US4229339A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the preparation of polymer dispersions
Assignee: Imperial Chemical Industries Ltd
•
Filing: 1977-05-09
•
Granted: 1980-10-21
•
Expires: 1997-05-09
Abstract
Abstract A dispersion of a condensation polymer in an organic liquid medium in which the polymer is insoluble is prepared by heating in the liquid medium one or more appropriate reactants one of which is present in the liquid disperse phase of an emulsion of which the continuous phase is constituted by the said liquid medium, in the presence dissolved in the liquid medium of a single-chain polymeric material of molecular weight between 1000 and 20,000 which carries at least one reactive group capable of taking part in the condensation polymer-forming reaction.
Inventors
- 👤 John Bentley
- 👤 Morice W. Thompson
- 👤 Auguste L. L. Palluel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 10:50
CPC Classifications
C; C08; C08G; C08G85/00
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
240 words
A process for the preparation of a dispersion of a condensation polymer in which the links between the reactants which form the polymer involve atoms other than carbon and in which a low molecular weight by-product is eliminated during the polymerisation reaction by which said polymer is made in an organic liquid medium in which the polymer is insoluble, the process comprising heating in the said liquid medium at the polymerisation temperature one or more condensation polymer-forming reactants, the reactant or at least one of the reactants being present in the liquid disperse phase of an emulsion of which the liquid continuous phase is constituted by the aforesaid liquid medium, said reactant being selected from the group consisting of a reactant which is liquid at normal temperature, a reactant which is melted by heating in the organic liquid medium at a temperature not higher than the polymerisation temperature, and a reactant which is a solid which cannot be melted at the reaction temperature and which is dissolved in a second, inert liquid which is substantially immiscible with the organic liquid medium, there being also present dissolved in the said liquid medium a polymeric material having a single polymer chain of molecular weight between 1000 and 20,000 which carries at least one reactive group capable of taking part in the condensation polymer-forming reaction, said single polymer chain being a homopolymer or a random copolymer but not a block or graft copolymer.
Claim 2
Dependent Claim
240 words
A process for the preparation of a dispersion of a condensation polymer in which the links between the reactants which form the polymer involve atoms other than carbon and in which a low molecular weight by-product is eliminated during the polymerisation reaction by which said polymer is made in an organic liquid medium in which the polymer is insoluble, the process comprising heating in the said liquid medium at the polymerisation temperature one or more condensation polymer-forming reactants, the reactant or at least one of the reactants being present in the liquid disperse phase of an emulsion of which the liquid continuous phase is constituted by the aforesaid liquid medium, said reactant being selected from the group consisting of a reactant which is liquid at normal temperature, a reactant which is melted by heating in the organic liquid medium at a temperature not higher than the polymerisation temperature, and a reactant which is a solid which cannot be melted at the reaction temperature and which is dissolved in a second, inert liquid which is substantially immiscible with the organic liquid medium, there being also present dissolved in the said liquid medium a polymeric material having a single polymer chain of molecular weight between 1000 and 20,000 which carries at least one reactive group capable of taking part in the condensation polymer-forming reaction, said single polymer chain being a homopolymer or a random copolymer but not a block or graft copolymer.
Claim 3
Dependent Claim
27 words
A process as claimed in claim 1, wherein the reactant which is present in an emulsified disperse phase is a reactant which is liquid at normal temperatures.
Claim 4
Dependent Claim
36 words
A process as claimed in claim 1, wherein the reactant which is present in an emulsified disperse phase is melted by heating in the organic liquid medium at a temperature not higher than the polymerisation temperature.
Claim 5
Dependent Claim
47 words
A process as claimed in claim 1, wherein the reactant which is present in an emulsified disperse phase is a solid which cannot be melted at the reaction temperature and which is dissolved in a second, inert liquid which is substantially immiscible with the organic liquid medium.
Claim 6
Dependent Claim
17 words
A process as claimed in claim 1, wherein the condensation polymer is a polyester or a polyamide.
Claim 7
Dependent Claim
44 words
A process as claimed in claim 1, wherein the reactive group carried by the polymeric material of molecular weight between 1000 and 20,000 which is soluble in the organic liquid medium is identical with the reactive group present in one of the polymer-forming reactants.
Claim 8
Dependent Claim
44 words
A process as claimed in claim 1, wherein the reactive group carried by the polymeric material of molecular weight between 1000 and 20,000 which is soluble in the organic liquid medium is a group capable of reacting rapidly with the polymer-forming reactant or reactants.
Claim 9
Dependent Claim
73 words
A process as claimed in claim 7, wherein the polymerisation reaction involves the reaction of amino and/or hydroxyl groups together with carboxyl groups, or chemical equivalents thereof, and the reactive group in the polymeric material of molecular weight between 1000 and 20,000 is selected from acid anhydride groups, epoxide groups, oxetane groups, lactone groups, azlactone groups, N-carboxyanhydride groups, isocyanate groups, isothiocyanate groups, azide groups, azidoformate groups, reactive ester groups and substituted urea groups.
Claim 10
Dependent Claim
34 words
A process as claimed in claim 8, wherein the polymeric material containing the reactive group is a maleinised polybutadiene of molecular weight 1500-2000 containing on average approximately 1 succinic anhydride residue per polymer chain.
Claim 11
Dependent Claim
29 words
A process as claimed in claim 8, wherein the polymeric material containing the reactive group is a polybutadiene of molecular weight 12,000 chain-terminated by a single glycidyl ether grouping.
Claim 12
Dependent Claim
26 words
A process as claimed in claim 8, wherein the polymeric material containing the reactive group is the glycidyl ester of poly(12-hydroxystearic acid) of molecular weight 1450-2000.
Claim 13
Dependent Claim
28 words
A process as claimed in claim 8, wherein the polymeric material containing the reactive group is a 97/3 lauryl methacrylate/methacrylic anhydride copolymer of weight average molecular weight 18,000.
Claim 14
Dependent Claim
30 words
A process as claimed in claim 1, wherein the proportion used of the polymeric material containing the reactive group is from 0.1% to 25% by weight of the disperse polymer.
Claim 15
Dependent Claim
21 words
A process as claimed in claim 13, wherein the proportion of the polymeric material is from 0.5% to 25% by weight.
Claim 16
Dependent Claim
26 words
A process as claimed in claim 1, wherein the concentration of the polymer-forming reactants is from 10% to 80% by volume of the total reaction mixture.
Claim 17
Dependent Claim
16 words
A dispersion of a condensation polymer whenever prepared by a process as claimed in claim 1.
References Cited (Backward Citations)
US3390206A
Cited
US3532663A
Cited
US3634303A
Cited
US3925295A
Cited
US3917741A
Cited
US3981839A
Cited
US4000218A
Cited
US4059557A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-21 | 1984-04-21 | 1984-10-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-21 | 1988-04-21 | 1988-10-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-21 | 1992-04-21 | 1992-10-21 | $7700.00 | Window Closed / Lapsed |