Foamable polymeric alloy composition

Claim 2

A foamable moldable polymeric alloy composition for structural foams consisting essentially of: A. an addition polymer polyblend which comprises a mixture of a major amount of: 1. a polymer of at least one alkenyl aromatic monomer, and a minor amount of: 2. A grafted diene rubber, grafted with said alkenyl aromatic monomer, B. an interpolymer of an alkenyl aromatic monomer and maleic anhydride, wherein the weight ratio of said addition polymer to said interpolymer in said alloy is about 85:15 to 50:50, and C. a foaming agent selected from the group consisting of carbonates, bicarbonates, azo, hydrazides, hydrazines, azide and amide compounds, nitrogen, carbon dioxide or mixtures thereof.

Claim 3

An alloy of claim 1 wherein said polymer is polystyrene.

Claim 4

An alloy of claim 1 wherein said interpolymers is styrene-maleic anhydride wherein the ratio of styrene to maleic anhydride is 85:15 to 95:5.

Claim 5

An alloy of claim 1 wherein said diene rubber is selected from the group consisting of polybutadiene and copolymers of butadiene-styrene, butadiene-acrylonitrile, polychloroprene, polyisoprene or mixtures thereof.

Claim 6

An alloy of claim 1 wherein said diene rubber is grafted with styrene.

Claim 7

An alloy of claim 1 wherein said diene rubber is dispersed as rubber particles, said particles having present grafted and occluded polymers of polystyrene in an amount of about 0.5 to 5 parts per part of diene rubber and having a particle size of about 0.5 to 20 microns.

Claim 8

An alloy of claim 1 wherein said gas liberating compound is present in an amount of about 0.2 to 2.0% by weight based on said alloy.

Claim 9

An alloy of claim 1 wherein said compound is present in an amount sufficient to reduce the density of said alloy about 5 to 50% by weight when foamed by melt processing at temperatures of about 200° 275° C.

Claim 10

An alloy of claim 1 wherein said polymer has a molecular weight of about 100,000 to 300,000 Mw and said interpolymer has molecular weight of about 100,000 to 400,000 Mw.

Claim 11

An alloy of claim 1 wherein said grafted diene rubber is present in an amount such that the diene rubber moiety is present in amounts from 2 to 15% by weight of said alloy.

Claim 12

An alloy of claim 1 wherein said foaming agent is alkaline and/or alkaline metal earth carbonates and/or bicarbonates.

Claim 13

An alloy of claim 1 wherein said foaming agent is sodium bicarbonate.

Claim 14

An alloy of claim 1 wherein said compound is an azo compound selected from the group diazoaminobenzene, 1,3-diphenyl triazene, azo dicarbonamide, 1,1'-azo-bis-formamide, 2,2'-azo-isobutyronitrile and azo-hexahydrobenzonitrile or mixtures thereof.

Claim 15

An alloy of claim 1 wherein said compound is a hydrazide selected from the group consisting of benzene sulfonyl hydrazide, p,p'-oxy-bis-benzene sulfonylhydrazide.

Claim 16

An alloy of claim 1 wherein said compound is p-t-butyl benzolazide.

Claim 17

An alloy of claim 1 wherein said compound is N,N-dimethyl-N,N' dinitrosoterephthal-amide.

Claim 18

An alloy of claim 1 wherein said compound is a trihydrozaide triazene.

Claim 19

A foamable moldable polymeric alloy composition consisting essentially of: A. an addition polymer selected from the group consisting of: 1. a copolymer of said alkenyl aromatic monomer and an alkenyl nitrile monomer, 2. a grafted diene rubber grafted with said alkenyl aromatic and said alkenyl nitrile monomers or mixtures of (1) and (2), said mixtures having a major amount of (1) and a minor amount of (2), B. an interpolymer of an alkenyl aromatic monomer and maleic anhydride, wherein the weight ratio of said addition polymer to said interpolymer in said alloy is about 85:15 to 50:50, and C. a foaming agent selected from the group consisting of carbonates, bicarbonates, azo, hydrazides, hydrazines, azide and amide compounds, nitrogen, carbon dioxide or mixtures thereof.

Claim 20

A foamable moldable polymeric alloy composition consisting essentially of: A. an addition polymer selected from the group consisting of: 1. a copolymer of said alkenyl aromatic monomer and an alkenyl nitrile monomer, 2. a grafted diene rubber grafted with said alkenyl aromatic and said alkenyl nitrile monomers or mixtures of (1) and (2), said mixtures having a major amount of (1) and a minor amount of (2), B. an interpolymer of an alkenyl aromatic monomer and maleic anhydride, wherein the weight ratio of said addition polymer to said interpolymer in said alloy is about 85:15 to 50:50, and C. a foaming agent selected from the group consisting of carbonates, bicarbonates, azo, hydrazides, hydrazines, azide and amide compounds, nitrogen, carbon dioxide or mixtures thereof.

Claim 21

An alloy of claim 18 wherein said copolymer is styrene-acrylonitrile wherein the ratio of styrene to acrylonitrile is about 85:15 to 15:85.

Claim 22

An alloy of claim 18 wherein said interpolymers are styrene-maleic anhydride wherein the ratio of styrene to maleic anhydride is 65:35 to 95:5.

Claim 23

An alloy of claim 18 wherein said diene rubber is selected from the group consisting of polybutadiene and copolymers of butadiene-styrene, butadiene-acrylonitrile, polychloroprene, polyisoprene or mixtures thereof.

Claim 24

An alloy of claim 18 wherein said diene rubber is dispersed as rubber particles grafted with styrene and acrylonitrile in amounts of 10 to 100 parts of monomer per 100 parts of rubber.

Claim 25

An alloy of claim 18 wherein said compound is present in an amount of about 0.2 to 2.0% by weight based on said alloy.

Claim 26

An alloy of claim 18 wherein said compound is present in an amount sufficient to reduce the density of said alloy about 5 to 50% by weight when foamed by melt processing at temperatures of about 200° to 275° C.

Claim 27

An alloy of claim 18 wherein said copolymer has a molecular weight of about 100,000 to 300,000 Mw and said interpolymer has a molecular weight of about 100,000 to 400,000 Mw.

Claim 28

An alloy of claim 18 wherein said grafted diene rubber is present in an amount such that the diene rubber moiety is present in an amount from 2 to 35% by weight of said alloy.

Claim 29

An alloy of claim 18 wherein said alloy composition includes a diene rubber grafted with styrene and maleic anhydride.

Claim 30

An alloy of claim 1 wherein said alloy composition includes a diene rubber grafted with styrene and maleic anhydride.

Claim 31

A foamable moldable polymeric alloy composition for structural foams consisting essentially of: A. an addition polymer polyblend which comprises a mixture of a major amount of: 1. polystyrene, and a minor amount of: 2. a grafted diene rubber grafted with styrene monomer, B. an interpolymer of styrene and maleic anhydride wherein the weight ratio of said addition polymer to said interpolymer in said alloy is about 85:15 to 50:50, and C. a foaming agent selected from the group consisting of carbonates, bicarbonates, azo, hydrazides, hydrazines, azide and amide compounds, nitrogen, carbon dioxide or mixtures thereof.

Claim 32

A foamable moldable polymeric alloy composition for structural foams consisting essentially of: A. an addition polymer polyblend which comprises a mixture of a major amount of: 1. polystyrene, and a minor amount of: 2. a grafted diene rubber grafted with styrene monomer, B. an interpolymer of styrene and maleic anhydride wherein the weight ratio of said addition polymer to said interpolymer in said alloy is about 85:15 to 50:50, and C. a foaming agent selected from the group consisting of carbonates, bicarbonates, azo, hydrazides, hydrazines, azide and amide compounds, nitrogen, carbon dioxide or mixtures thereof.

Claim 33

A foamable moldable polymeric alloy composition consisting essentially of: A. an addition polymer selected from the group consisting of: 1. a copolymer of styrene-acrylonitrile monomer, 2. a grafted diene rubber grafted with styrene-acrylonitrile monomers or mixtures of (1) and (2), said mixture having a major amount of (1) and a minor amount of (2), B. an interpolymer of an alkenyl aromatic monomer and maleic anhydride, wherein the weight ratio of said addition polymer to said interpolymer in said alloy is about 85:15 to 50:50, and C. a foaming agent selected from the group consisting of carbonates, bicarbonates, azo, hydrazides, hydrazines, azide and amide compounds, nitrogen, carbon dioxide or mixtures thereof.

Claim 34

A foamable moldable polymeric alloy composition consisting essentially of: A. an addition polymer selected from the group consisting of: 1. a copolymer of styrene-acrylonitrile monomer, 2. a grafted diene rubber grafted with styrene-acrylonitrile monomers or mixtures of (1) and (2), said mixture having a major amount of (1) and a minor amount of (2), B. an interpolymer of an alkenyl aromatic monomer and maleic anhydride, wherein the weight ratio of said addition polymer to said interpolymer in said alloy is about 85:15 to 50:50, and C. a foaming agent selected from the group consisting of carbonates, bicarbonates, azo, hydrazides, hydrazines, azide and amide compounds, nitrogen, carbon dioxide or mixtures thereof.

Claim 35

A foamable composition of claim 1 wherein said foaming agent is nitrogen, said nitrogen being present in said composition in an amount sufficient to reduce the weight of said alloy 5 to 50% when foamed by melt processing at temperatures of 200° to 275° C.

Claim 36

A foamable composition of claim 1 wherein said foaming agent is carbon dioxide, said carbon dioxide being present in an amount sufficient to reduce the densities of said alloy about 5 to 50% when melt processed at temperatures of 200° to 275° C.

Claim 37

A foamable composition of claim 18 wherein said foaming agent is nitrogen, said nitrogen being present in said composition in an amount sufficient to reduce the weight of said alloy 5 to 50% when foamed by melt processing at temperatures of 200° to 275° C.

Claim 38

A foamable composition of claim 18 wherein said foaming agent is carbon dioxide, said carbon dioxide being present in an amount sufficient to reduce the densities of said alloy about 5 to 50% when melt processed at temperatures of 200° to 275° C.

Claim 39

A composition of claim 1 wherein said composition includes a diene rubber grafted with styrene and maleic anhydride.

Claim 40

A composition of claim 18 wherein said composition includes a diene rubber grafted with styrene and maleic anhydride.

Claim 41

A composition of claim 1 wherein a fire-retarding material, providing a halogen source, in an amount of about 2 to 30% by weight based on said composition.

Claim 42

A composition of claim 37 wherein said fire-retarding material is present in combination with an inorganic compound, said inorganic compound being present in an amount of about 0.01 to 20% by weight based on said composition.

Claim 43

A composition of claim 38 wherein said halogen source is selected from the group consisting of halogen containing polymers, rubbers, phenolics, aliphatic, aromatic and heterocylic compounds or mixtures thereof and wherein said inorganic material is selected from the group consisting of Sb 2 O 3 , Al 2 O 3 , Fe 2 O 3 , zincborate, borophosphates and complex polyphosphates.