Polymer dispersions
Assignee: Imperial Chemical Industries Ltd
•
Filing: 1976-04-19
•
Granted: 1977-11-22
•
Expires: 1996-04-19
Abstract
Abstract A process is described for the production of a stable dispersion of a copolymer, in particular of a copolyester, copolyamide or copolyesteramide, in a non-solvent organic liquid. The process involves the steps of (1) dispersing two or more comonomers, each of which is capable of undergoing homopolymerization and is solid at the copolymerization temperature, in the liquid with the aid of a defined monomer-stabilizing agent and so as to produce monomer particles no larger than 50 mu , and (2) heating the dispersion so obtained so as to bring about copolymerization, in the presence of a defined polymer-stabilizing agent. The copolymers so produced are believed to be different in structure from those obtained from the same comonomers by melt or solution copolymerization.
Inventors
- 👤 John Bentley
- 👤 Morice William Thompson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:48
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/02; C08G63/12; C08G63/16; C08G63/18; C08G63/19; C08G69/00; C08G69/02; C08G69/04; C08G85/00
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
230 words
A process for the production of a stable dispersion of particles of a copolymer selected from the group consisting of copolyester, copolyamide and copolyesteramide in an inert organic liquid medium in which the copolymer is insoluble by the copolymerization of two or more reactive comonomers each of which is capable of undergoing homopolymerization and each of which is solid at the temperature at which the copolymerization reaction takes place and is insoluble in the liquid medium at that temperature, the process comprising the steps of (1) dispersing the solid comonomers in an inert organic liquid in the presence of at least one monomerstabilizing agent so as to produce stably dispersed particles of the comonomers having a mean diameter not greater than 50μ, each monomer-stabilizing agent being per se soluble in the inert organic liquid and incorporating (i) a polymeric component which is solvatable by the liquid and (ii) a grouping which is capable of becoming associated with the particles of solid comonomer and (2) heating the dispersion of solid comonomers at the copolymerization temperature so as to bring about the copolymerization reaction, in the presence of a copolymerstabilizing agent which is per se soluble in the inert organic liquid and incorporated (a) a polymeric component which is solvatable by the liquid and (b) a grouping which is capable of effecting association with the resulting copolymer as the copolymer is formed.
Claim 2
Dependent Claim
230 words
A process for the production of a stable dispersion of particles of a copolymer selected from the group consisting of copolyester, copolyamide and copolyesteramide in an inert organic liquid medium in which the copolymer is insoluble by the copolymerization of two or more reactive comonomers each of which is capable of undergoing homopolymerization and each of which is solid at the temperature at which the copolymerization reaction takes place and is insoluble in the liquid medium at that temperature, the process comprising the steps of (1) dispersing the solid comonomers in an inert organic liquid in the presence of at least one monomerstabilizing agent so as to produce stably dispersed particles of the comonomers having a mean diameter not greater than 50μ, each monomer-stabilizing agent being per se soluble in the inert organic liquid and incorporating (i) a polymeric component which is solvatable by the liquid and (ii) a grouping which is capable of becoming associated with the particles of solid comonomer and (2) heating the dispersion of solid comonomers at the copolymerization temperature so as to bring about the copolymerization reaction, in the presence of a copolymerstabilizing agent which is per se soluble in the inert organic liquid and incorporated (a) a polymeric component which is solvatable by the liquid and (b) a grouping which is capable of effecting association with the resulting copolymer as the copolymer is formed.
Claim 3
Dependent Claim
31 words
A process as claimed in claim 1, wherein any by-product of the copolymerisation reaction is capable of forming an azeotrope with the inert organic liquid medium or with a constituent thereof.
Claim 4
Dependent Claim
23 words
A process as claimed in claim 1, wherein the particle size of the comonomers in dispersion is in the range 0.1 - 10μ.
Claim 5
Dependent Claim
50 words
A process as claimed in claim 1, wherein the monomer-stabilising agent contains a plurality of groups capable of becoming associated with the particles of solid monomer, the said groups forming part of, or being attached to, a polymeric backbone to which the solvatable components are also attached as pendant groups.
Claim 6
Dependent Claim
30 words
A process as claimed in claim 4, wherein the polymeric backbone of the monomer-stabilising agent is flexible under the conditions of dispersing the solid monomers in the inert organic liquid.
Claim 7
Dependent Claim
27 words
A process as claimed in claim 1, wherein the total amount of monomer-stabilising agent used is from 0.1% to 20% by volume of the dispersed monomer phase.
Claim 8
Dependent Claim
30 words
A process as claimed in claim 1, wherein the solvatable polymeric group of the polymerstabilising agent is of a similar type to the solvatable polymeric group of the monomer-stabilising agent.
Claim 9
Dependent Claim
31 words
A process as claimed in claim 1, wherein the grouping of the polymer-stabilising agent which effects association with the polymer is a polymeric grouping of similar composition to the polymer itself.
Claim 10
Dependent Claim
38 words
A process as claimed in claim 8, wherein the polymerassociating grouping of the polymer-stabilising agent is produced during the course of the polymerisation reaction by participation in that reaction of a reactive grouping present in the polymer-stabilising agent.
Claim 11
Dependent Claim
62 words
A process as claimed in claim 1, wherein there is used a single stabilising agent capable of acting as both monomer-stabilising agent and polymer-stabilising agent, the agent comprising (i) a solvatable polymeric component, (ii) a grouping capable of anchoring the agent to the particles of solid monomer and (iii) a grouping capable of effecting association of the agent with the polymer formed.
Claim 12
Dependent Claim
56 words
A process as claimed in claim 10, wherein reactive groups present in the single stabilising agent which are capable of participating in the polymerisation reaction are located in a portion of the molecule of the stabilising agent remote from the solvatable component thereof or from the grouping capable of anchoring the agent to the monomer particles.
Claim 13
Dependent Claim
47 words
A process as claimed in claim 10, wherein the single stabilising agent is a graft copolymer of which one polymeric component is a residue of poly(12-hydroxystearic acid) or of poly(tertbutylstyrene) and another polymeric component is an ethyl acrylate copolymer containing a minor proportion of pendant carboxyl groups.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-11-21 | 1981-05-23 | 1981-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-11-21 | 1985-05-23 | 1985-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-11-21 | 1989-05-23 | 1989-11-22 | $7700.00 | Window Closed / Lapsed |