Polypropylene separator for use in alkaline storage batteries and process for making same
Assignee: Raytheon Co
•
Filing: 1978-10-23
•
Granted: 1980-08-12
•
Expires: 1998-10-23
Abstract
Abstract Intrinsically nonwettable polypropylene battery separators are rendered wettable by treating them with polybenzimidazole. Polybenzimidazole (PBI) treated polypropylene (PP) separators exhibited excellent thermal and chemical stabilities, show excellent electrolyte retention, and are gas permeable.
Inventors
- 👤 Scott A. Verzwyvelt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 14:16
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0081; B01D67/0088; C; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; D; D06; D06M; D06M15/00; D06M15/19; D06M15/37; D06M15/59; H; H01; H01M; H01M50/00; H01M50/40; H01M50/409; H01M50/411; H01M50/414; H01M50/417; H01M50/44; C08J2479/00; H01M2300/00; H01M2300/0002; H01M2300/0014; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
185 words
The process of providing an improved organic separator that is chemically resistant to and wettable by an aqueous KOH solution for use in alkaline storage batteries comprising the steps of: a. providing an uncontaminated fabric comprised of fibers selected from the group consisting of polyethylene, polypropylene, and polybutylene, suitable for use as a separator; b. forming a coating solution by dissolving a polymer selected from the group consisting of polybenzimidazole, polybenzoxazole, and polybenzothiazole in a selected polar solvent; c. immersing said fabric in said solution and allowing said fabric to soak in said solution until saturated while maintaining a constant polymer-solvent concentration; d. sequentially removing said saturated fabric from said soaking solution and removing any excess soaking solution from said fabric thereby leaving said fabric impregnated and coated with the solvent and polymer of said soaking solution; e. causing said solvent to be removed from said coating solution by subjecting said fabric to a solvent removal technique selected from the group consisting of solvent evaporation and solvent precipitation; and f. drying said coated fabric at an elevated temperature prior to use as a battery separator.
Claim 2
Dependent Claim
185 words
The process of providing an improved organic separator that is chemically resistant to and wettable by an aqueous KOH solution for use in alkaline storage batteries comprising the steps of: a. providing an uncontaminated fabric comprised of fibers selected from the group consisting of polyethylene, polypropylene, and polybutylene, suitable for use as a separator; b. forming a coating solution by dissolving a polymer selected from the group consisting of polybenzimidazole, polybenzoxazole, and polybenzothiazole in a selected polar solvent; c. immersing said fabric in said solution and allowing said fabric to soak in said solution until saturated while maintaining a constant polymer-solvent concentration; d. sequentially removing said saturated fabric from said soaking solution and removing any excess soaking solution from said fabric thereby leaving said fabric impregnated and coated with the solvent and polymer of said soaking solution; e. causing said solvent to be removed from said coating solution by subjecting said fabric to a solvent removal technique selected from the group consisting of solvent evaporation and solvent precipitation; and f. drying said coated fabric at an elevated temperature prior to use as a battery separator.
Claim 3
Dependent Claim
21 words
The process of claim 1 wherein said separator fabric is polypropylene, said polymer is polybenzimidazole, and said selected solvent is dimethylacetamide.
Claim 4
Dependent Claim
67 words
An improvement in porous polypropylene separators intended for use in alkaline storage batteries wherein said improvement consists of a thin coating of a stable polymer selected from the group consisting of polybenzimidazole, polybenzoxazole, and polybenzothiazole applied to the surface of said separator, which provides a wettable surface capable of resisting the chemical action of aqueous KOH electrolytes while retaining said electrolytes within the pores of said separator.
Claim 5
Dependent Claim
67 words
An improvement in porous polypropylene separators intended for use in alkaline storage batteries wherein said improvement consists of a thin coating of a stable polymer selected from the group consisting of polybenzimidazole, polybenzoxazole, and polybenzothiazole applied to the surface of said separator, which provides a wettable surface capable of resisting the chemical action of aqueous KOH electrolytes while retaining said electrolytes within the pores of said separator.
Claim 6
Dependent Claim
14 words
The improvement of claim 3 wherein said coating is a thin coating of polybenzimidazole.
Claim 7
Independent Claim
66 words
A method of rendering extrinsically non-wettable polymeric fibers, films, sheet and rod surfaces wettable comprising the steps of providing a thin coating of a wettable polymer selected from the group consisting of polybenzimidazole, polybenzoxazole, and polybenzothiazole deposited onto the surface of said fibers, films, sheets and rods from a polymer-solvent solution, removing said solvent and drying said coating fiber, film, sheet and rod at elevated temperatures.
Claim 8
Independent Claim
66 words
A method of rendering extrinsically non-wettable polymeric fibers, films, sheet and rod surfaces wettable comprising the steps of providing a thin coating of a wettable polymer selected from the group consisting of polybenzimidazole, polybenzoxazole, and polybenzothiazole deposited onto the surface of said fibers, films, sheets and rods from a polymer-solvent solution, removing said solvent and drying said coating fiber, film, sheet and rod at elevated temperatures.
Claim 9
Dependent Claim
37 words
The method of claim 5 wherein said wettable polymer is removed from said polymer solvent solution by a precipitation process which leaves particles of said polymer adhering to the surface of said films, sheets, rods and fibers.
Claim 10
Dependent Claim
20 words
The method of claim 5 wherein said coating is comprised of polybenzimidazole deposited from a solution of polybenzimidazole and dimethylacetamide.
Claim 11
Dependent Claim
104 words
In an alkaline storage battery having electro members spaced apart by organic separators which retain a liquid electrolyte and provide a current path between said electrodes, an improved organic separator comprising a porous substrate of non-wettable fibers selected from the group consisting of polyethylene, polypropylene and polybutylene first polymers having a multiplicity of interstices and a thin layer of thermally stable wettable polybenzimidazole polymer formed around and about said fibers which permanently adheres to said fibers, without altering the structural characteristics of said fibers, to render them wettable in aqueous potassium hydroxide solution and permits the passage of ions and gases through said separator.
Claim 12
Dependent Claim
104 words
In an alkaline storage battery having electro members spaced apart by organic separators which retain a liquid electrolyte and provide a current path between said electrodes, an improved organic separator comprising a porous substrate of non-wettable fibers selected from the group consisting of polyethylene, polypropylene and polybutylene first polymers having a multiplicity of interstices and a thin layer of thermally stable wettable polybenzimidazole polymer formed around and about said fibers which permanently adheres to said fibers, without altering the structural characteristics of said fibers, to render them wettable in aqueous potassium hydroxide solution and permits the passage of ions and gases through said separator.
Claim 13
Dependent Claim
13 words
An improved organic separator of claim 8 wherein said first polymer is polypropylene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-08-12 | 1984-02-11 | 1984-08-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-08-12 | 1988-02-11 | 1988-08-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-08-12 | 1992-02-11 | 1992-08-12 | $7700.00 | Window Closed / Lapsed |