Method for applying reacted boron oxide layer to vitreous silica substrate
Assignee: Philips North America LLC
•
Filing: 1979-03-02
•
Granted: 1980-09-30
•
Expires: 1999-03-02
Abstract
Abstract Mercury metal-halide HID lamp having a discharge-sustaining filling comprising sodium halide and scandium halide is improved by providing a thin transparent layer comprising boron oxide adhered to and reacted with the exterior surface portion of the vitreous silica arc tube. Such a coating substantially inhibits migration of sodium ions through the arc tube. The coating also imparts devitrification resistance to any vibreous silica surface to which it is applied. The layer comprising boron oxide preferably is applied to the vitreous silica substrate by forming a clear, partially hydrolyzed solution principally comprising boron alkoxide and silicon alkoxide which is applied to the vitreous silica substrate. The substrate and applied solution are then heated to react the glass-forming constituents of the applied solution with the arc tube.
Inventors
- 👤 Bulent E. Yoldas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 10:19
CPC Classifications
H; H01; H01J; H01J61/00; H01J61/02; H01J61/30; H01J61/35; C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/27; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/23; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/113; C03C2218/30; C03C2218/32; C03C2218/322
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
135 words
The method of applying a thin transparent layer comprising boron oxide to the surface of a vitreous silica substrate, wherein the applied layer comprising boron oxide is adhered to and reacted with the surface of said substrate, said method comprising: a. forming a partially hydrolyzed aqueous clear solution principally comprising boron alkoxide and silicon alkoxide wherein the molar ratio of silicon alkoxide to boron alkoxide is from 0.02 to 0.25; b. applying the formed solution to the surface of the substrate to be coated; and c. heating the substrate and applied coating at a temperature of from about 500° C. to about 1100° C. for a sufficient time to liberate the hydroxyl and organic components from the applied solution and completely react the glass-forming residual constituents of said solution with the surface of said substrate.
Claim 2
Independent Claim
135 words
The method of applying a thin transparent layer comprising boron oxide to the surface of a vitreous silica substrate, wherein the applied layer comprising boron oxide is adhered to and reacted with the surface of said substrate, said method comprising: a. forming a partially hydrolyzed aqueous clear solution principally comprising boron alkoxide and silicon alkoxide wherein the molar ratio of silicon alkoxide to boron alkoxide is from 0.02 to 0.25; b. applying the formed solution to the surface of the substrate to be coated; and c. heating the substrate and applied coating at a temperature of from about 500° C. to about 1100° C. for a sufficient time to liberate the hydroxyl and organic components from the applied solution and completely react the glass-forming residual constituents of said solution with the surface of said substrate.
Claim 3
Dependent Claim
41 words
The method as specified in claim 1, wherein the total water solvent in said formed solution is present in amount not to exceed 1.5 mol water per mol of boron alkoxide plus 1 mol water per 0.25 mol of silicon alkoxide.
Claim 4
Dependent Claim
23 words
The method as specified in claim 1, wherein said boron alkoxide in said solution is trimethylborate and said silicon alkoxide is silicon tetraethoxide.
Claim 5
Independent Claim
210 words
The method of applying a thin transparent layer comprising boron oxide to the surface of a vitreous silica substrate, wherein the applied layer comprising boron oxide is adhered to and reacted with the surface of said substrate, said method comprising: a. forming a partially hydrolyzed aqueous clear solution principally comprising boron alkoxide and silicon alkoxide and alkali metal compound of at least one of soluble sodium or potassium organometallic compound, the amount of said alkali metal organometallic compound in said solution being determined by replacing up to about 20 mole percent of the boron alkoxide of a silicon alkoxide and boron alkoxide solution having a silicon alkoxide to boron alkoxide molar ratio of from 0.02 to 0.25 with said alkali metal organometallic compound, with the atoms of boron in said replaced boron alkoxide approximating the total atoms of alkali metal in said replacing organometallic compound; b. applying the formed solution to the surface of the substrate to be coated; and c. heating the substrate and applied coating at a temperature of from about 500° C. to about 1100° C. for a sufficient time to liberate the hydroxyl and organic components from the applied solution and completely react the glass-forming residual constituents of said solution with the surface of said substrate.
Claim 6
Independent Claim
210 words
The method of applying a thin transparent layer comprising boron oxide to the surface of a vitreous silica substrate, wherein the applied layer comprising boron oxide is adhered to and reacted with the surface of said substrate, said method comprising: a. forming a partially hydrolyzed aqueous clear solution principally comprising boron alkoxide and silicon alkoxide and alkali metal compound of at least one of soluble sodium or potassium organometallic compound, the amount of said alkali metal organometallic compound in said solution being determined by replacing up to about 20 mole percent of the boron alkoxide of a silicon alkoxide and boron alkoxide solution having a silicon alkoxide to boron alkoxide molar ratio of from 0.02 to 0.25 with said alkali metal organometallic compound, with the atoms of boron in said replaced boron alkoxide approximating the total atoms of alkali metal in said replacing organometallic compound; b. applying the formed solution to the surface of the substrate to be coated; and c. heating the substrate and applied coating at a temperature of from about 500° C. to about 1100° C. for a sufficient time to liberate the hydroxyl and organic components from the applied solution and completely react the glass-forming residual constituents of said solution with the surface of said substrate.
Claim 7
Dependent Claim
94 words
The method as specified in claim 4, wherein said alkali metal organometallic compound is potassium organometallic compound, the amount of said potassium organometallic compound in said solution is determined by relacing with said potassium organometallic compound from about 10 mole percent to about 20 mole percent of the boron alkoxide of a silicon alkoxide and boron alkoxide solution having a silicon alkoxide to boron alkoxide molar ratio of from about 0.03 to about 0.13, with the atoms of boron in said replaced boron alkoxide approximating the atoms of potassium in said replacing organometallic compound.
Claim 8
Dependent Claim
15 words
The method as specified in claim 5, wherein said potassium organometallic compound is potassium acetate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-30 | 1984-03-31 | 1984-09-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-30 | 1988-03-31 | 1988-09-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-30 | 1992-03-31 | 1992-09-30 | $7700.00 | Window Closed / Lapsed |