US4230654A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of concurrently-biaxially drawing polyvinyl alcohol film
Assignee: Unitika Ltd
•
Filing: 1979-01-31
•
Granted: 1980-10-28
•
Expires: 1999-01-31
Abstract
Abstract A concurrent-biaxially drawn polyvinyl alcohol film is prepared by fabricating a molten hydrate polyvinyl alcohol into a film; drying it under preventing an orientation thereof to form a substantially non-orientated substrate film having a water content of 3 to 20 wt. %; coating an aqueous dispersion of a macromolecular compound on at least one surface of the substrate film to form a coated film having an average water content of 5 to 30 wt. % with an increased water content of 2 to 10 wt. %; concurrent-biaxially drawing the coated film at an area elongation percent of 600 to 1300% to form a drawn film; drying the drawn film under releasing stress at a water content of less than 3 wt. % to form a dried film; and heat-treating continuously the dried film at higher than 160° C. and lower than a decomposition temperature for a short time.
Inventors
- 👤 Mutsuo Kuga
- 👤 Kiyoshi Kitagawa
- 👤 Motoo Kawasaki
- 👤 Junkichi Watanabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 17:01
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/048; C08J7/052; C08J2329/00; C08J2329/02; C08J2329/04
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
200 words
A process for preparing a concurrently-biaxially drawn polyvinyl alcohol film, comprising the steps of: (a) fabricating a molten, hydrated polyvinyl alcohol into a film; (b) drying said film while preventing orientation of the film thereby obtaining a substrate film which is in a substantially non-oriented state and which has a water content of 3 to 20 wt. %; (c) coating said dried film on at least one surface with an aqueous dispersion of a macromolecular compound thereby forming a coated film wherein the film substrate has an average water content of 5 to 30 wt. % as a result of water permeation into the substrate film from said coating, the average water content of said substrate film increasing by 2 to 10 wt. % as a result of said water permeation; (d) concurrently-biaxially drawing said coated film to achieve an area elongation of 600 to 1300%; (e) heat treating said drawn film to relieve stress in said film and to dry said film to a water content of less than 3 wt.%; and (f) continuing the heat treating of said dried film at a temperature greater than 160° C. but less than the decomposition temperature to achieve the film product.
Claim 2
Dependent Claim
200 words
A process for preparing a concurrently-biaxially drawn polyvinyl alcohol film, comprising the steps of: (a) fabricating a molten, hydrated polyvinyl alcohol into a film; (b) drying said film while preventing orientation of the film thereby obtaining a substrate film which is in a substantially non-oriented state and which has a water content of 3 to 20 wt. %; (c) coating said dried film on at least one surface with an aqueous dispersion of a macromolecular compound thereby forming a coated film wherein the film substrate has an average water content of 5 to 30 wt. % as a result of water permeation into the substrate film from said coating, the average water content of said substrate film increasing by 2 to 10 wt. % as a result of said water permeation; (d) concurrently-biaxially drawing said coated film to achieve an area elongation of 600 to 1300%; (e) heat treating said drawn film to relieve stress in said film and to dry said film to a water content of less than 3 wt.%; and (f) continuing the heat treating of said dried film at a temperature greater than 160° C. but less than the decomposition temperature to achieve the film product.
Claim 3
Dependent Claim
24 words
The process according to claim 1 wherein said molten polyvinyl alcohol is fabricated by a hydrate extruding method to form a flat substrate film.
Claim 4
Dependent Claim
23 words
The process according to claim 1 wherein said molten polyvinyl alcohol is fabricated by a flow-casting method to form a flat substrate film.
Claim 5
Dependent Claim
23 words
The process according to claim 1 wherein said molten polyvinyl alcohol is fabricated by a tubular shaping device to form a substrate film.
Claim 6
Dependent Claim
41 words
The process according to claim 1, wherein said substrate film having been uniaxially drawn longitudinally and transversely at 100° C. has a tensile stress ratio in the longitudinal direction to the transverse direction of 1.10 at an elongation percent of 100%.
Claim 7
Dependent Claim
115 words
The process according to claim 1 wherein said macromolecular compound in said aqueous dispersion is a homopolymer selected from the group consisting of polyethylene, polystyrene, polyvinyl, polyacryl and polyurethane; a resin selected from the group consisting of fluorinated resins, silicone resins, epoxy resins, natural resins; a copolymer selected from the group consisting of vinylidene chloride/vinyl chloride copolymers, vinylidene chloride/acryl copolymers, vinylacetate/acryl copolymers, styrene/acryl copolymers and ethylene/vinyl acetate copolymers; a terpolymer selected from the group consisting of methyl methacrylate/ethylacrylate/acrylic acid terpolymers, ethylene/vinylacetate/vinyl ester of a C 10 aliphatic acid terpolymers, and a modified resin selected from the group consisting of nitrocellulose and derivatives thereof, synthetic rubber modified resins, vinyl acetate modified resins and acryl modified resins.
Claim 8
Dependent Claim
30 words
The process according to claim 1 wherein said aqueous dispersion of the macromolecular compound has a solid concentration of 20 to 60 wt.% and a pH of 2 to 9.
Claim 9
Dependent Claim
27 words
The process of claim 1, wherein the amount of solid component from said aqueous dispersion coated on said substrate film is greater than 10 g/m 2 .
Claim 10
Dependent Claim
27 words
The process according to claim 1, 6, 7 or 8 wherein said aqueous dispersion of the macromolecular compound is coated on both surfaces of said substrate film.
Claim 11
Dependent Claim
36 words
The process according to claim 1 wherein during concurrent-biaxial drawing the ratio of longitudinal drawing to transverse drawing from the start of drawing to the end of drawing is in the range of 0.5 to 2.0.
Claim 12
Dependent Claim
20 words
The process according to claim 1 wherein said concurrent-biaxial drawing of said coated film is conducted by a tenter device.
Claim 13
Dependent Claim
20 words
The process according to claim 1 wherein said concurrent-biaxial drawing of said coated film is conducted by a tubular device.
Claim 14
Dependent Claim
70 words
The process of claim 1, wherein in the heat treatment of said drawn film to dry the film and relieve stress in the film, the heating is conducted at a temperature of T≦100x 2 +30x+150(°C.) as determined by the relationship: x=(Fmax-F)/Fmax wherein Fmax is the maximum stress at the end of the drawing step, F is the stress in the stress releasing step and x is the stress release coefficient.
Claim 15
Dependent Claim
17 words
The process according to claim 13 wherein the stress-releasing and drying are gradually conducted in a dryer.
Claim 16
Dependent Claim
24 words
The process according to claim 13 wherein stress releasing and drying are conducted on the connected part of a drawing machine link driving device.
Claim 17
Dependent Claim
28 words
The process of claim 1, wherein said dried film is heat treated while said film, free of stress in the transverse direction, passes over a plurality of rollers.
Claim 18
Dependent Claim
26 words
The process of claim 1, wherein said dried film is heat treated with a tenter device which maintains the film at constant longitudinal and transverse lengths.
References Cited (Backward Citations)
DE1202974B
Cited
US3136657A
Cited
US3214291A
Cited
US3440316A
Cited
DE2455504A1
Cited
US3985849A
Cited
JPS5128169A
Cited
JPS5150370A
Cited
JPS5161569A
Cited
JPS5226787A
Cited
US4124677A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-28 | 1984-04-28 | 1984-10-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-28 | 1988-04-28 | 1988-10-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-28 | 1992-04-28 | 1992-10-28 | $7700.00 | Window Closed / Lapsed |