Method for producing refractories
Assignee: Shinagawa Refractories Co Ltd
•
Filing: 1979-01-15
•
Granted: 1980-10-21
•
Expires: 1999-01-15
Abstract
Abstract A method for producing refractories which comprises the steps: continuously feeding as a raw material a heavy oil having a boiling point higher than 150 DEG C. obtained by thermal cracking or steam cracking of petroleum hydrocarbons in a first state stirring vessel maintained at a pressure of higher than 2 Kg/cm2G and a temperature within the range of from 300 DEG to 360 DEG C.; maintaining said raw material oil at an average residence time of longer than 15 minutes; continuously withdrawing a first stage treated oil from said first stage stirring vessel; supplying said first stage treated oil in a second stage stirring vessel maintained at a temperature within the range of from 370 DEG to 450 DEG C.; continuously withdrawing a second stage treated oil from said second stage stirring vessel while maintaining said first stage treated oil at an average residence time of from 30 minutes to 10 hours; continuously obtaining pitch by eliminating lighter components from said second stage treated oil; and producing unburned refractories and refractories, the former being obtained by mixing said pitch with basic refractory materials, followed by molding, and the latter being obtained by impregnating and filling said pitch in open porous portions of refractories.
Inventors
- 👤 Seiichi Uemura
- 👤 Syunichi Yamamoto
- 👤 Takao Hirose
- 👤 Hiroaki Takashima
- 👤 Osamu Kato
- 👤 Minoru Nagai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:22
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B35/00; C04B35/01; C04B35/013; C04B41/45; C04B41/46; C04B41/47; C04B41/478; C04B41/80; C04B41/81; C04B41/82; C10; C10C; C10C3/00; C10C3/002
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
180 words
A method for producing unburned refractories which comprises the steps; continuously feeding a heavy oil having a boiling point more than 150° C. obtained by thermal cracking or steam cracking of petroleum hydrocarbons as a raw material oil in a first stage stirring vessel maintained at a pressure of more than 2 Kg/cm 2 G and at a temperature in the range of from 300° to 360° C.; maintaining the average residence time of said raw material oil at a time of more than 15 minutes; continuously withdrawing a first stage treated oil from said first stage stirring vessel; supplying said first stage treated oil in a second stage stirring vessel maintained at a temperature from 370° C. to 450° C.; continuously withdrawing a second stage treated oil from said second stage stirring vessel while maintaining the average residence time of said oil therein at a time of from 30 minutes to 10 hours; continuously obtaining a pitch by eliminating lighter components from said second stage treated oil; and producing unburned refractories by mixing said pitch with basic refractory materials.
Claim 2
Independent Claim
180 words
A method for producing unburned refractories which comprises the steps; continuously feeding a heavy oil having a boiling point more than 150° C. obtained by thermal cracking or steam cracking of petroleum hydrocarbons as a raw material oil in a first stage stirring vessel maintained at a pressure of more than 2 Kg/cm 2 G and at a temperature in the range of from 300° to 360° C.; maintaining the average residence time of said raw material oil at a time of more than 15 minutes; continuously withdrawing a first stage treated oil from said first stage stirring vessel; supplying said first stage treated oil in a second stage stirring vessel maintained at a temperature from 370° C. to 450° C.; continuously withdrawing a second stage treated oil from said second stage stirring vessel while maintaining the average residence time of said oil therein at a time of from 30 minutes to 10 hours; continuously obtaining a pitch by eliminating lighter components from said second stage treated oil; and producing unburned refractories by mixing said pitch with basic refractory materials.
Claim 3
Independent Claim
182 words
A method for producing refractories which comprises the steps; continuously feeding a heavy oil having a boiling point more than 150° C. obtained by thermal cracking or steam cracking of petroleum hydrocarbons as a raw material oil in a first stage stirring vessel maintained at a pressure of more than 2 Kg/cm 2 G and at a temperature in the range of from 300° to 360° C.; maintaining the average residence time of said raw material oil at a time of more than 15 minutes; continuously withdrawing a first stage treated oil from said first stage stirring vessel; supplying said first stage treated oil in a second stage stirring vessel maintained at a temperature from 370° to 450° C.; continuously withdrawing a second stage treated oil from said second stage stirring vessel while maintaining the average residence time of said oil therein at a time of from 30 minutes to 10 hours; continuously obtaining a pitch by eliminating lighter components from said second stage treated oil; and producing refractories by impregnating and filling said pitch in the porous portions of burned refractories.
Claim 4
Independent Claim
182 words
A method for producing refractories which comprises the steps; continuously feeding a heavy oil having a boiling point more than 150° C. obtained by thermal cracking or steam cracking of petroleum hydrocarbons as a raw material oil in a first stage stirring vessel maintained at a pressure of more than 2 Kg/cm 2 G and at a temperature in the range of from 300° to 360° C.; maintaining the average residence time of said raw material oil at a time of more than 15 minutes; continuously withdrawing a first stage treated oil from said first stage stirring vessel; supplying said first stage treated oil in a second stage stirring vessel maintained at a temperature from 370° to 450° C.; continuously withdrawing a second stage treated oil from said second stage stirring vessel while maintaining the average residence time of said oil therein at a time of from 30 minutes to 10 hours; continuously obtaining a pitch by eliminating lighter components from said second stage treated oil; and producing refractories by impregnating and filling said pitch in the porous portions of burned refractories.
Claim 5
Dependent Claim
24 words
A method according to claim 1 or 2, wherein the pitch comprises substantially a heavy oil having a boiling point higher than 400° C.
Claim 6
Dependent Claim
29 words
A method according to claim 1, wherein the basic refractory material is at least one member selected from the group consisting of dolomite-containing refractory materials and magnesia-containing refractory materials.
Claim 7
Dependent Claim
30 words
A method according to claim 2, wherein the burned refractories are selected from the group consisting of burned dolomite-containing brick, burned magnesia-dolomite-containing brick, burned alumina-containing brick and burned magnesia-spinel-containing brick.
Claim 8
Independent Claim
88 words
A method according to claims 1 or 2 wherein said first stage stirring vessel is maintained at a pressure of 2-30 Kg/cm 2 G and a temperature of 330°-350° C., the average residence time of said raw material oil in said first stage stirring vessel is 1-5 hours, said second stage stirring vessel is maintained at a temperature of 390°-430° C. and a pressure of 2-20 Kg/cm 2 G and said oil is maintained in said second stage stirring vessel for an average residence time of 1-5 hours.
Claim 9
Dependent Claim
34 words
A method as claimed in claim 6 wherein the pressure in said first stage stirring vessel is 5-20 Kg/cm 2 G and the pressure in said second stirring vessel is 5-15 Kg/cm 2 G.
Claim 10
Dependent Claim
27 words
A method according to claim 3 wherein said pitch has a softening point of less than 100° C. and a fixed carbon content of at least 45%.
References Cited (Backward Citations)
US3497581A
Cited
US3664853A
Cited
US3994738A
Cited
US3826662A
Cited
US4022739A
Cited
US4008194A
Cited
US4072531A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-21 | 1984-04-21 | 1984-10-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-21 | 1988-04-21 | 1988-10-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-21 | 1992-04-21 | 1992-10-21 | $7700.00 | Window Closed / Lapsed |