claim 14
Dependent Claim
61 words
A method according to claim 10 wherein said spacing of said orifices is no smaller than twice d b so as to prevent bubble coalescence where d b is the bubble diameter defined by the equation ##EQU17## where θ=contact angle of the bubble on the sparger plate σ=surface tension g=gravity ρ liq =density of liquid ρ gas =density of fluxing gas.
References Cited (Backward Citations)
US23123A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-25 | 1984-05-26 | 1984-11-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-25 | 1988-05-26 | 1988-11-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-25 | 1992-05-26 | 1992-11-25 | $7700.00 | Window Closed / Lapsed |