Abstract A threadlocking composition for mating threaded fasteners utilizes an epoxy resin system with a component adapted to effect dispersion of lubricants or other organic films on the mating threaded surfaces to thereby improve the threadlocking capabilities thereof without requiring pretreatment. The threadlocking composition comprises an epoxy resin, an amine hardener therefor and 1-25 percent of an aminoalcohol compound which is soluble in the resin/hardener system and wherein the amine and hydroxyl groups are disposed on a carbon chain and on different carbon atoms of that chain. In using the composition, it is placed upon the threads of at least one of the cooperating members which are then assembled and allowed to remain so assembled to produce curing of the epoxy composition. Pretreatment of the fastener surfaces is not required. At the end of three hours, this results in an increase in the torque required for disassembly to a level equal to at least 75 percent of the torque required for assembly. However, the epoxy composition remains substantially free from bonding to the threaded members so as to permit the disassembly when required. Further increases in disassembly torque result from further curing.
An epoxy resin threadlocking composition consisting essentially of: A. 30-70 percent by weight of an epoxy resin; B. 30-70 percent by weight of an amine hardener component therefor; C. up to 25 percent by weight of a polyfunctional amine accelerator therefor; D. up to 10 percent by weight of an inert filler; and E. 1-25 percent by weight of an aminoalcohol compound soluble in the resin/hardener system and wherein the amine and hydroxyl groups are dispersed on a carbon chain and on different carbon atoms of that chain.
Claim 2
Dependent Claim
88 words
An epoxy resin threadlocking composition consisting essentially of: A. 30-70 percent by weight of an epoxy resin; B. 30-70 percent by weight of an amine hardener component therefor; C. up to 25 percent by weight of a polyfunctional amine accelerator therefor; D. up to 10 percent by weight of an inert filler; and E. 1-25 percent by weight of an aminoalcohol compound soluble in the resin/hardener system and wherein the amine and hydroxyl groups are dispersed on a carbon chain and on different carbon atoms of that chain.
Claim 3
Dependent Claim
14 words
The threadlocking composition of claim 1 wherein said aminoalcohol compound is an aliphatic compound.
Claim 4
Dependent Claim
12 words
The threadlocking composition of claim 2 wherein said aminoalcohol compound is 2-dimethylaminoethanol.
Claim 5
Dependent Claim
37 words
The threadlocking composition of claim 1 wherein said epoxy resin comprises 40-55 percent, said hardener component comprises 35-55 percent, said accelerator comprises 2-15 percent, and said aminoalcohol comprises 2-15 percent, all by weight of said threadlocking composition.
Claim 6
Dependent Claim
18 words
The threadlocking composition of claim 1 wherein said polyfunctional amine accelerator includes at least two tertiary amine groups.
Claim 7
Dependent Claim
15 words
The threadlocking composition of claim 5 wherein said polyfunctional amine accelerator is a (dialkyl aminomethyl)phenol.
Claim 8
Dependent Claim
40 words
The threadlocking composition of claim 1 wherein a volume of 10 grams of said composition has a pot life of at least 5 minutes at ambient temperature and, upon curing, has an adhesive shear strength of less than 50 psi.