Abstract Composition for obtaining rapidly hardening portland cement containing caum sulfate and calcium oxide wherein active di-aluminium trioxide is included in the form of di-aluminium pentahydroxychloride having the weight ratio of Al 2 O 3 :CASO 4 :CaO equal to 1:3.5 to 4.3:1.3 to 1.8. A method by which the composition is to be utilized, wherein 4 to 8 parts by weight of the composition are mixed with water, and initially introducing the dialuminium pentahydroxychloride. After its dissolution there are added, in succession, the calcium sulfate and the calcium oxide which are stirred and mixed with 100 parts by weight of pure clinker portland cement having a strength not less than 350. With the mixture thus obtained there are mixed cement pastes, cementsand mortars and concretes.
A method for production of an additive mixture for rapid hardening of portland cement which comprises dissolving dialuminium pentahydroxychloride in water, adding successively thereto calcium sulfate and calcium oxide in the weight ratios respectively of Al 2 O 3 :CaSO 4 :CaO=1:3.5 to 4.3:1.3 to 1.8 and thereafter homogenizing the resulting mixture.
Claim 2
Independent Claim
52 words
A method for production of an additive mixture for rapid hardening of portland cement which comprises dissolving dialuminium pentahydroxychloride in water, adding successively thereto calcium sulfate and calcium oxide in the weight ratios respectively of Al 2 O 3 :CaSO 4 :CaO=1:3.5 to 4.3:1.3 to 1.8 and thereafter homogenizing the resulting mixture.
Claim 3
Dependent Claim
17 words
A method according to claim 1 wherein the calcium sulfate is in the form of semi-hydrated gypsum.
Claim 4
Dependent Claim
16 words
A method according to claim 1 wherein calcium oxide is in the form of hydrated lime.