Urea formaldehyde foam with low shrinkage
Assignee: Hexion Inc
•
Filing: 1979-08-06
•
Granted: 1980-09-30
•
Expires: 1999-08-06
Abstract
Abstract This foaming system includes a foaming agent solution and a resin solution. The foaming agent includes the relative amounts of 15 to 30 parts by weight of a salt of an alkyl diphenyl oxide sulfonate, 10 to 25 parts of 85% phosphoric acid and 15 to 25 parts urea, all in an aqueous solution. The resin solution includes a resin prepared by reacting 1 to 2.4 mols of formaldehyde per 1 mol of urea, 6.5 to 500 mmols polyethylene glycol as foam charring agent, 0.3 to 1.2 mmols of calcium carbonate as uniform foam cell size agent, 3 to 310 mmols of dicyandiamide as foam hydrolysis resistance agent, 2 to 30 mmols of sodium bromide as foam aging agent, and sufficient water to make a 35 to 45% solution. In preparing the foam, one part by weight of the foaming agent solution of about 5% solids concentration is aerated and then 1.0 to 1.5 parts by weight of the resin solution is sprayed thereon to obtain foam with an average linear shrinkage of about 0.25%.
Inventors
- 👤 James H. Williams
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:09
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/30; Y; Y10; Y10S; Y10S516/00; Y10S516/01; Y10S516/02; Y10S516/03; Y10S516/05
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
205 words
Foam with very low shrinkage which is prepared from mixing an aqueous foaming agent solution and an aqueous urea-formaldehyde solution, the foaming agent solution comprises the relative amounts, in parts by weight, of 15 to 30 parts of an anionic surfactant selected from salts of diphenyl oxide sulfonates and mixtures thereof, 10 to 25 parts of 85% phosphoric acid, and 15 to 25 parts of urea; the resin solution comprises a condensation product of urea and formaldehyde in the ratio of 1.0 to 2.4 mols of formaldehyde per mol of urea; from 6.5 to 500 mmols of a foaming charring agent selected from ethylene glycol and polyalkylene glycols containing from 2 to 8 carbon atoms in the alkylene moiety and having an average molecular weight no greater than 200, glycerine, pentaerythrytol, sugars and mixtures thereof; from 0.3 to 1.2 mmols of a component to provide uniform cell size in the foam selected from water-soluble alkaline earth metal salts and mixtures thereof; from 3 to 310 mmols of a foam hydrolysis resistance component selected from dicyandiamide, guanylurea, calcium cyanamide, guanidine derivatives, hexamethylene tetramine and mixtures thereof; and from 2 to 30 mmols of a foam aging component selected from water-soluble alkali metal halogens and mixtures thereof.
Claim 2
Dependent Claim
205 words
Foam with very low shrinkage which is prepared from mixing an aqueous foaming agent solution and an aqueous urea-formaldehyde solution, the foaming agent solution comprises the relative amounts, in parts by weight, of 15 to 30 parts of an anionic surfactant selected from salts of diphenyl oxide sulfonates and mixtures thereof, 10 to 25 parts of 85% phosphoric acid, and 15 to 25 parts of urea; the resin solution comprises a condensation product of urea and formaldehyde in the ratio of 1.0 to 2.4 mols of formaldehyde per mol of urea; from 6.5 to 500 mmols of a foaming charring agent selected from ethylene glycol and polyalkylene glycols containing from 2 to 8 carbon atoms in the alkylene moiety and having an average molecular weight no greater than 200, glycerine, pentaerythrytol, sugars and mixtures thereof; from 0.3 to 1.2 mmols of a component to provide uniform cell size in the foam selected from water-soluble alkaline earth metal salts and mixtures thereof; from 3 to 310 mmols of a foam hydrolysis resistance component selected from dicyandiamide, guanylurea, calcium cyanamide, guanidine derivatives, hexamethylene tetramine and mixtures thereof; and from 2 to 30 mmols of a foam aging component selected from water-soluble alkali metal halogens and mixtures thereof.
Claim 3
Dependent Claim
53 words
Foam of claim 1 wherein the surfactant is selected from salts of mono- and di-substituted diphenyl oxide sulfonates, the amount of the charring component is 20 to 250 mmols, that of the uniform cell size component is 0.5 to 0.8 mmols and that of the hydrolysis resistance component is 7 to 30 mmols.
Claim 4
Dependent Claim
65 words
Foam of claim 2 wherein the substituent(s) on the phenyl ring(s) of the surfactant is selected from linear and branched carbon chains, the salts are selected from alkali metal and alkaline earth metal salts of diphenyl oxide sulfonates, the charring component is ethylene glycol, the aging component is sodium bromide, the hydrolysis resistance component is dicyandiamide, and the uniform cell size component is calcium chloride.
Claim 5
Dependent Claim
17 words
Foam of claim 3 wherein the resin solution has a solids concentration of about 30 to 60%.
Claim 6
Dependent Claim
39 words
Foam of claim 4 wherein the foaming agent solution comprises about 50 parts of sodium salt of a branched C 12 carbon chain diphenyl oxide sulfonate, about 15 parts of 85% phosphoric acid and about 17 parts of urea.
Claim 7
Dependent Claim
29 words
Foam of claim 5 wherein the foaming agent solution has a solids concentration of about 5% and the resin solution has a solids concentration of about 35 to 45%.
Claim 8
Dependent Claim
66 words
Foam which is prepared from mixing an aqueous urea-formaldehyde solution and an aqueous agent solution and an aqueous resin solution wherein the foaming agent solution comprises the relative amounts, in parts by weight, of 15 to 30 parts of anionic surfactant selected from salts of diphenyl oxide sulfonates and mixtures thereof, 10 to 25 parts of 85% phosphoric acid, and 15 to 25 parts of urea.
Claim 9
Dependent Claim
66 words
Foam which is prepared from mixing an aqueous urea-formaldehyde solution and an aqueous agent solution and an aqueous resin solution wherein the foaming agent solution comprises the relative amounts, in parts by weight, of 15 to 30 parts of anionic surfactant selected from salts of diphenyl oxide sulfonates and mixtures thereof, 10 to 25 parts of 85% phosphoric acid, and 15 to 25 parts of urea.
Claim 10
Dependent Claim
18 words
Foam of claim 7 wherein the surfactant is selected from salts of mono- and di-substituted diphenyl oxide sulfonates.
Claim 11
Dependent Claim
47 words
Foam of claim 2 wherein the substituent(s) on the phenyl ring(s) of the surfactant is (are) selected from linear and branched carbon chains, the salts are selected from alkali metal and alkaline earth metal salts of diphenyl oxide sulfonates, and the resin solution is urea-formaldehyde resin solution.
Claim 12
Dependent Claim
52 words
Foam of claim 9 wherein the resin solution has a solids concentration of about 30 to 60% and the foaming agent solution comprises about 50 parts of sodium salt of a branched C 12 carbon chain diphenyl oxide sulfonate, about 15 parts of 85% phosphoric acid and about 17 parts of urea.
Claim 13
Dependent Claim
24 words
Foam of claim 10 wherein the foaming agent solution has a solids concentration of about 5% and the resin solution about 35 to 45%.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-30 | 1984-03-31 | 1984-09-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-30 | 1988-03-31 | 1988-09-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-30 | 1992-03-31 | 1992-09-30 | $7700.00 | Window Closed / Lapsed |