US4224360A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of welding for exfoliation prevention of stainless steel weld-overlay
Assignee: Japan Steel Works Ltd
•
Filing: 1979-02-09
•
Granted: 1980-09-23
•
Expires: 1999-02-09
Abstract
Abstract A welding method for stainless steel overlays is disclosed wherein a welded stainless steel overlay is prevented from exfoliating out of an inner surface of a high pressure vessel. Hydrogen exists at a partial pressure of less than 150 kg/cm2 and a temperature less then 450 DEG C. in the pressure vessel. At least one low alloy steel weld-overlay is preliminarily welded over the inner surface of the pressure vessel. The preliminarily low alloy steel weld-overlay is composed of similar composition to the base metal of the vessel, containing niobium and/or nickel. Thereafter, at least one customary ferritic steel or austenitic steel weld-overlay is welded thereon.
Inventors
- 👤 Keizo Ohnishi
- 👤 Takao Adachi
- 👤 Akiyoshi Fuji
- 👤 Ryuichi Chiba
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 09:22
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/001; B23K35/004; B23K9/00; B23K9/04; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12951; Y10T428/12972; Y10T428/12979
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
139 words
A method of welding for prevention of exfoliation of a stainless steel weld overlay metal on a base metal comprising the steps of: under-laying by welding at least one low alloy steel layer having substantially the same chemical composition as the base metal, said low alloy steel containing niobium of at least eight times the quantity percentage of carbon in the low alloy steel; and overlaying by welding at least one low austenitic or ferritic stainless steel layer on said underlaid layer, whereby exfoliation of the stainless steel overlay is effectively prevented; and wherein said base metal defines a surface of a pressure vessel, said pressure vessel containing hydrogen at a partial pressure of 150 kg/cm 2 or less at a temperature of 450° C. or less and the exfoliation of the stainless steel overlay is due to hydrogen.
Claim 2
Independent Claim
139 words
A method of welding for prevention of exfoliation of a stainless steel weld overlay metal on a base metal comprising the steps of: under-laying by welding at least one low alloy steel layer having substantially the same chemical composition as the base metal, said low alloy steel containing niobium of at least eight times the quantity percentage of carbon in the low alloy steel; and overlaying by welding at least one low austenitic or ferritic stainless steel layer on said underlaid layer, whereby exfoliation of the stainless steel overlay is effectively prevented; and wherein said base metal defines a surface of a pressure vessel, said pressure vessel containing hydrogen at a partial pressure of 150 kg/cm 2 or less at a temperature of 450° C. or less and the exfoliation of the stainless steel overlay is due to hydrogen.
Claim 3
Dependent Claim
16 words
A method as defined in claim 1, wherein the underlaid low alloy metal further includes nickel.
Claim 4
Independent Claim
50 words
A method as defined in claims 1 or 2, wherein the underlaid low alloy metal further includes carbon 0.1% or less, silicon 1.0% or less, manganese 1.0% or less, chrome 3.5% or less, molybdenum 1.5% or less, niobium 1.2% or less, and the remainder iron with or without incidental impurities.
Claim 5
Dependent Claim
13 words
A method as defined in claim 3, wherein nickel is 1.0% or less.
Claim 6
Dependent Claim
13 words
A method as defined in claim 2, wherein nickel is 1.0% or less.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-23 | 1984-03-24 | 1984-09-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-23 | 1988-03-24 | 1988-09-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-23 | 1992-03-24 | 1992-09-23 | $7700.00 | Window Closed / Lapsed |