Abstract This invention is directed to a process for forming a wettable battery separator comprising a non-woven mat of polyolefin fiber by forming a non-woven mat of polyolefin fiber having a thickness in the range 10 to 40 mils and pore sizes less than 40 microns, contacting the mat with an aqueous solution of a water soluble peroxy compound, e.g. hydrogen peroxide or potassium persulfate at a temperature below 70 DEG C., rinsing the mat in water and thereafter immersing the thus treated mat in an aqueous solution of a hydrophilic vinyl monomer such as acrylic, methacrylic, vinyl sulfonic acid, said solution containing a redox catalyst, e.g. an ion of a transition metal, e.g. ferrous, cerous, cobaltous, or an organic amine, thereby causing a graft polymerization of said hydrophilic vinyl monomer on said polyolefin mat to give a wettable polyolefin battery separator.
The process of forming a wettable battery separator from a polyolefin which comprises extruding a heated polyolefin through multiple die openings into a gas stream which attenuates the polyolefin into fibers having an average diameter between 1 to about 10 microns, collecting said fibers as a self-supporting mat on a collecting device, compacting the thus formed mat to a thickness between 10 and 40 mils and pore sizes less than 40 microns, contacting the mat with an aqueous solution of a water-soluble, peroxy compound at a temperature below 70° C. without the introduction of oxygen, rinsing the thus contacted mat in a water bath and thereafter at a temperature below 70° C. immersing the thus rinsed mat in an aqueous solution of a hydrophilic vinyl monomer of the formula ##STR3## wherein at least one of R and R 1 are hydrophilic radicals, said solution containing a redox catalyst, thereby causing a graft polymerization of said hydrophilic vinyl monomer onto said polyolefin mat to form a wettable polyolefin battery separator.
Claim 2
Dependent Claim
169 words
The process of forming a wettable battery separator from a polyolefin which comprises extruding a heated polyolefin through multiple die openings into a gas stream which attenuates the polyolefin into fibers having an average diameter between 1 to about 10 microns, collecting said fibers as a self-supporting mat on a collecting device, compacting the thus formed mat to a thickness between 10 and 40 mils and pore sizes less than 40 microns, contacting the mat with an aqueous solution of a water-soluble, peroxy compound at a temperature below 70° C. without the introduction of oxygen, rinsing the thus contacted mat in a water bath and thereafter at a temperature below 70° C. immersing the thus rinsed mat in an aqueous solution of a hydrophilic vinyl monomer of the formula ##STR3## wherein at least one of R and R 1 are hydrophilic radicals, said solution containing a redox catalyst, thereby causing a graft polymerization of said hydrophilic vinyl monomer onto said polyolefin mat to form a wettable polyolefin battery separator.
Claim 3
Dependent Claim
14 words
The process according to claim 1 wherein the hydrophilic vinyl monomer is acrylic acid.
Claim 4
Dependent Claim
14 words
The process according to claim 1 wherein the redox catalyst is FeSO 4 .
Claim 5
Dependent Claim
14 words
The process according to claim 1 wherein the water-soluble peroxy compound is hydrogen peroxide.