US4215032A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Polyester composition
Assignee: Toyobo Co Ltd
•
Filing: 1979-05-09
•
Granted: 1980-07-29
•
Expires: 1999-05-09
Abstract
Abstract The present application provides a polyester composition composed of polyethylene terephthalate or a polyester containing at least 80 mol % of ethylene terephthalate repeating units and 0.1 to 15 weight %, based on the polyester, of an organic crystallization promoting agent having a polyoxyalkylene chain and at least one epoxy group. The latter promoting agents are represented by such materials as a glycidyl ether of a polyalkylene glycol having a molecular weight less than 5000. Such crystallization promoting agents serve to prevent streaks and pock marks on the surface of articles molded from such polyester compositions.
Inventors
- 👤 Shigeo Kobayashi
- 👤 Nori Yoshihara
- 👤 Kiyoji Nanbu
- 👤 Yukio Goto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 06:14
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/02; C08K; C08K3/00; C08K3/01; C08K5/00; C08K5/04; C08K5/15; C08K5/151; C08K5/1515; C08K5/16; C08L23/00; C08L23/02; C08L23/16; C08L31/00; C08L31/02; C08L31/04; C08L33/00; C08L33/04; C08L33/06; C08L33/08; C08L63/00; C08L67/025; C08L71/00; Y; Y10; Y10S; Y10S260/00; Y10S260/35
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
50 words
A polyester composition composed of solid polyethylene terephthalate or a solid polyester containing at least 80 mol % ethylene terephthalate repeating units and 0.1 to 15 weight %, based on the polyester, of an organic crystallization promoting agent added thereto having a polyoxyalkylene chain and at least one epoxy group.
Claim 2
Dependent Claim
50 words
A polyester composition composed of solid polyethylene terephthalate or a solid polyester containing at least 80 mol % ethylene terephthalate repeating units and 0.1 to 15 weight %, based on the polyester, of an organic crystallization promoting agent added thereto having a polyoxyalkylene chain and at least one epoxy group.
Claim 3
Dependent Claim
30 words
The polyester composition as claimed in claim 1 wherein the amount of addition of the organic crystallization promoting agent is from 0.5 to 15 weight % based on the polyester.
Claim 4
Dependent Claim
45 words
The polyester composition as claimed in claim 1 wherein the organic crystallization promoting agent is glycidyl ether of a polyalkylene glycol or glycidyl ether of a derivative of a polyalkylene glycol, said polyalkylene glycol or said derivative thereof having a molecular weight less than 5000.
Claim 5
Dependent Claim
30 words
The polyester composition as claimed in claim 1 wherein the organic crystallization promoting agent is polyglycidyl ether of a polyalkylene glycol having a molecular weight of from 200 to 1500.
Claim 6
Dependent Claim
60 words
The polyester composition as claimed in claim 1 wherein the organic crystallization promoting agent is an epoxy compound represented by the general formula: ##STR4## wherein A stands for an aliphatic hydrocarbon group, hydrogen, or a glycidyl group; R stands for an aliphatic hydrocarbon group of C 2 -C 5 , and n stands for an integer not less than 2.
Claim 7
Dependent Claim
75 words
A polyester composition composed of solid polyethylene terephthalate or a solid polyester containing at least 80 mol % ethylene terephthalate repeating units, to which are added (a) 0.1 to 15 weight %, based on the polyester, of an organic crystallization promoting agent containing a polyoxyalkylene chain and at least one expoxyl group, and (b) less than 40 weight %, based on the total composition, of an inorganic filler having a particular diameter less than 30μ.
Claim 8
Dependent Claim
75 words
A polyester composition composed of solid polyethylene terephthalate or a solid polyester containing at least 80 mol % ethylene terephthalate repeating units, to which are added (a) 0.1 to 15 weight %, based on the polyester, of an organic crystallization promoting agent containing a polyoxyalkylene chain and at least one expoxyl group, and (b) less than 40 weight %, based on the total composition, of an inorganic filler having a particular diameter less than 30μ.
Claim 9
Dependent Claim
26 words
The polyester composition as claimed in claim 6 wherein the amount of the inorganic filler is 1 to 30 weight % based on the total composition.
Claim 10
Dependent Claim
15 words
The polyester composition as claimed in claim 6 wherein the inorganic filler is a silicate.
Claim 11
Dependent Claim
80 words
A polyester composition composed of solid polyethlene terephthalate or a solid polyester containing at least 80 mol % ethylene terephthalate repeating units, to which are added (a) 0.1 to 15 weight %, based on the polyester, of an organic crystallization promoting agent containing a polyoxyalkylene chain and at least one epoxy group, and (b) less than 20 weight %, based on the polyester, of an elastic substance of the polyester family having a glass transition temperature lower than 10° C.
Claim 12
Dependent Claim
80 words
A polyester composition composed of solid polyethlene terephthalate or a solid polyester containing at least 80 mol % ethylene terephthalate repeating units, to which are added (a) 0.1 to 15 weight %, based on the polyester, of an organic crystallization promoting agent containing a polyoxyalkylene chain and at least one epoxy group, and (b) less than 20 weight %, based on the polyester, of an elastic substance of the polyester family having a glass transition temperature lower than 10° C.
Claim 13
Dependent Claim
31 words
The polyester composition as claimed in claim 9 wherein the amount of addition of the elastic substance of the polyester family is 1 to 10 weight % based on the polyester.
Claim 14
Dependent Claim
68 words
A polyester composition composed of solid polyethylene terephthalate or a solid polyester containing at least 80 mol % ethylene terephthalate repeating units, to which are added (a) 0.1 to 15 weight %, based on the polyester, of an organic crystallization promoting agent containing a polyoxyalkylene chain and at least one epoxy group, and (b) less than 10 weight %, based on the polyester, of a mold releasing agent.
Claim 15
Dependent Claim
68 words
A polyester composition composed of solid polyethylene terephthalate or a solid polyester containing at least 80 mol % ethylene terephthalate repeating units, to which are added (a) 0.1 to 15 weight %, based on the polyester, of an organic crystallization promoting agent containing a polyoxyalkylene chain and at least one epoxy group, and (b) less than 10 weight %, based on the polyester, of a mold releasing agent.
Claim 16
Dependent Claim
60 words
The polyester composition as claimed in claim 11 wherein the mold releasing agent is at least one compound selected from the group consisting of an ester of an aliphatic acid of C 15 -C 50 and an alcohol, a salt of said aliphatic acid and a metal of IA Group or IIA Group of the Periodic Table of the Elements.
Claim 17
Dependent Claim
134 words
A polyester composition composed of solid polyethylene terephthalate or a solid polyester containing at least 80 mol % ethylene terephthalate repeating units, to which are added (a) 0.5 to 15 weight %, based on the polyester, of an organic crystallization promoting agent containing a polyoxylalkylene chain and at least one epoxy group, (b) 0 to 20 weight %, based on the polyester, of an elastic substance of the polyester family having a glass transition temperature lower than 10° C., (c) 0 to 10 weight %, based on the polyester, of a mold releasing agent, (d) 0 to 40 weight %, based on the total composition, of an inorganic filler having a particle diameter less than 30μ, and (e) 0 to 50 weight %, based on the total resin component, of a fibrous reinforcing material.
Claim 18
Dependent Claim
134 words
A polyester composition composed of solid polyethylene terephthalate or a solid polyester containing at least 80 mol % ethylene terephthalate repeating units, to which are added (a) 0.5 to 15 weight %, based on the polyester, of an organic crystallization promoting agent containing a polyoxylalkylene chain and at least one epoxy group, (b) 0 to 20 weight %, based on the polyester, of an elastic substance of the polyester family having a glass transition temperature lower than 10° C., (c) 0 to 10 weight %, based on the polyester, of a mold releasing agent, (d) 0 to 40 weight %, based on the total composition, of an inorganic filler having a particle diameter less than 30μ, and (e) 0 to 50 weight %, based on the total resin component, of a fibrous reinforcing material.
Claim 19
Dependent Claim
16 words
The polyester composition as claimed in claim 13 wherein the fibrous reinforcing material is glass fiber.
Claim 20
Dependent Claim
33 words
The polyester composition as claimed in claim 13 wherein the surface crystallinity of a molded article formed by injection molding at a mold temperature of 85° to 90° C. is at least 0.5.
Claim 21
Dependent Claim
18 words
Polyester molded articles obtained by injection molding or compression molding the polyester composition as claimed in claim 13.
References Cited (Backward Citations)
US3560605A
Cited
US4016142A
Cited
US4147737A
Cited
US3886104A
Cited
US4076767A
Cited
US4065438A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-07-29 | 1984-01-28 | 1984-07-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-07-29 | 1988-01-28 | 1988-07-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-07-29 | 1992-01-28 | 1992-07-29 | $7700.00 | Window Closed / Lapsed |