Paper having good absorbency and alkali resistance and method of making said paper
Assignee: CH Dexter Ltd
•
Filing: 1978-11-24
•
Granted: 1980-08-19
•
Expires: 1998-11-24
Abstract
Abstract Fibrous paper webs of high water absorbency and improved alkaline wet tensile strength are obtained by treating the fibers prior to web formation or subsequent to web formation with aqueous solutions of a water-soluble thermosetting reaction product of a polyamide and an epichlorohydrin, a water-soluble nonviscose film-forming material such as hydroxy ethyl cellulose and a water-soluble polyethylene imine. The resultant absorbent sheet material maintains its absorbency upon aging, exhibits high wet caustic strength and can be used in the manufacture of tea bags or food casings.
Inventors
- 👤 Newlyn Jones
- 👤 Alistair C. Stewart
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 13:27
CPC Classifications
D; D21; D21H; D21H17/00; D21H17/20; D21H17/21; D21H17/24; D21H17/25; D21H17/26; A; A22; A22C; A22C13/00; A22C13/0013; D21H17/33; D21H17/46; D21H17/54; D21H17/55; D21H17/56
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
141 words
A process for the production of absorbent fibrous webs of improved alkaline wet tensile strength comprising the steps of forming a fibrous web material, treating the fibers of the web material with an aqueous solution of a water-soluble cationic, thermosetting, polyamide or polyamine epihalohydrin-containing resin to provide in the web about 0.05% to 4.0% by weight of said resin on a dry weight basis, treating the fibers of the web material with an aqueous solution of a non-viscose film-forming polymer material containing a hydroxyl group to provide in the web about 0.5% to 8.0% by weight of said film-forming material on a dry weight basis and treating the fibers of the web material with an aqueous solution of a polyalkylene imine polymer to provide in the web about 0.05% to 2.0% by weight of said polymer on a dry weight basis.
Claim 2
Dependent Claim
141 words
A process for the production of absorbent fibrous webs of improved alkaline wet tensile strength comprising the steps of forming a fibrous web material, treating the fibers of the web material with an aqueous solution of a water-soluble cationic, thermosetting, polyamide or polyamine epihalohydrin-containing resin to provide in the web about 0.05% to 4.0% by weight of said resin on a dry weight basis, treating the fibers of the web material with an aqueous solution of a non-viscose film-forming polymer material containing a hydroxyl group to provide in the web about 0.5% to 8.0% by weight of said film-forming material on a dry weight basis and treating the fibers of the web material with an aqueous solution of a polyalkylene imine polymer to provide in the web about 0.05% to 2.0% by weight of said polymer on a dry weight basis.
Claim 3
Dependent Claim
32 words
The process of claim 1 wherein the water-soluble cationic, thermosetting epihalohydrin-containing resin, the non-viscose film-forming material and the polyalkylene imine polymer are applied to the fibers after the formation of the web.
Claim 4
Dependent Claim
34 words
The process of claim 1 wherein the water-soluble cationic, thermosetting epihalohydrin-containing resin, the non-viscose film-forming material and the polyalkylene imine polymer are added to the fiber slurry prior to the formation of the web.
Claim 5
Dependent Claim
27 words
The process of claim 1 wherein the water-soluble cationic, thermosetting, epihalohydrin-containing resin, the non-viscose film-forming material and the polyalkylene imine polymer are applied to the fibers simultaneously.
Claim 6
Dependent Claim
13 words
The process of claim 1 wherein the film-forming material is hydroxy ethyl cellulose.
Claim 7
Dependent Claim
14 words
The process of claim 1 wherein the cationic, thermosetting resin is an epichlorohydrin-containing resin.
Claim 8
Dependent Claim
15 words
The process of claim 6 wherein the cationic, thermosetting, epihalohydrin-containing resin is a polyamide-epichlorohydrin resin.
Claim 9
Dependent Claim
22 words
The process of claim 1 wherein the polyalkylene imine polymer is selected from the group consisting of polyethylene imine and copolymers thereof.
Claim 10
Dependent Claim
44 words
The process of claim 1 wherein the treating agents are applied in amounts sufficient to provide, on a dry weight basis, 1% to 2.5% of the epihalohydrin-containing resin, 0.5% to 5% of the film-forming material and 0.1% to 0.8% of the polyalkylene imine polymer.
Claim 11
Dependent Claim
44 words
The process of claim 1 wherein the treating agents are applied in amounts sufficient to provide, on a dry weight basis, 0.05% to 1.0% of the epihalohydrin-containing resin, 0.1% to 5% of the film-forming material and 0.05% to 1.0% of the polyalkylene imine polymer.
Claim 12
Dependent Claim
44 words
The process of claim 10 wherein the treating agents are applied in amounts sufficient to provide, on a dry weight basis, 0.1% to 0.5% of the epihalohydrin-containing resin, 0.3% to 3.0% of the film-forming material and 0.1% to 0.8% of the polyalkylene imine polymer.
Claim 13
Dependent Claim
76 words
A water absorbent fibrous sheet material of improved alkaline wet tensile strength comprising a fibrous web containing about 0.05% to 4.0% by weight on a dry weight basis of a water-soluble cationic, thermosetting polyamide or polyamine epihalohydrin-containing resin, about 0.5% to 8.0% by weight on a dry weight basis of a non-viscose film-forming polymer material containing a hydroxyl group and about 0.5% to 8.0% by weight on a dry weight basis of a polyalkylene imine polymer.
Claim 14
Dependent Claim
76 words
A water absorbent fibrous sheet material of improved alkaline wet tensile strength comprising a fibrous web containing about 0.05% to 4.0% by weight on a dry weight basis of a water-soluble cationic, thermosetting polyamide or polyamine epihalohydrin-containing resin, about 0.5% to 8.0% by weight on a dry weight basis of a non-viscose film-forming polymer material containing a hydroxyl group and about 0.5% to 8.0% by weight on a dry weight basis of a polyalkylene imine polymer.
Claim 15
Dependent Claim
14 words
The sheet material of claim 12 wherein the film-forming material is hydroxy ethyl cellulose.
Claim 16
Dependent Claim
16 words
The sheet material of claim 12 wherein the cationic, thermosetting epihalohydrin-containing resin is a polyamideepichlorohydrin resin.
Claim 17
Dependent Claim
23 words
The sheet material of claim 12 wherein the polyalkylene imine polymer is selected from the group consisting of polyethylene imine and copolymers thereof.
Claim 18
Dependent Claim
43 words
The process of claim 5 wherein the treating agents are applied in amounts sufficient to provide, on a dry weight basis, 1% to 2.5% of the epihalohydrin-containing resin, 0.5% to 5% of hydroxyethyl cellulose and 0.1% to 0.8% of the polyalklyene imine polymer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-08-19 | 1984-02-18 | 1984-08-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-08-19 | 1988-02-18 | 1988-08-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-08-19 | 1992-02-18 | 1992-08-19 | $7700.00 | Window Closed / Lapsed |