US4217337A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for manufacturing an alumina substrate by acid purifying a prefired substrate before final firing
Assignee: Fujitsu Ltd
•
Filing: 1978-10-30
•
Granted: 1980-08-12
•
Expires: 1998-10-30
Abstract
Abstract Disclosed is an alumina substrate having a high density, a high degree of surface smoothness and excellent dielectric properties and a process for its manufacture. The process comprises prefiring a green sheet prepared from alumina powder at an elevated temperature, for example between 1200 DEG and 1350 DEG C., to remove combustible substances from the sheet, treating the resultant prefired substrate with an acid aqueous solution to eliminate acid-soluble and decomposable substances from the substrate, and firing the acid-treated substrate at an elevated temperature, for example between 1500 DEG and 1650 DEG C.
Inventors
- 👤 Seiichi Yamada
- 👤 Nobuo Kamehara
- 👤 Kyohei Murakawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:39
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C01; C01F; C01F7/00; C01F7/02; C01F7/46; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B41/53; C04B41/5338; C04B41/5353; C04B41/80; C04B41/91
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
67 words
A process for manufacturing an alumina substrate, from alumina powder produced by the Bayer method, said process comprising the steps of: providing a green sheet formed from said alumina powder; purifying said green sheet of alumina by prefiring said green sheet at a temperature in the range from 1200° to 1350° C. and treating said prefired substrate with an acid aqueous solution; and firing said acid-treated substrate.
Claim 2
Dependent Claim
67 words
A process for manufacturing an alumina substrate, from alumina powder produced by the Bayer method, said process comprising the steps of: providing a green sheet formed from said alumina powder; purifying said green sheet of alumina by prefiring said green sheet at a temperature in the range from 1200° to 1350° C. and treating said prefired substrate with an acid aqueous solution; and firing said acid-treated substrate.
Claim 3
Dependent Claim
26 words
A process as claimed in claim 1, wherein said green sheet is formed by powder-pressing a dry mixture of said alumina powder and a binding agent.
Claim 4
Dependent Claim
31 words
A process as claimed in claim 1, wherein said green sheet is formed by casting a slip comprising said alumina powder, a binding agent and a plasticizer dispersed in a solvent.
Claim 5
Dependent Claim
32 words
A process as claimed in claim 1, wherein said acid aqueous solution comprises a member selected from the group consisting of hydrochloric acid, sulfuric acid, nitric acid, hydrofluoric acid and phosphoric acid.
Claim 6
Dependent Claim
19 words
A process as claimed in claim 1, wherein said acid-treated substrate is washed with water before said firing operation.
Claim 7
Dependent Claim
31 words
A process as claimed in claim 1, wherein said acid treating operation is carried out at a temperature of from 60° C. to the boiling temperature of said acid aqueous solution.
Claim 8
Dependent Claim
23 words
A process as claimed in claim 1, wherein said firing operation is carried out at a temperature of from 1500° to 1650° C.
Claim 9
Dependent Claim
29 words
A process as claimed in claim 1, wherein said firing operation is carried out in an atmosphere chosen from the group consisting of clean hydrogen, impure hydrogen and air.
Claim 10
Dependent Claim
22 words
A process as claimed in claim 1, wherein said alumina powder to be formed into said green sheet comprises a binding agent.
Claim 11
Dependent Claim
15 words
The process of claim 1, said alumina powder having a purity of at least 99.5%.
Claim 12
Dependent Claim
18 words
The process of claim 1, said alumina powder having an average particle size of 1 micron or less.
Claim 13
Dependent Claim
21 words
The process of claim 1, said prefiring step comprising prefiring said green sheet for a period between 30 and 180 minutes.
Claim 14
Dependent Claim
17 words
The process of claim 1, said prefiring step of said green sheet occurring in an air atmosphere.
Claim 15
Dependent Claim
14 words
The process of claim 1, said acid solution comprising at least a 1% solution.
Claim 16
Dependent Claim
15 words
The process of claim 1, said acid solution comprising a solution between 3 and 10%.
Claim 17
Dependent Claim
17 words
The process of claim 1, said acid treatment occurring for a period between 60 and 120 minutes.
Claim 18
Dependent Claim
111 words
A process for manufacturing an alumina substrate, comprising steps of: providing a green sheet formed from an alumina powder which has been produced by the Bayer process; prefiring said green sheet at a temperature of from 1200° to 1350° C., for a period of from 30 to 180 minutes, in an air atmosphere, to provide a prefired substrate; treating said prefired substrate with an at least 1 percent mineral acid aqueous solution, at a temperature of from 60° C. to the boiling temperature of the acid aqueous solution, for a period of from 60 to 120 minutes and firing said acid-treated substrate at a temperature of from 1500° to 1650° C.
Claim 19
Dependent Claim
111 words
A process for manufacturing an alumina substrate, comprising steps of: providing a green sheet formed from an alumina powder which has been produced by the Bayer process; prefiring said green sheet at a temperature of from 1200° to 1350° C., for a period of from 30 to 180 minutes, in an air atmosphere, to provide a prefired substrate; treating said prefired substrate with an at least 1 percent mineral acid aqueous solution, at a temperature of from 60° C. to the boiling temperature of the acid aqueous solution, for a period of from 60 to 120 minutes and firing said acid-treated substrate at a temperature of from 1500° to 1650° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-08-12 | 1984-02-11 | 1984-08-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-08-12 | 1988-02-11 | 1988-08-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-08-12 | 1992-02-11 | 1992-08-12 | $7700.00 | Window Closed / Lapsed |