Manufacture of a titanium-containing component for catalysts of the Ziegler-Natta type

Claim 1

A process for the manufacture of a titanium-containing component of a catalyst for the Ziegler-Natta homopolymerization or copolymerization of α-monoolefins of 3 to 6 carbon atoms, by milling together (a) a titanium-containing compound of the general formula TiCl.sub.3.nAlCl.sub.3 where n is a number from 0.01 to 1 and (b) an ester of a total of 2 to 34 carbon atoms, having the general formula R.sup.3 --O--CO--R.sup.4 or ##STR3## where R 3 is (I) alkyl of 1 to 16 carbon atoms or (II) phenylalkyl of a total of 7 to 23 carbon atoms, in which up to 5 hydrogens of the phenyl may be substituted by alkyl of 1 to 4 carbon atoms, and R 4 is (I) hydrogen, (II) alkyl of 1 to 18 carbon atoms, (III) phenylalkyl of a total of 7 to 23 carbon atoms, in which up to 5 hydrogens of the phenyl may be substituted by alkyl of 1 to 4 carbon atoms, (IV) phenyl or (V) alkylphenyl of a total of 7 to 23 carbon atoms, in which up to 4 hydrogens of the phenyl may be substituted by alkyl of 1 to 5 carbon atoms, wherein (1) a vibratory ball mill having a milling acceleration of from 30 to 80 m.sec -2 is used, (2) the mill is first charged with the titanium-containing compound (a), after which it is run at from -50° to +100° C. for a period of from 0.5 to 100 hours in the absence of a diluent, thereafter (3) whilst milling, with the material in the mill at from -50° to +80° C., the amount of the ester (b) which corresponds to a molar ratio of aluminum in the titanium-containing compound (a) to ester (b) of from 1:5 to 1:0.05 is added continuously or in small portions, at a rate of from 0.01 to 200 ml per minute per 2.5 kg of titanium-containing compound (a), in the absence of a diluent, then (4) the material in the mill is brought to from +10° to +100° C. whilst being milled, and is kept in this temperature range for from 5 to 150 hours, after which (5) the product obtained from stage (4) is washed with at least 0.6 times its amount by weight of a hydrocarbon which is liquid under normal conditions and boils below 150° C., and is dried, and following which (6) the product obtained from stage (5) is milled for a period of from 5 to 60 minutes at from -50° to -10° C. in the absence of a diluent, next (7) the product obtained from stage (6) is brought together with at least 0.5 times its amount by weight of a promoter of the general formula SiX.sub.x R.sup.5.sub.4-x with the proviso that if two or more radicals R 5 are present in the compound, these radicals are identical with one another, or of the general formula SiX.sub.y R.sup.5.sub.4-y with the proviso that if two or more radicals R 5 are present in the compound, at least two of these radicals are different from one another, or of the general formula SnX.sub.y R.sup.5.sub.4-y, Si(OR.sup.5).sub.z R.sup.5.sub.4-z or SiPhR.sup.5.sub.3 with the proviso that if two or more radicals R 5 are present in the compound, these radicals are identical with one another or at least two of these radicals are different from one another, in which general formulae x is from 0 to 4, y is from 0 to 3, z is from 1 to 3, X is halogen, R 5 is (I) hydrogen, with the proviso that in none of the compounds more than three of these radicals are hydrogen , (II) alkyl of 1 to 12 carbon atoms or (III) phenyl, and Ph is phenyl, in which from 0 to 5 hydrogens of the phenyl may be substituted by alkyl or alkoxy of 1 to 5 carbon atoms, phenyl or phenoxy, chlorine or trialkylsilyl, where alkyl is of 1 to 5 carbon atoms, and the batch is kept at from 0° to 250° C. for a period of from 0.2 to 10 hours and is separated into a solid-phase product and a liquid-phase product, and thereafter (8) the solid-phase product obtained from stage (7) is washed with at least 0.4 times its amount by weight of a hydrocarbon which is liquid under normal conditions and boils below 150° C. or of a promoter listed under (7), and is dried, following which (9) the product obtained from stage (8) is milled for a period of from 5 to 60 minutes at from -50° to 0° C. in the absence of a diluent.