Novel spraying composition, method of applying the same and article produced thereby
Assignee: Ceradyne Inc
•
Filing: 1978-05-19
•
Granted: 1980-10-07
•
Expires: 1998-05-19
Abstract
Abstract This application discloses a new powder composition which may be plasma sprayed onto the surface of an article to provide a protective coating therefor. The protective coating may be resistant to heat, wear, and corrosion. The coating may also provide a thermal or radiation barrier. In particular, the coating composition for arc plasma spraying consists of finely divided silicon carbide mixed with finely divided silicon. This coating composition is applied to a substrate by developing a plasma spray, feeding the coating composition to the plasma spray and directing the plasma spray at an exposed surface of the substrate so that the exposed substrate is coated with a coating which consists essentially of beta silicon carbide and silicon. The new article of manufacture disclosed in this application, is a substrate with a tightly adherent coating thereon consisting essentially of beta silicon carbide and silicon. The substrate may be any material, either metallic or non-metallic, to which the coating adheres. The coating may provide the substrate with wear resistant characteristics as, for example, if the substrate is to be used for machining metals or as a valve seat in an aluminum engine. The substrate, with the coating thereon, may be used to withstand severe temperatures as, for example, in rocket nozzles and other areas where a substrate would be subjected to extreme temperatures.
Inventors
- 👤 Leslie L. Terner
- 👤 David Moskowitz
- 👤 Roy L. Van Alsten
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 12:33
CPC Classifications
C; C23; C23C; C23C4/00; C23C4/04; B; B23; B23B; B23B27/00; B23B27/14; B23B27/148; C04; C04B; C04B41/00; C04B41/45; C04B41/50; C04B41/5053; C04B41/5057; C04B41/5059; C23C4/06
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
50 words
As a new article of manufacture: a substrate, and, a tightly adherent wear and heat resistant coating on said substrate composed of beta silicon carbide and silicon, said coating being applied to said substrate by a plasma spray of a finely divided mixture consisting essentially of silicon carbide and silicon.
Claim 2
Dependent Claim
50 words
As a new article of manufacture: a substrate, and, a tightly adherent wear and heat resistant coating on said substrate composed of beta silicon carbide and silicon, said coating being applied to said substrate by a plasma spray of a finely divided mixture consisting essentially of silicon carbide and silicon.
Claim 3
Dependent Claim
70 words
The new article of manufacture as defined in claim 1, wherein said finely divided mixture for plasma spraying consisting essentially of silicon carbide and silicon is formed from individual silicon carbide particles having a size range in the range from 100 mesh (149 microns) to 325 mesh (44 microns) and individual silicon particles having a size range in the range from 180 mesh (85 microns) to 325 mesh (44 microns).
Claim 4
Dependent Claim
65 words
The new article of manufacture as defined in claim 1, wherein said finely divided mixture consisting essentially of silicon carbide and silicon is formed from silicon carbide in the form of beta silicon carbide microballons having diameters in the range from 5 to 120 microns and silicon particles having a size range in the range from 180 mesh 85 microns) to 325 mesh (44 microns).
Claim 5
Dependent Claim
35 words
The new article of manufacture as defined in either claims 2 or 3, wherein silicon carbide forms from at least 70 to 90% by Volume of said finely divided mixture of silicon carbide and silicon.
Claim 6
Dependent Claim
34 words
The new article of manufacture as defined in either claims 2 or 3, wherein said silicon carbide forms from 80 to 85% by volume of said finely divided mixture of silicon carbide and silicon.
Claim 7
Independent Claim
64 words
A method of developing a coating on a substrate which comprises: developing a plasma spray, feeding a mixture of finely divided silicon carbide and silicon to said plasma spray, and directing said plasma spray at an exposed surface of the substrate whereby said exposed surface is coated with a tightly adherent wear and heat resistant coating consisting essentially of beta silicon carbide and silicon.
Claim 8
Independent Claim
64 words
A method of developing a coating on a substrate which comprises: developing a plasma spray, feeding a mixture of finely divided silicon carbide and silicon to said plasma spray, and directing said plasma spray at an exposed surface of the substrate whereby said exposed surface is coated with a tightly adherent wear and heat resistant coating consisting essentially of beta silicon carbide and silicon.
Claim 9
Dependent Claim
80 words
The method of developing a tightly adherent wear and heat resistant coating on a substrate as defined in claim 6, wherein said finely divided mixture for plasma spraying consisting essentially of silicon carbide and silicon is formed from individual silicon carbide particles having a size range in the range from 100 mesh (149 microns) to 325 mesh (44 microns) and individual silicon particles having a size range in the range from 180 mesh (85 microns) to 325 mesh (44 microns).
Claim 10
Dependent Claim
75 words
The method of developing a tightly adherent wear and heat resistant coating on a substrate as defined in claim 6, wherein said finely divided mixture consisting essentially of silicon carbide and silicon is formed from silicon carbide in the form of beta silicon carbide microballoons having diameters in the range from 5 to 120 microns and silicon particles having a size range in the range from 180 mesh (85 microns) to 325 mesh (44 microns).
Claim 11
Dependent Claim
47 words
The method of developing a tightly adherent wear and heat resistant coating on a substrate as defined in either claim 7 or 8, wherein silicon carbide forms from at least 70 to 90% by volume of the finely divided mixture consisting essentially of silicon carbide and silicon.
Claim 12
Dependent Claim
43 words
The method of developing a tightly adherent wear and heat resistant coating on a substrate as defined in either claim 7 or 8, wherein silicon carbide forms from 80 to 85% by volume of said finely divided mixture of silicon carbide and silicon.
Claim 13
Independent Claim
115 words
A method of forming a tightly adherent wear and heat resistant coating on a substrate comprising: projecting onto an exposed surface of the substrate by means of a plasma spray gun both silicon carbide and silicon, said silicon carbide being sublimed to the gaseous state and broken down to silicon and carbon by the plasma spray gun and said silicon being vaporized to the gaseous state by the plasma spray gun, a portion of said gaseous materials condensing on said substrate, the carbon condensing on said substrate reacting with silicon condensing on said substrate to form beta silicon carbide thereby to form a beta silicon carbide, silicon phase coating which is adherent to said substrate.
Claim 14
Independent Claim
115 words
A method of forming a tightly adherent wear and heat resistant coating on a substrate comprising: projecting onto an exposed surface of the substrate by means of a plasma spray gun both silicon carbide and silicon, said silicon carbide being sublimed to the gaseous state and broken down to silicon and carbon by the plasma spray gun and said silicon being vaporized to the gaseous state by the plasma spray gun, a portion of said gaseous materials condensing on said substrate, the carbon condensing on said substrate reacting with silicon condensing on said substrate to form beta silicon carbide thereby to form a beta silicon carbide, silicon phase coating which is adherent to said substrate.
Claim 15
Dependent Claim
80 words
The method of forming a tightly adherent wear and heat resistant coating on a substrate as defined in claim 11, wherein said finely divided mixture for plasma spray consisting essentially of silicon carbide and silicon is formed from individual silicon carbide particles having a size range in the range from 100 mesh (149 microns) to 325 mesh (44 microns) and individual silicon particles having a size range in the range from 180 mesh (85 microns) to 325 mesh (44 microns).
Claim 16
Dependent Claim
74 words
The method of forming a tightly adherent wear and heat resistant coating on a substrate as defined in claim 11, wherein said finely divided mixture consisting essentially of silicon carbide and silicon is formed from silicon carbide in the form of beta silicon carbide microballoons having diameters in the range from 5 to 120 microns and silicon particles having size range in the range frim 180 mesh (85 microns) to 325 mesh (44 microns).
Claim 17
Dependent Claim
45 words
The method of forming a tightly adherent wear and heat resistant coating on a substrate as defined in either claim 12 or 13, wherein silicon carbide forms from at least 70 to 90% by volume of said finely divided mixture of silicon carbide and silicon.
Claim 18
Dependent Claim
44 words
The method of forming a tightly adherent wear and heat resistant coating on a substrate as defined in either claim 12 or 13, wherein said silicon carbide forms from 80 to 85% by volume of said finely divided mixture of silicon carbide and silicon.
References Cited (Backward Citations)
US2775531A
Cited
GB716836A
Cited
US3019128A
Cited
US2998322A
Cited
US3095316A
Cited
US3275471A
Cited
US3274007A
Cited
US3419415A
Cited
US3676179A
Cited
US3925577A
Cited
US4075376A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-07 | 1984-04-07 | 1984-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-07 | 1988-04-07 | 1988-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-07 | 1992-04-07 | 1992-10-07 | $7700.00 | Window Closed / Lapsed |