Method of manufacturing products of cross-linked thermoplastic material
Assignee: Pont a Mousson SA
•
Filing: 1978-02-15
•
Granted: 1980-06-24
•
Expires: 1998-02-15
Abstract
Abstract The process comprises forming a mixture containing a thermoplastic material and a cross-linking agent and causing the mixture to enter a die head. A pressure is exerted on the mixture in the die head along the axis of the die head so as to sinter the mixture. The die head is heated to a temperature lower than the temperature at which the cross-linking agent becomes substantially decomposed so as to cause fusion of the mixture and produce a formed material. The formed material is passed through a bath of molten salt downstream of the die head. The temperature of the molten salt is such as to achieve the decomposition of the cross-linking agent and the cross-linking of the formed material. A device is described for carrying out the process.
Inventors
- 👤 Gerard M. Denis
- 👤 Bernard M. Ginglinger
- 👤 Claude M. Rothamel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 13:12
CPC Classifications
B; B29; B29C; B29C35/00; B29C35/02; B29C35/04; B29C35/06; B29C37/00; B29C37/0089; B29C48/00; B29C48/022; B29C48/03; B29C48/05; B29C48/06; B29C48/07; B29C48/08; B29C48/09; B29C48/25; B29C48/36; B29C48/475; B29C48/88; B29C48/90; B29C48/91; B29C35/041; B29C2035/042; B29C48/001; B29C48/0017; B29C48/04; B29C48/10; B29C48/906; B29K; B29K2101/00; B29K2101/10; B29K2105/00; B29K2105/24; B29K2105/25; B29K2105/251; B29K2301/00; B29K2301/10; B29L; B29L2023/00; B29L2023/22
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
268 words
A process for producing long products of cross-linked high-density polyethylene having a molecular weight of at least 200,000, comprising forming a mixture which is essentialy a powdered mixture containing said polyethylene and a cross-linking agent, charging the mixture into a heated substantially cylindrical die head, exerting a pressure on the mixture in the die head in a direction along the axis of the die head so as to sinter the mixture in a sintering region of the die head while maintaining the sintering region of the die head at a temperature lower than the temperature at which the cross-linking agent becomes substantially decomposed but sufficient to cause fusion of the mixture and produce a formed material, and constraining the formed material issuing from the die head to enter a bath of molten salt located downstream of the die head relative to the travel of the formed material by first driving means located adjacent an inlet end of the bath and engaged with the formed material and second driving means located adjacent an outlet end of the bath and engaged with the formed material, the bath of molten salt having a temperature which causes the decomposition of the cross-linking agent and the cross-linking of the formed material in a cross-linking region of the bath, said second driving means driving the formed material at a rate which is higher than the rate at which the first driving means drives the formed material whereby the formed material is stretched upstream of said cross-linking region of the bath so that the formed material assumes the desired cross-sectional size before it is cross-linked.
Claim 2
Dependent Claim
268 words
A process for producing long products of cross-linked high-density polyethylene having a molecular weight of at least 200,000, comprising forming a mixture which is essentialy a powdered mixture containing said polyethylene and a cross-linking agent, charging the mixture into a heated substantially cylindrical die head, exerting a pressure on the mixture in the die head in a direction along the axis of the die head so as to sinter the mixture in a sintering region of the die head while maintaining the sintering region of the die head at a temperature lower than the temperature at which the cross-linking agent becomes substantially decomposed but sufficient to cause fusion of the mixture and produce a formed material, and constraining the formed material issuing from the die head to enter a bath of molten salt located downstream of the die head relative to the travel of the formed material by first driving means located adjacent an inlet end of the bath and engaged with the formed material and second driving means located adjacent an outlet end of the bath and engaged with the formed material, the bath of molten salt having a temperature which causes the decomposition of the cross-linking agent and the cross-linking of the formed material in a cross-linking region of the bath, said second driving means driving the formed material at a rate which is higher than the rate at which the first driving means drives the formed material whereby the formed material is stretched upstream of said cross-linking region of the bath so that the formed material assumes the desired cross-sectional size before it is cross-linked.
Claim 3
Dependent Claim
28 words
A process as claimed in claim 1, wherein the axial pressure exerted on the mixture is exerted by piston means and is of the order of 1000 bars.
Claim 4
Dependent Claim
20 words
A process as claimed in claim 1, wherein the temperature of the sintering region is between 150° and 180° C.
Claim 5
Dependent Claim
20 words
A process as claimed in claim 1, wherein the temperature of the cross-linking region is between 200° and 300° C.
Claim 6
Dependent Claim
53 words
A process as claimed in claim 1, wherein the bath of molten salt comprises two compartments, the temperature of the molten salt in the compartment adjacent the outlet end being the cross-linking temperature whereas the temperature of the molten salt of the compartment adjacent the inlet end is lower than the cross-linking temperature.
Claim 7
Dependent Claim
25 words
A process as claimed in claim 1, comprising shaping and calibrating the formed material in a region between the cross-linking region and the die head.
Claim 8
Dependent Claim
44 words
A process as claimed in claim 1, wherein the stretching of the formed material occurs in a region having a temperature in the neighborhood of the temperature of the forming of the material in the die head before the cross-linking of the formed material.
Claim 9
Dependent Claim
17 words
A process as claimed in claim 7, wherein said region is in a bath of molten salt.
Claim 10
Dependent Claim
310 words
A process for producing long products of cross-linked high-density polyethylene having a molecular weight of at least 200,000, comprising forming a mixture which is essentially a powdered mixture containing said polyethylene and a cross-linking agent, charging the mixture into a heated substantially cylindrical die head, exerting by reciprocating piston means a pressure on the mixture in the die head in a direction along the axis of the die head so as to sinter the mixture in a sintering region of the die head while maintaining the sintering region of the die head at a temperature lower than the temperature at which the cross-linking agent becomes substantially decomposed but sufficient to cause fusion of the mixture and produce a formed material, and constraining the formed material issuing from the die head to change direction and form a loop portion to accommodate the irregular rate of flow of the formed material through the die head owing to the reciprocating action of the piston means, and thereafter constraining the formed material to enter a bath of molten salt located downstream of the die head relative to the travel of the formed material by first driving means located adjacent an inlet end of the bath and engaged with the formed material and second driving means located adjacent an outlet end of the bath and engaged with the formed material, the bath of molten salt having a temperature which causes the decomposition of the cross-linking agent and the cross-linking of the formed material in a cross-linking region of the bath, said second driving means driving the formed material at a rate which is higher than the rate at which the first driving means drives the formed material whereby the formed material is stretched upstream of said cross-linking region of the bath so that the formed material assumes the desired cross-sectional size before it is cross-linked.
Claim 11
Dependent Claim
310 words
A process for producing long products of cross-linked high-density polyethylene having a molecular weight of at least 200,000, comprising forming a mixture which is essentially a powdered mixture containing said polyethylene and a cross-linking agent, charging the mixture into a heated substantially cylindrical die head, exerting by reciprocating piston means a pressure on the mixture in the die head in a direction along the axis of the die head so as to sinter the mixture in a sintering region of the die head while maintaining the sintering region of the die head at a temperature lower than the temperature at which the cross-linking agent becomes substantially decomposed but sufficient to cause fusion of the mixture and produce a formed material, and constraining the formed material issuing from the die head to change direction and form a loop portion to accommodate the irregular rate of flow of the formed material through the die head owing to the reciprocating action of the piston means, and thereafter constraining the formed material to enter a bath of molten salt located downstream of the die head relative to the travel of the formed material by first driving means located adjacent an inlet end of the bath and engaged with the formed material and second driving means located adjacent an outlet end of the bath and engaged with the formed material, the bath of molten salt having a temperature which causes the decomposition of the cross-linking agent and the cross-linking of the formed material in a cross-linking region of the bath, said second driving means driving the formed material at a rate which is higher than the rate at which the first driving means drives the formed material whereby the formed material is stretched upstream of said cross-linking region of the bath so that the formed material assumes the desired cross-sectional size before it is cross-linked.
References Cited (Backward Citations)
US3024492A
Cited
US2971221A
Cited
US3054142A
Cited
US3051992A
Cited
US3186032A
Cited
US3201503A
Cited
US3296661A
Cited
US3456294A
Cited
US3591674A
Cited
US3699197A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-06-24 | 1983-12-24 | 1984-06-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-06-24 | 1987-12-24 | 1988-06-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-06-24 | 1991-12-24 | 1992-06-24 | $7700.00 | Window Closed / Lapsed |