Process for manufacturing a multi-colored display polarizer
Assignee: Sanritsu Electric Co Ltd
•
Filing: 1978-09-12
•
Granted: 1980-09-02
•
Expires: 1998-09-12
Abstract
Abstract A multi-colored display polarizer is manufactured by supporting on a transparent substrate a multi-colored polarizing film which is produced by a required number of repetitions, each using a coloring means producing a different color, a sequence of operations comprising coating a photosensitive resin onto the surface of a polarizing film blank and drying the same, exposing the coated film through a photographic negative having a desired pattern thereon to photo-set a portion of the film corresponding to the transparent portion of the negative, developing the thus exposed film, coloring the thus developed film with a suitable coloring means, and removing the photosensitive resin remaining on said photoset portion of the film.
Inventors
- 👤 Shigeyoshi Sugibuchi
- 👤 Mitsuo Hiramatsu
- 👤 Takeo Aizawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:48
CPC Classifications
G; G02; G02F; G02F1/00; G02F1/01; G02F1/13; G02F1/133; G02F1/1333; G02F1/1335; G02F1/133528; G02F1/133533; G02B; G02B5/00; G02B5/30; G02B5/3025; G02B5/3033
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
265 words
In a process for producing a polarizer comprising a film and a transparent support substrate, the improvement comprising the steps of coating a normally liquid photo-sensitive resin onto the surface of a polyvinyl alcohol film blank oriented in one direction and drying said coating; exposing said coated film blank to light through a first photographic negative to photo-set said photosensitive resin at portions thereof corresponding to transparent portions of said first negative; developing the thus exposed film blank by dissolving and removing the resin remaining on the unexposed portions of said coated film blank to reveal the film blank thereunder; causing ink containing iodine and a first dyestuff to be adsorbed into said oriented film blank at said revealed portions thereof; removing said photo-set resin from the exposed portions of said film blank by use of an organic solvent containing xylene; applying another coating of a photosensitive resin to the thus obtained film blank and drying said coating; exposing said obtained coated film blank to light through a second photographic negative having opaque portions corresponding to the transparent portions of said first photographic negative to photo-set said photosensitive resin at portions corresponding to the transparent portions of said second negative; developing the thus exposed film blank by dissolving and removing the resin remaining on the unexposed portions of said film blank to reveal the film blank thereunder; causing ink containing iodine and a second dyestuff to be adsorbed into said film blank at revealed portions thereof; and removing said photo-set resin from the exposed portions of said film blank, thereby producing a multi-colored display polariser.
Claim 2
Dependent Claim
265 words
In a process for producing a polarizer comprising a film and a transparent support substrate, the improvement comprising the steps of coating a normally liquid photo-sensitive resin onto the surface of a polyvinyl alcohol film blank oriented in one direction and drying said coating; exposing said coated film blank to light through a first photographic negative to photo-set said photosensitive resin at portions thereof corresponding to transparent portions of said first negative; developing the thus exposed film blank by dissolving and removing the resin remaining on the unexposed portions of said coated film blank to reveal the film blank thereunder; causing ink containing iodine and a first dyestuff to be adsorbed into said oriented film blank at said revealed portions thereof; removing said photo-set resin from the exposed portions of said film blank by use of an organic solvent containing xylene; applying another coating of a photosensitive resin to the thus obtained film blank and drying said coating; exposing said obtained coated film blank to light through a second photographic negative having opaque portions corresponding to the transparent portions of said first photographic negative to photo-set said photosensitive resin at portions corresponding to the transparent portions of said second negative; developing the thus exposed film blank by dissolving and removing the resin remaining on the unexposed portions of said film blank to reveal the film blank thereunder; causing ink containing iodine and a second dyestuff to be adsorbed into said film blank at revealed portions thereof; and removing said photo-set resin from the exposed portions of said film blank, thereby producing a multi-colored display polariser.
Claim 3
Dependent Claim
19 words
A process according to claim 1, wherein said polarizing film blank has a thickness of from 18μ to 25μ.
Claim 4
Dependent Claim
22 words
A process according to claim 1 or 2, wherein said photosensitive resin is water-soluble resins having a liquid state under normal conditions.
Claim 5
Dependent Claim
14 words
A process according to claim 3, wherein said water-soluble resins include dichromate type photo-resists.
Claim 6
Dependent Claim
32 words
A process according to claim 4, wherein said dichromate type photoresists are obtained by blending a dichromate with a material selected from the group consisting of insinglass, casein, and polyvinyl alcohol (PVA).
Claim 7
Dependent Claim
13 words
A process according to claim 3, wherein said water-soluble resins include acrylic photo-resists.
Claim 8
Dependent Claim
20 words
A process according to claim 6, wherein said acrylic photo-resists are obtained by copolymerizing a vinyl monomer with methyl methacrylate.
Claim 9
Dependent Claim
22 words
A process according to claim 1 or 2, wherein said photosensitive resin is oil-soluble resins having a liquid state under normal conditions.
Claim 10
Dependent Claim
15 words
A process according to claim 8, wherein said oil-soluble resins include polyvinyl cinnamate type photo-resists.
Claim 11
Dependent Claim
21 words
A process according to claim 9, wherein said polyvinyl cinnamate type photo-resists are obtained by blending a polyvinyl cinnamate with photosensitizers.
Claim 12
Dependent Claim
15 words
A process according to claim 8, wherein said oil-soluble resins include cyclized rubber-azide type photo-resists.
Claim 13
Dependent Claim
24 words
A process according to claim 11, wherein said cyclized rubber-azide type photo-resists are obtained by blending a cyclized rubber with an aromatic bisazide compound.
Claim 14
Dependent Claim
14 words
A process according to claim 12, wherein said aromatic bisazide compound includes 2,6-di(4'azidebenzal)-cyclohexanone, etc.
Claim 15
Dependent Claim
33 words
A process according to claim 1, wherein said removal of the resin on the unexposed portion of the coated film is performed by cleaning off said photo sensitive layer with an organic solvent.
Claim 16
Dependent Claim
23 words
A process according to claim 1, wherein said dyestuff includes a member selected from the group consisting of acid dye and direct dye.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-02 | 1984-03-03 | 1984-09-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-02 | 1988-03-03 | 1988-09-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-02 | 1992-03-03 | 1992-09-02 | $7700.00 | Window Closed / Lapsed |