Selective etching of polymeric materials embodying silicones via reactor plasmas
Assignee: General Electric Co
•
Filing: 1978-10-18
•
Granted: 1980-06-24
•
Expires: 1998-10-18
Abstract
Abstract Silicon is employed as a masking material for the selective plasma chemical etching of a coating material of a polyimide-silicone copolymer disposed on selective surface areas of electronic devices.
Inventors
- 👤 Leonard Stein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 16:39
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/286; H10P50/287
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
349 words
A method for the selective chemical etching of a cured layer of a silicone-polyimide copolymer material disposed on a surface of a body to open windows therein to expose selected surface portions of the surface thereat including the process steps of: (a) forming a layer of a cured silicone-polyimide copolymer material on a processed body of semiconductor material, the copolymer material consisting of a reaction product of a silicon-free organic diamine, an organic tetracarboxylic dianhydride and a polysiloxane which when cured has the recurring structural units of the formula: ##STR8## with from 5 to 40 mol percent intercondensed structural units of the formula: ##STR9## wherein R is a divalent hydrocarbon radical; R' is a monovalent hydrocarbon radical; R" is a tetravalent organic radical; Q is a divalent silicon-free organic radical which is the residue of an organic diamine; x is an integer having a value of 1-4, and m and n are integers greater than 1; (b) depositing a layer of silicon of a predetermined thickness on the layer of silicone-polyimide copolymer material; (c) depositing a photoresist material on the layer of silicon; (d) processing the layer of photoresist material to open one or more windows therein to expose a selected surface area of the layer of silicon thereat; (e) chemically etching selectively the exposed silicon in a plasma of CF 4 /4% oxygen at about 100 watts RF power at a pressure range of from about 0.3 torr to about 0.5 torr to open one or more windows therein, aligned with the respective windows in the layer of photoresist, to expose selected surface areas of the layer of silicone-polyimide copolymer material thereat, and (f) chemically etching the layer of silicone-polyimide copolymer material selectively in an oxygen plasma at a range of RF power from about 200 watts to about 400 watts at a range of pressure from about 0.8 torr to about 2.0 torr to open one or more windows in the copolymer layer, aligned with the respective windows of the layer of silicon, to expose the selected surface areas of the surface of the processed body thereat.
Claim 2
Independent Claim
349 words
A method for the selective chemical etching of a cured layer of a silicone-polyimide copolymer material disposed on a surface of a body to open windows therein to expose selected surface portions of the surface thereat including the process steps of: (a) forming a layer of a cured silicone-polyimide copolymer material on a processed body of semiconductor material, the copolymer material consisting of a reaction product of a silicon-free organic diamine, an organic tetracarboxylic dianhydride and a polysiloxane which when cured has the recurring structural units of the formula: ##STR8## with from 5 to 40 mol percent intercondensed structural units of the formula: ##STR9## wherein R is a divalent hydrocarbon radical; R' is a monovalent hydrocarbon radical; R" is a tetravalent organic radical; Q is a divalent silicon-free organic radical which is the residue of an organic diamine; x is an integer having a value of 1-4, and m and n are integers greater than 1; (b) depositing a layer of silicon of a predetermined thickness on the layer of silicone-polyimide copolymer material; (c) depositing a photoresist material on the layer of silicon; (d) processing the layer of photoresist material to open one or more windows therein to expose a selected surface area of the layer of silicon thereat; (e) chemically etching selectively the exposed silicon in a plasma of CF 4 /4% oxygen at about 100 watts RF power at a pressure range of from about 0.3 torr to about 0.5 torr to open one or more windows therein, aligned with the respective windows in the layer of photoresist, to expose selected surface areas of the layer of silicone-polyimide copolymer material thereat, and (f) chemically etching the layer of silicone-polyimide copolymer material selectively in an oxygen plasma at a range of RF power from about 200 watts to about 400 watts at a range of pressure from about 0.8 torr to about 2.0 torr to open one or more windows in the copolymer layer, aligned with the respective windows of the layer of silicon, to expose the selected surface areas of the surface of the processed body thereat.
Claim 3
Dependent Claim
21 words
The method of claim 1 wherein the photoresist material is removed simultaneously with the plasma etching of the polyimide-silicone copolymer material.
Claim 4
Dependent Claim
21 words
The method of claim 1 wherein the layer of silicon is from about 500 A to about 2,000 A in thickness.
Claim 5
Dependent Claim
18 words
The method of claim 3 wherein the depositing of the layer of silicon is by electron beam deposition.
Claim 6
Dependent Claim
16 words
The method of claim 3 wherein the layer of silicon is about 1000 A in thickness.
Claim 7
Dependent Claim
18 words
The method of claim 5 wherein the depositing of the layer of silicon is by electron beam deposition.
Claim 8
Dependent Claim
60 words
The method of claim 1 and including the additional process step prior to process step (e) of selective etching of the exposed silicon of preheating the processed body in a plasma of nitrogen for a sufficient period of time to raise the temperature of the processed body to about that temperature required for uniform plasma chemical etching of the silicon.
Claim 9
Dependent Claim
42 words
The method of claim 7 wherein the nitrogen plasma is formed at an RF power of about 100 watts at a pressure of about 0.5 torr, and the processed body is heated to a temperature ranging from 65° C. to 85° C.
Claim 10
Dependent Claim
30 words
The method of claim 1 wherein the flow of the CF 4 containing 4% oxygen by volume is from about 100 cc per minute to about 150 cc per minute.
Claim 11
Dependent Claim
18 words
The method of claim 1 wherein the oxygen gas flow of the oxygen plasma is about 300 CCPM.
Claim 12
Dependent Claim
24 words
The method of claim 10 wherein the RF power is about 300 watts, and the pressure is about 1.6 torr for the oxygen plasma.
Claim 13
Dependent Claim
52 words
The method of claim 8 wherein the chemical etching of the exposed silicon is practiced at a pressure of about 0.3 torr and the exposed polyimide-silicone copolymer material is chemically etched by a plasma of oxygen formed at a RF power of about 300 watts at a pressure of about 1.6 torr.
Claim 14
Dependent Claim
42 words
The method of claim 12 wherein the flow of plasma gas of CF 4 containing 4% oxygen by volume is from about 100 cc/minute to about 150 cc/minute, and the flow of oxygen gas for the oxygen plasma is about 300 CCPM.
Claim 15
Dependent Claim
26 words
The method of claim 1 and including introducing from 10% by volume to 15% by volume of CF 4 into the oxygen of the oxygen plasma.
Claim 16
Dependent Claim
20 words
The method of claim 14 wherein the oxygen plasma is formed at about 50 watts and about 0.2 torr pressure.
Claim 17
Dependent Claim
22 words
The method of claim 1 wherein the chemical etching of the exposed silicon is practiced at a pressure of about 0.3 torr.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-06-24 | 1983-12-24 | 1984-06-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-06-24 | 1987-12-24 | 1988-06-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-06-24 | 1991-12-24 | 1992-06-24 | $7700.00 | Window Closed / Lapsed |