Process for producing sodium amalgam particles
Assignee: APL Inc A CORP OF OHIO
•
Filing: 1976-02-02
•
Granted: 1980-08-05
•
Expires: 1996-02-02
Abstract
Abstract Substantially pure, free flowing, sodium amalgam particles of predetermined composition and controlled particle size are prepared for use as vaporizable fill for high pressure discharge lamp devices, whereby accurately measurable quantities of the sodium amalgam may be introduced into the lamp devices. A process for producing the substantially pure amalgam particles of accurately controlled size includes heating a mixture of sodium and mercury to form a melt, passing the melt through a vibrating discharge nozzle and subjecting the droplets so formed to an inert cooling fluid maintained at a temperature below the solidification point of the amalgam. An apparatus for producing the amalgam particles comprises a vessel to contain an alkali metal amalgam melt, a vibrating discharge nozzle adapted to form the melt into uniformly sized droplets, and a column of inert cooling fluid maintained at a low temperature at which the melt droplets are solidified.
Inventors
- 👤 Scott Anderson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:49
CPC Classifications
B; B05; B05B; B05B17/00; B05B17/04; B05B17/06; B05B17/0607; B01; B01J; B01J2/00; B01J2/02; B01J2/04; B22; B22F; B22F9/00; B22F9/02; B22F9/06; B22F9/08; C; C22; C22C; C22C7/00; B22F2999/00
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
88 words
A method for producing free-flowing, discrete sodium-amalgam particles of controlled particle size and sodium oxide content less than 10 p.p.m. comprising: heating a mixture of sodium and mercury in a vessel to form an amalgam melt of determinable unoxidized sodium content; withdrawing a portion of said melt from the vessel at a point other than at an upper surface of said melt; and passing the withdrawn portion of said melt through a vibrating discharge conduit into an inert, quenching atmosphere to form free-flowing, discreet particles of said amalgam.
Claim 2
Independent Claim
88 words
A method for producing free-flowing, discrete sodium-amalgam particles of controlled particle size and sodium oxide content less than 10 p.p.m. comprising: heating a mixture of sodium and mercury in a vessel to form an amalgam melt of determinable unoxidized sodium content; withdrawing a portion of said melt from the vessel at a point other than at an upper surface of said melt; and passing the withdrawn portion of said melt through a vibrating discharge conduit into an inert, quenching atmosphere to form free-flowing, discreet particles of said amalgam.
Claim 3
Dependent Claim
16 words
The method of claim 1 wherein the inert, quenching atmosphere is composed of dry gaseous helium.
Claim 4
Dependent Claim
19 words
The method of claim 2 wherein said gaseous helium is maintained at a temperature less than minus 150° C.
Claim 5
Dependent Claim
21 words
The method of claim 3 wherein said gaseous helium is maintained at said temperature by indirect heat exchange with liquid nitrogen.
Claim 6
Dependent Claim
17 words
The method of claim 1 wherein the inert, quenching atmosphere is composed of substantially water-free liquid nitrogen.
Claim 7
Dependent Claim
29 words
The method of claim 1 wherein said amalgam contains from about 2 to about 30 weight percent sodium and concomitantly from about 98 to about 70 weight percent mercury.
Claim 8
Dependent Claim
28 words
The method of claim 6 wherein said amalgam contains from about 10 to about 26 weight percent sodium and from about 90 to about 74 weight percent mercury.
Claim 9
Dependent Claim
22 words
The method of claim 1 wherein said melt is filtered to remove solid impurities prior to passing through said vibrating discharge conduit.
Claim 10
Dependent Claim
66 words
The method of claim 1 wherein said mixture of sodium and mercury is formed by heating the vessel to a temperature above the melting point of the amalgam, adding sodium to said vessel and thereafter adding mercury in incremental form to said sodium to form the amalgam, at least the additions of sodium and mercury being conducted while an argon atmosphere is maintained in the vessel.
Claim 11
Dependent Claim
25 words
The method of claim 1 wherein said sodium contains less than about 100 p.p.m. of potassium and said mercury is triple-distilled to remove impurities therefrom.
Claim 12
Independent Claim
112 words
A method for producing free-flowing, discrete particles of a sodium amalgam containing from about 10 to about 26 weight percent sodium, balance essentially mercury which comprises: heating a mixture of said sodium and mercury in a vessel to a temperature above the melting point of the sodium amalgam while passing argon gas therethrough, filtering the sodium amalgam melt to remove solid impurities therefrom, passing the filtered melt through a vibrating discharge conduit to form said melt into droplets, passing said particles through a quenching atmosphere of dry gaseous helium maintained at a temperature of less than minus 150° C. by indirect heat exchange with liquid nitrogen to solidify and cool said particles.
Claim 13
Independent Claim
112 words
A method for producing free-flowing, discrete particles of a sodium amalgam containing from about 10 to about 26 weight percent sodium, balance essentially mercury which comprises: heating a mixture of said sodium and mercury in a vessel to a temperature above the melting point of the sodium amalgam while passing argon gas therethrough, filtering the sodium amalgam melt to remove solid impurities therefrom, passing the filtered melt through a vibrating discharge conduit to form said melt into droplets, passing said particles through a quenching atmosphere of dry gaseous helium maintained at a temperature of less than minus 150° C. by indirect heat exchange with liquid nitrogen to solidify and cool said particles.
Claim 14
Dependent Claim
40 words
The method of claim 11 wherein said mixture of sodium and mercury is formed by heating sodium metal in said vessel to a temperature above the melting point of the sodium amalgam and incrementally adding mercury to said molten sodium.
Claim 15
Dependent Claim
22 words
The method of claim 12 wherein argon gas is passed through said molten sodium while said mercury is being incrementally added thereto.
Claim 16
Dependent Claim
20 words
The method of claim 11 wherein said sodium contains less than 100 ppm of potassium and said mercury is triple-distilled.
Claim 17
Dependent Claim
15 words
The method of claim 11 wherein said mixture of sodium and mercury is pre-formed amalgam.
References Cited (Backward Citations)
US3676534A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-08-05 | 1984-02-04 | 1984-08-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-08-05 | 1988-02-04 | 1988-08-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-08-05 | 1992-02-04 | 1992-08-05 | $7700.00 | Window Closed / Lapsed |