Abstract
Abstract A coating (28) is applied over an advancing electrical conductor (21) and partially dried by exposing it to a first temperature for a predetermined time. This renders the coating substantially insoluble in water so that it is retained on the conductor as the conductor is moved through apparatus (34) which forms a ribbon (35) of pulpous material longitudinally with the conductor. The ribbon is reshaped into an insulative cover (41) concentrically disposed about the coated conductor, after which the pulp-insulated conductor is exposed for a predetermined length of time to a second temperature which is substantially greater than the first temperature. This reduces substantially the moisture content of the pulpous material and simultaneously tackifies the coating which cause the pulp insulation to have excellent crush resistance and adheres the pulp insulation to the conductor to form an insulation cover having substantial integrity.
Inventors
- 👤 Helmut E. Durr
- 👤 James G. Wright, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 10:52
CPC Classifications
H; H01; H01B; H01B13/00; H01B13/06; H01B13/12
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
173 words
A method of making a pulp-insulated electrical conductor, said method including the steps of: enclosing an electrical conductor in a coating which is capable of being treated to render the coating substantially insoluble in water and which when covered with a pulpous material comprising a water-pulp mixture is capable of being further treated to create an adhesive bond between the pulpous material and the conductor; treating said electrical conductor which is enclosed in said coating to render the coating substantially insoluble in water; enclosing said electrical conductor and said coating in a pulpous material having a relatively high moisture content and being disposed substantially concentrically about the conductor; and treating said coating and said pulpous material to reduce substantially the moisture content of the pulpous material and, simultaneously, to tackify the coating, which cause the crush resistance of the pulpous material to be increased so that it remains substantially concentrically disposed about the conductor and which cause the pulpous material to adhere to the conductor to form an insulative cover having substantial integrity.
Claim 2
Independent Claim
173 words
A method of making a pulp-insulated electrical conductor, said method including the steps of: enclosing an electrical conductor in a coating which is capable of being treated to render the coating substantially insoluble in water and which when covered with a pulpous material comprising a water-pulp mixture is capable of being further treated to create an adhesive bond between the pulpous material and the conductor; treating said electrical conductor which is enclosed in said coating to render the coating substantially insoluble in water; enclosing said electrical conductor and said coating in a pulpous material having a relatively high moisture content and being disposed substantially concentrically about the conductor; and treating said coating and said pulpous material to reduce substantially the moisture content of the pulpous material and, simultaneously, to tackify the coating, which cause the crush resistance of the pulpous material to be increased so that it remains substantially concentrically disposed about the conductor and which cause the pulpous material to adhere to the conductor to form an insulative cover having substantial integrity.
Claim 3
Independent Claim
203 words
A method of making a pulp-insulated electrical conductor, said method including the steps of: enclosing an electrical conductor in a coating which when exposed for a predetermined time to a first temperature is partially dried to render it substantially insoluble in water and essentially non-tacky, and which when covered with pulpous material and exposed for a predetermined time to a second temperature that is substantially greater than said first temperature is further dried and tackified; exposing said electrical conductor which is enclosed in said coating for a predetermined time to said first temperature; enclosing said electrical conductor, which is enclosed in said coating, in an insulative cover of pulpous material having a relatively high moisture content and being disposed concentrically about the conductor; and exposing said coating and said cover of pulpous material for a predetermined time to said second temperature to reduce substantially the moisture content of the cover of pulpous material and to further dry and to tackify the coating which cause the crush resistance of the pulpous material to be increased so that it remains substantially concentrically disposed about the conductor and which cause the pulpous material to adhere to the conductor to form an insulative cover having substantial integrity.
Claim 4
Independent Claim
203 words
A method of making a pulp-insulated electrical conductor, said method including the steps of: enclosing an electrical conductor in a coating which when exposed for a predetermined time to a first temperature is partially dried to render it substantially insoluble in water and essentially non-tacky, and which when covered with pulpous material and exposed for a predetermined time to a second temperature that is substantially greater than said first temperature is further dried and tackified; exposing said electrical conductor which is enclosed in said coating for a predetermined time to said first temperature; enclosing said electrical conductor, which is enclosed in said coating, in an insulative cover of pulpous material having a relatively high moisture content and being disposed concentrically about the conductor; and exposing said coating and said cover of pulpous material for a predetermined time to said second temperature to reduce substantially the moisture content of the cover of pulpous material and to further dry and to tackify the coating which cause the crush resistance of the pulpous material to be increased so that it remains substantially concentrically disposed about the conductor and which cause the pulpous material to adhere to the conductor to form an insulative cover having substantial integrity.
Claim 5
Dependent Claim
36 words
The method of claim 2 wherein the first temperature is at least about 260° C. and the method further includes the step of advancing the conductor at a rate which is about 61 meters per minute.
Claim 6
Dependent Claim
20 words
The method of claim 2, wherein the second temperature is in the range of about 480° C. to 870° C.
Claim 7
Dependent Claim
17 words
The method of claim 2, wherein the coating is an aqueous emulsion of an acrylic latex copolymer.
Claim 8
Dependent Claim
14 words
The method of claim 5, wherein the coating is an ethyl acrylate-methyl acrylate copolymer.
Claim 9
Dependent Claim
24 words
The method of claim 2, wherein the moisture content of the pulp insulation is in the range of about 3 to 6% by weight.
Claim 10
Dependent Claim
14 words
The method of claim 2, wherein the first temperature is provided by infra-red heat.
Claim 11
Dependent Claim
21 words
The method of claim 2, wherein the thickness of the partially dried coating is in the range of about 0.005 mm.
References Cited (Backward Citations)
US1615418A
Cited
US1615375A
Cited
US1615422A
Cited
US1945538A
Cited
US2191584A
Cited
US2187391A
Cited
US2440802A
Cited
US2934458A
Cited
US3250641A
Cited
US3595720A
Cited
US3521375A
Cited
US3737982A
Cited
US3763554A
Cited
GB1401931A
Cited
US4125645A
Cited
US4113534A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-08-19 | 1984-02-18 | 1984-08-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-08-19 | 1988-02-18 | 1988-08-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-08-19 | 1992-02-18 | 1992-08-19 | $7700.00 | Window Closed / Lapsed |