Shell process foundry resin compositions

Claim 2

A shell process foundry resin composition consisting essentially of a mixture of an uncured novolak resin, an effective amount of a curing agent for said resin and 0.5 to 10% based on the weight of the resin of a finely divided, siliceous material selected from the group consisting of fumed silica, kaolin clay, bentonite, attapulgus clay and mixtures thereof.

Claim 3

The resin composition of claim 1 wherein the resin is the acid catalyzed reaction product of an aldehyde with a phenolic compound in a ratio of about 0.5 to 0.85 mole of aldehyde per mole of phenolic compound.

Claim 4

The resin composition of claim 1 wherein the quantity of said siliceous material is in the range of from about 0.5 to about 10 percent, based on resin weight.

Claim 5

The resin composition of claim 1 wherein the quantity of said siliceous material is in the range of from about 2 to about 6 percent, based on resin weight.

Claim 6

The resin composition of claim 1 and further including a release agent.

Claim 7

The resin composition of claim 1 wherein the mixture is in the form of flakes.

Claim 8

The resin composition of claim 1 wherein the siliceous material is fumed silica.

Claim 9

The resin composition of claim 6 wherein the siliceous material is fumed silica.

Claim 10

The resin composition of claim 1 wherein the siliceous material is kaolin clay.

Claim 11

The resin composition of claim 6 wherein the siliceous material is kaolin clay.

Claim 12

The resin composition of claim 1 wherein the siliceous material is bentonite.

Claim 13

The resin composition of claim 6 wherein the siliceous material is bentonite.

Claim 14

The resin composition of claim 1 wherein the siliceous material is attapulgus clay.

Claim 15

The resin composition of claim 6 wherein the siliceous material is attapulgus clay.

Claim 16

Foundry sand coated with: (1) about 1 to about 8 parts, per each 100 parts by weight of the sand, of a bonding resin composition consisting essentially of an intimate admixture of an uncured novolak resin and a finely divided siliceous material selected from the group consisting of fumed silica, kaolin clay, bentonite, attapulgus clay and mixtures thereof, the amount of said siliceous material being about 0.5 to about 10 percent, based on the weight of the resin; and (2) an effective amount of a curing agent for said resin.

Claim 17

Foundry sand coated with: (1) about 1 to about 8 parts, per each 100 parts by weight of the sand, of a bonding resin composition consisting essentially of an intimate admixture of an uncured novolak resin and a finely divided siliceous material selected from the group consisting of fumed silica, kaolin clay, bentonite, attapulgus clay and mixtures thereof, the amount of said siliceous material being about 0.5 to about 10 percent, based on the weight of the resin; and (2) an effective amount of a curing agent for said resin.

Claim 18

The coated foundry sand of claim 15 wherein the resin is the acid catalyzed reaction product of an aldehyde with a phenolic compound in a ratio of about 0.5 to 0.85 mole of aldehyde per mole of phenolic compound.

Claim 19

The coated foundry sand of claim 16 wherein the phenolic compound is phenol and the curing agent is hexamethylenetetramine.

Claim 20

The coated foundry sand of claim 15 wherein the quantity of said siliceous material is in the range from about 2 to about 6 percent, based on the weight of the resin.

Claim 21

The coated foundry sand of claim 15 wherein the siliceous material is fumed silica.

Claim 22

The coated foundry sand of claim 15 wherein the siliceous material is kaolin clay.

Claim 23

The coated foundry sand of claim 15 wherein the siliceous material is bentonite.

Claim 24

The coated foundry sand of claim 15 wherein the siliceous material is attapulgus clay.

Claim 25

A process for forming foundry cores and molds comprising the steps of: (1) contacting a hot pattern with a free flowing foundry sand coated with: (a) about 1 to about 8 parts, per each 100 parts by weight of the sand, of a bonding resin composition consisting essentially of an intimate admixture of an uncured novolak resin and a finely divided siliceous material selected from the group consisting of fumed silica, kaolin clay, bentonite, attapulgus clay and mixtures thereof, the amount of said siliceous material being about 0.5 to about 10 percent, based on the weight of the resin; and (b) an effective amount of a curing agent for said resin; (2) holding the resin coated sand against the hot pattern to bond a portion of the particles of resin coated sand together to form a foundry mold or core of suitable thickness; (3) removing unbonded particles of resin coated sand from bonded particles of sand forming the foundry mold or core; (4) curing the foundry mold or core, the hot pattern having a temperature of from about 350° F. to about 600° F.; and (5) removing the foundry mold or core from the pattern.

Claim 26

A process for forming foundry cores and molds comprising the steps of: (1) contacting a hot pattern with a free flowing foundry sand coated with: (a) about 1 to about 8 parts, per each 100 parts by weight of the sand, of a bonding resin composition consisting essentially of an intimate admixture of an uncured novolak resin and a finely divided siliceous material selected from the group consisting of fumed silica, kaolin clay, bentonite, attapulgus clay and mixtures thereof, the amount of said siliceous material being about 0.5 to about 10 percent, based on the weight of the resin; and (b) an effective amount of a curing agent for said resin; (2) holding the resin coated sand against the hot pattern to bond a portion of the particles of resin coated sand together to form a foundry mold or core of suitable thickness; (3) removing unbonded particles of resin coated sand from bonded particles of sand forming the foundry mold or core; (4) curing the foundry mold or core, the hot pattern having a temperature of from about 350° F. to about 600° F.; and (5) removing the foundry mold or core from the pattern.

Claim 27

The process of claim 23 wherein the resin is the acid catalyzed reaction product of phenol with formaldehyde in a ratio of about 0.5 to 0.85 mole of formaldehyde per mole of phenol, and the curing agent is hexamethylenetetramine.

Claim 28

The process of claim 23 wherein the quantity of said siliceous material is in the range of about 2 to about 6 percent, based on the weight of the resin.

Claim 29

The process of claim 23 wherein the siliceous material is fumed silica.

Claim 30

The process of claim 23 wherein the siliceous material is kaolin clay.

Claim 31

The process of claim 23 wherein the siliceous material is bentonite.

Claim 32

The process of claim 23 wherein the siliceous material is attapulgus clay.

Claim 33

A sand mold prepared by the process of claim 23.

Claim 34

A sand core prepared by the process of claim 23.