Method of making ommateal lenses and plates
Assignee: American Optical Corp
•
Filing: 1979-04-23
•
Granted: 1980-11-04
•
Expires: 1999-04-23
Abstract
Abstract Columnar lens elements of a crossed multi-ocular array are each formed of a rectangular preform of core glass containing a modifying oxide which is clad on each of two of its opposite sides with a glass having an affinity to ions of the modifying oxide and on remaining sides with a substantially non-reactive glass, all cladding glasses being preferentially soluble relative to the core glass. The clad preform is heated and drawn to the cross-sectional size desired of the aforesaid lens elements and cut transaxially into component lengths equal to or greater than desired for the array. A multiplicity of the cut components are tightly juxtapositioned, heated for diffusion of oxide ions into the first mentioned cladding glasses, cooled, annealed and leached free of all claddings for final crossed assembly.
Inventors
- 👤 Walter P. Siegmund
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 10:31
CPC Classifications
C; C03; C03C; C03C3/00; C03C3/04; C03C3/062; C03C3/064; C03C3/068; C03B; C03B23/00; C03B23/04; C03B23/047; C03C23/00
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
231 words
The method of making a unidirectionally graded refractive index columnar lens element comprising: preparing an elongated lens preform of optical glass having a composition which includes a modifying oxide, said preform being of rectangular cross-sectional shape and having a pair of optically finished sides, one opposite the other; positioning against each of said optically finished sides a piece of a first cladding glass which is preferentially soluble relative to the glass of said preform and substantially non-reactive with said modifying oxide; positioning against each of remaining sides of said preform a piece of a second cladding glass which is also preferentially soluble relative to the glass of said preform but has an affinity to ions of said modifying oxide; zonally heating and drawing the assembly of said preform and all cladding pieces sufficiently to bring at least a portion of said preform to the cross-sectional size desired of said lens element substantially without alteration of said rectangular shape of said preform; substantially uniformly heating said portion of said preform and corresponding portions of said cladding pieces to a temperature and for a time sufficient to effect extraction of ions of the modifying oxide substantially only into said second cladding glasses; cooling and annealing said portion of said preform; and leaching all cladding glasses away from said portion of said preform whereby said portion constitutes said unidirectionally grades refractive index lens element.
Claim 2
Independent Claim
231 words
The method of making a unidirectionally graded refractive index columnar lens element comprising: preparing an elongated lens preform of optical glass having a composition which includes a modifying oxide, said preform being of rectangular cross-sectional shape and having a pair of optically finished sides, one opposite the other; positioning against each of said optically finished sides a piece of a first cladding glass which is preferentially soluble relative to the glass of said preform and substantially non-reactive with said modifying oxide; positioning against each of remaining sides of said preform a piece of a second cladding glass which is also preferentially soluble relative to the glass of said preform but has an affinity to ions of said modifying oxide; zonally heating and drawing the assembly of said preform and all cladding pieces sufficiently to bring at least a portion of said preform to the cross-sectional size desired of said lens element substantially without alteration of said rectangular shape of said preform; substantially uniformly heating said portion of said preform and corresponding portions of said cladding pieces to a temperature and for a time sufficient to effect extraction of ions of the modifying oxide substantially only into said second cladding glasses; cooling and annealing said portion of said preform; and leaching all cladding glasses away from said portion of said preform whereby said portion constitutes said unidirectionally grades refractive index lens element.
Claim 3
Dependent Claim
58 words
The method according to claim 1 including the application of high isostatic pressure to said drawn portion of said preform and corresponding portions of said cladding pieces during said step of surface heating for said extraction of ions of said modifying oxide, and removing said high isostatic pressure following said step of cooling said portion of said preform.
Claim 4
Dependent Claim
65 words
The method according to claim 1 wherein said modifying oxide is thallium oxide and said second cladding glass comprises a composition containing a substantial proportion of potassium oxide whereby said substantially uniform heating of said portion of said preform and cladding pieces effects interdiffusion of Tl + and K + ions through contacting surfaces of said glass of said preform and said second cladding glasses.
Claim 5
Dependent Claim
45 words
The method according to claim 1 wherein said leaching of all cladding glasses away from said portion of said preform is effected in an acid and said resulting graded refractive index lens element is cleaned of residue of said acid following said step of leaching.
Claim 6
Independent Claim
272 words
The method of mass producing unidirectionally graded refractive index columnar lens elements comprising: preparing an elongated lens element preform of optical glass having a composition which includes a modifying oxide, said preform being of rectangular cross-sectional shape and having a pair of optically finished sides, one opposite the other; positioning against each of said optically finished sides a piece of a first cladding glass which is preferentially soluble relative to the glass of said preform and substantially non-reactive with said modifying oxide; positioning against each of remaining sides of said preform a piece of a second cladding glass which is also preferentially soluble relative to the glass of said preform but has an affinity to ions of said modifying oxide; zonally heating and drawing the assembly of said preform and all cladding pieces sufficiently to bring at least a portion of said preform to the configuration of a long element of the cross-sectional size desired of said lens element substantially without alteration of said rectangular shape of preform; dividing said long element into a number of shorter lengths; bundling said shorter lengths of said element together; applying a high substantially isostatic compressing force to said bundle and heating same to a temperature above the deformation temperature of said glass of said preform for a period of time sufficient to effect extraction of ions of said modifying oxide substantially only into said second cladding pieces of said drawn assembly; cooling and annealing said bundle; removing said applied pressure; and leaching said cladding glasses away from said drawn preform glasses whereby said remaining preform glasses constitute said mass produced unidirectionally graded refractive lens elements.
Claim 7
Independent Claim
272 words
The method of mass producing unidirectionally graded refractive index columnar lens elements comprising: preparing an elongated lens element preform of optical glass having a composition which includes a modifying oxide, said preform being of rectangular cross-sectional shape and having a pair of optically finished sides, one opposite the other; positioning against each of said optically finished sides a piece of a first cladding glass which is preferentially soluble relative to the glass of said preform and substantially non-reactive with said modifying oxide; positioning against each of remaining sides of said preform a piece of a second cladding glass which is also preferentially soluble relative to the glass of said preform but has an affinity to ions of said modifying oxide; zonally heating and drawing the assembly of said preform and all cladding pieces sufficiently to bring at least a portion of said preform to the configuration of a long element of the cross-sectional size desired of said lens element substantially without alteration of said rectangular shape of preform; dividing said long element into a number of shorter lengths; bundling said shorter lengths of said element together; applying a high substantially isostatic compressing force to said bundle and heating same to a temperature above the deformation temperature of said glass of said preform for a period of time sufficient to effect extraction of ions of said modifying oxide substantially only into said second cladding pieces of said drawn assembly; cooling and annealing said bundle; removing said applied pressure; and leaching said cladding glasses away from said drawn preform glasses whereby said remaining preform glasses constitute said mass produced unidirectionally graded refractive lens elements.
Claim 8
Dependent Claim
28 words
The method according to claim 5 wherein said modifying oxide is thallium oxide and said second cladding pieces comprise a glass containing a substantial proportion of potassium oxide.
Claim 9
Dependent Claim
44 words
The method according to claim 6 wherein said step of heating said drawn portion of said preform and corresponding cladding pieces effects interdiffusion of Tl + and K + ions through contacting surfaces of said glasses of said preforms and said second cladding glasses.
Claim 10
Dependent Claim
42 words
The method according to claim 5 wherein said cladding pieces are leached away from said drawn portions of said preform in an acid and said leached portions of said preform are cleaned of residue of said acid following said step of leaching.
Claim 11
Dependent Claim
17 words
A multi-ocular array of crossed columnar lens elements each produced according to the method of claim 1.
Claim 12
Dependent Claim
17 words
A crossed multi-ocular array of columnar lens elements mass produced according to the method of claim 5.
References Cited (Backward Citations)
US3004368A
Cited
US3455667A
Cited
US4002452A
Cited
US3941474A
Cited
US3801181A
Cited
US3843228A
Cited
US3667832A
Cited
US3791806A
Cited
US3879182A
Cited
US3989495A
Cited
US4011071A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-04 | 1984-05-05 | 1984-11-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-04 | 1988-05-05 | 1988-11-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-04 | 1992-05-05 | 1992-11-04 | $7700.00 | Window Closed / Lapsed |