US4223085A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Semi-conductive nickel carrier particles
Assignee: Xerox Corp
•
Filing: 1976-04-05
•
Granted: 1980-09-16
•
Expires: 1996-04-05
Abstract
Abstract Magnetically-responsive electrostatographic nickel carrier particles having semi-conductive and lower triboelectric charging properties are prepared by heat treating nickel particles in an ambient atmosphere as to provide the carrier particles with an oxide coating. More particularly, commercially available nickel particles are placed in a furnace and the particles are heat treated at a temperature of between about 600° C. and about 1,000° C. for a period of time of between about 5 and 10 minutes. When employed with finely-divided toner particles to develop electrostatic latent images in a magnetic-brush development apparatus, the treated carriers have been found to alleviate shorting problems and to provide developed images having lower background densities and higher resolution than prior carrier materials.
Inventors
- 👤 Robert J. Hagenbach
- 👤 Rudolph Forgensi
- 👤 Stewart W. Volkers
- 👤 Dennis F. Di Orazio
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 11:20
CPC Classifications
G; G03; G03G; G03G9/00; G03G9/08; G03G9/10; G03G9/107; G03G9/1087; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
106 words
A magnetically-responsive electrostatographic carrier particle having an oxide coating, said carrier particle having been prepared by heat treating nickel particles in an ambient atmosphere at a temperature of between about 600° C. and about 1000° C. for between about 5 and about 10 minutes, said carrier particle having an average particle diameter of from between about 30 microns and about 1,000 microns, and wherein said carrier particle is further characterized as having semiconductive properties wherein the surface of said carrier particle has a volume resistivity of between about 10 6 ohm-cm at about 300 volts and up to about 10 8 ohm-cm at about 1,000 volts.
Claim 2
Dependent Claim
106 words
A magnetically-responsive electrostatographic carrier particle having an oxide coating, said carrier particle having been prepared by heat treating nickel particles in an ambient atmosphere at a temperature of between about 600° C. and about 1000° C. for between about 5 and about 10 minutes, said carrier particle having an average particle diameter of from between about 30 microns and about 1,000 microns, and wherein said carrier particle is further characterized as having semiconductive properties wherein the surface of said carrier particle has a volume resistivity of between about 10 6 ohm-cm at about 300 volts and up to about 10 8 ohm-cm at about 1,000 volts.
Claim 3
Dependent Claim
31 words
A magnetically-responsive electrostatographic carrier particle in accordance with claim 1 wherein said oxide coating is present in a thickness at least sufficient to form a thin continuous film on said particle.
Claim 4
Dependent Claim
37 words
A magnetically-responsive electrostatographic carrier particle in accordance with claim 1 wherein said oxide coating is present in an amount of from about 0.4 percent to about 4 percent by weight based on the weight of said particle.
Claim 5
Dependent Claim
141 words
An electrostatographic developer mixture comprising finely-divided toner particles electrostatically clinging to the surface of magnetically-responsive carrier particles having an oxide coating, said carrier particles having been prepared by heat treating nickel particles in an ambient atmosphere at a temperature of between about 600° C. and about 1,000° C. for between about 5 minutes and about 10 minutes, said carrier particles having an average particle diameter of from between about 30 microns and about 1,000 microns, and wherein said carrier particles are characterized as having semiconductive properties wherein the surface of said carrier particles has a volume resistivity of between about 10 6 ohm-cm at about 300 volts and up to about 10 8 ohm-cm at about 1,000 volts, said carrier particles being further characterized as providing developed electrostatographic images having lower background densities and higher resolution than untreated nickel carrier particles.
Claim 6
Dependent Claim
141 words
An electrostatographic developer mixture comprising finely-divided toner particles electrostatically clinging to the surface of magnetically-responsive carrier particles having an oxide coating, said carrier particles having been prepared by heat treating nickel particles in an ambient atmosphere at a temperature of between about 600° C. and about 1,000° C. for between about 5 minutes and about 10 minutes, said carrier particles having an average particle diameter of from between about 30 microns and about 1,000 microns, and wherein said carrier particles are characterized as having semiconductive properties wherein the surface of said carrier particles has a volume resistivity of between about 10 6 ohm-cm at about 300 volts and up to about 10 8 ohm-cm at about 1,000 volts, said carrier particles being further characterized as providing developed electrostatographic images having lower background densities and higher resolution than untreated nickel carrier particles.
Claim 7
Dependent Claim
31 words
An electrostatographic developer mixture in accordance with claim 4 wherein said oxide coating is present in a thickness at least sufficient to form a thin continuous film on said carrier particles.
Claim 8
Dependent Claim
37 words
An electrostatographic developer mixture in accordance with claim 4 wherein said oxide coating is present in an amount of from about 0.4 percent to about 4 percent by weight based on the weight of said carrier particles.
Claim 9
Dependent Claim
199 words
An electrostatographic imaging process comprising the steps of providing an electrostatographic imaging member having a recording surface, forming an electrostatic latent image on said recording surface, and contacting said electrostatic latent image with a developer mixture comprising finely-divided toner particles electrostatically clinging to the surface of magnetically-responsive carrier particles having an oxide coating, said carrier particles having been prepared by heat treating nickel particles in an ambient atmosphere at a temperature of between about 600° C. and about 1000° C. for between about 5 minutes and about 10 minutes, said carrier particles having an average particle diameter of from between about 30 microns and about 1,000 microns, and wherein said carrier particles are characterized as having semiconductive properties wherein the surface of said carrier particles has a volume resistivity of between about 10 6 ohm-cm at about 300 volts and up to about 10 8 ohm-cm at about 1,000 volts, said carrier particles being further characterized as providing developed electrostatographic images having lower background densities and higher resolution than untreated nickel carrier particles, whereby at least a portion of said finely-divided toner particles are attracted to and deposited on said recording surface in conformance with said electrostatic latent image.
Claim 10
Dependent Claim
199 words
An electrostatographic imaging process comprising the steps of providing an electrostatographic imaging member having a recording surface, forming an electrostatic latent image on said recording surface, and contacting said electrostatic latent image with a developer mixture comprising finely-divided toner particles electrostatically clinging to the surface of magnetically-responsive carrier particles having an oxide coating, said carrier particles having been prepared by heat treating nickel particles in an ambient atmosphere at a temperature of between about 600° C. and about 1000° C. for between about 5 minutes and about 10 minutes, said carrier particles having an average particle diameter of from between about 30 microns and about 1,000 microns, and wherein said carrier particles are characterized as having semiconductive properties wherein the surface of said carrier particles has a volume resistivity of between about 10 6 ohm-cm at about 300 volts and up to about 10 8 ohm-cm at about 1,000 volts, said carrier particles being further characterized as providing developed electrostatographic images having lower background densities and higher resolution than untreated nickel carrier particles, whereby at least a portion of said finely-divided toner particles are attracted to and deposited on said recording surface in conformance with said electrostatic latent image.
Claim 11
Dependent Claim
31 words
An electrostatographic imaging process in accordance with claim 7 wherein said oxide coating is present in a thickness at least sufficient to form a thin continuous film on said carrier particles.
Claim 12
Dependent Claim
37 words
An electrostatographic imaging process in accordance with claim 7 wherein said oxide coating is present in an amount of from about 0.4 percent to about 4 percent by weight based on the weight of said carrier particles.
Claim 13
Dependent Claim
103 words
A process for preparing magnetically-responsive electrostatographic carrier particles having an oxide coating, said process comprising heat treating nickel particles in an ambient atmosphere at a temperature of between about 600° C. and about 1000° C. for between about 5 and about 10 minutes, said carrier particles having an average particle diameter of from between about 30 microns and about 1,000 microns, and said carrier particles are characterized as having semiconductive properties wherein the surface of said carrier particles has a volume resistivity of between about 10 6 ohm-cm at about 300 volts and up to about 10 8 ohm-cm at about 1,000 volts.
Claim 14
Dependent Claim
103 words
A process for preparing magnetically-responsive electrostatographic carrier particles having an oxide coating, said process comprising heat treating nickel particles in an ambient atmosphere at a temperature of between about 600° C. and about 1000° C. for between about 5 and about 10 minutes, said carrier particles having an average particle diameter of from between about 30 microns and about 1,000 microns, and said carrier particles are characterized as having semiconductive properties wherein the surface of said carrier particles has a volume resistivity of between about 10 6 ohm-cm at about 300 volts and up to about 10 8 ohm-cm at about 1,000 volts.
Claim 15
Dependent Claim
34 words
A process for preparing magnetically-responsive electrostatographic carrier particles in accordance with claim 10 wherein said oxide coating is present in a thickness at least sufficient to form a thin continuous film on said particles.
Claim 16
Dependent Claim
40 words
A process for preparing magnetically-responsive electrostatographic carrier particles in accordance with claim 10 wherein said oxide coating is present in an amount of from about 0.4 percent to about 4 percent by weight based on the weight of said particles.
References Cited (Backward Citations)
US3632512A
Cited
US3679398A
Cited
US3849182A
Cited
US4018601A
Cited
US3767578A
Cited
US3767477A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-16 | 1984-03-17 | 1984-09-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-16 | 1988-03-17 | 1988-09-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-16 | 1992-03-17 | 1992-09-16 | $7700.00 | Window Closed / Lapsed |