Heat reflecting pane and a method of producing it
Assignee: BFG Glassgroup GIE
•
Filing: 1979-01-02
•
Granted: 1980-08-05
•
Expires: 1999-01-02
Abstract
Abstract A heat-reflecting pane consists of a substantially transparent glass substrate with two layers of titanium oxide, the outside layer being in the rutile form with the intermediate layer being in the anatase form. The pane is formed by double coating the glass substrate with layers of titanium applied by vacuum deposition. A weaker vacuum is used to obtain the anatase form with a stronger vacuum used to obtain the rutile form. Both layers are then oxidized at temperatures of at least 550° C. to form TiO 2 . The intermediate layer of TiO 2 in the anatase form prevents the rutile layer from becoming opaque when the pane is heated to the temperature necessary for heat treatment of the glass substrate. The treatment may be effected either during the heating step in which the titanium is oxidized or in a subsequent additional heating step.
Inventors
- 👤 Rolf Groth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:22
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/14; C23C14/16; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/27; C23C14/58; C23C14/5806; C23C14/5846; C23C14/5853; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/212; C03C2218/00; C03C2218/10; C03C2218/15; C03C2218/151; C03C2218/30; C03C2218/32; C03C2218/322; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
121 words
A heat-reflecting pane comprising: a substantially transparent glass substrate; and two adjacent layers of TiO 2 on said glass substrate comprising: an intermediate layer of TiO 2 on said glass substrate; said intermediate layer of TiO 2 being in the anatase form; and an outside layer of TiO 2 on said glass substrate; said outside layer of TiO 2 being in the rutile form; said adjacent layers having been formed by first depositing an intermediate Ti layer to said glass substrate by vapor deposition in vacuo followed by depositing an outside Ti layer to said intermediate layer of Ti by vapor deposition in vacuo and subsequently oxidizing said intermediate and outside Ti layers at a temperature of at least 400° C.
Claim 2
Dependent Claim
121 words
A heat-reflecting pane comprising: a substantially transparent glass substrate; and two adjacent layers of TiO 2 on said glass substrate comprising: an intermediate layer of TiO 2 on said glass substrate; said intermediate layer of TiO 2 being in the anatase form; and an outside layer of TiO 2 on said glass substrate; said outside layer of TiO 2 being in the rutile form; said adjacent layers having been formed by first depositing an intermediate Ti layer to said glass substrate by vapor deposition in vacuo followed by depositing an outside Ti layer to said intermediate layer of Ti by vapor deposition in vacuo and subsequently oxidizing said intermediate and outside Ti layers at a temperature of at least 400° C.
Claim 3
Dependent Claim
25 words
A heat-reflecting pane as defined in claim 1 wherein said adjacent layers of TiO 2 have a combined thickness of between 300 and 600 A.
Claim 4
Dependent Claim
23 words
A heat-reflecting pane as defined in claim 2 wherein said intermediate layer of TiO 2 has a thickness of at least 30 A.
Claim 5
Dependent Claim
24 words
A heat-reflecting pane as defined in claim 3 wherein said outside layer of TiO 2 has a thickness of no greater than 300 A.
Claim 6
Dependent Claim
23 words
A heat-reflecting pane as defined in claim 4 wherein said outside layer of TiO 2 has a thickness of at least 80 A.
Claim 7
Dependent Claim
24 words
A heat-reflecting pane as defined in claim 5 wherein said outside layer of TiO 2 has a thickness of between 220 and 250 A.
Claim 8
Dependent Claim
34 words
A heat-reflecting pane as defined in claim 1 wherein said glass substrate has been toughened by being heated to a temperature of at least 550° C., preferably 570° to 620° C., followed by chilling.
Claim 9
Independent Claim
138 words
A method of manufacturing a heat-reflecting pane comprising: providing a substantially transparent glass substrate; applying an intermediate Ti layer to the side of said glass substrate by vapor deposition in vacuo, using a pressure of approximately 10 -4 Torr in order to obtain the anatase form of TiO 2 ; applying an outside Ti layer to the previously formed Ti layer by vapor deposition in vacuo, using a pressure of at least 10 -5 Torr in order to obtain the rutile form of TiO 2 ; subsequently heating the pane in air to a temperature of at least 550° C. in order to oxidize both Ti layers to form two layers of TiO 2 , the outside Ti layer being in the rutile form with the intermediate layer being in the anatese form; and subsequently cooling the pane.
Claim 10
Independent Claim
138 words
A method of manufacturing a heat-reflecting pane comprising: providing a substantially transparent glass substrate; applying an intermediate Ti layer to the side of said glass substrate by vapor deposition in vacuo, using a pressure of approximately 10 -4 Torr in order to obtain the anatase form of TiO 2 ; applying an outside Ti layer to the previously formed Ti layer by vapor deposition in vacuo, using a pressure of at least 10 -5 Torr in order to obtain the rutile form of TiO 2 ; subsequently heating the pane in air to a temperature of at least 550° C. in order to oxidize both Ti layers to form two layers of TiO 2 , the outside Ti layer being in the rutile form with the intermediate layer being in the anatese form; and subsequently cooling the pane.
Claim 11
Dependent Claim
54 words
A manufacturing method as defined in claim 8 wherein said intermediate Ti layer is deposited in more than 60 seconds at a pressure of between 1×10 -4 and 2×10 -4 Torr and said outside Ti layer is deposited in less than 30 seconds at a pressure of between 1×10 -5 and 6×10 -5 Torr.
Claim 12
Dependent Claim
47 words
A manufacturing method as defined in claim 8 wherein the application steps occur in a vapor-coating device and comprise: applying said intermediate Ti layer; lowering the pressure; and applying said outside Ti layer, whereby the two Ti layers are vapor-deposited in succession using the same vapor-coating device.
Claim 13
Dependent Claim
33 words
A manufacturing method as defined in claim 8 wherein the heating step consists of heating the pane to a temperature of between 570° and 620° C. in order to oxidize the Ti films.
Claim 14
Dependent Claim
24 words
A manufacturing method as defined in claim 11 wherein the cooling step is effected rapidly to chill the glass substrate and toughen the same.
Claim 15
Dependent Claim
61 words
A manufacturing method as defined in claim 8 wherein after cooling of the pane subsequent to said step of heating the pane to at least 550° C. to oxidize the Ti layers, the pane is again heated to at least 550° C., preferably 570° to 620° C., and is then rapidly cooled to chill the glass substrate and toughen the same.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-08-05 | 1984-02-04 | 1984-08-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-08-05 | 1988-02-04 | 1988-08-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-08-05 | 1992-02-04 | 1992-08-05 | $7700.00 | Window Closed / Lapsed |