Fluorscent X-ray image intensifying screen
Assignee: Agfa Gevaert NV
•
Filing: 1978-04-18
•
Granted: 1980-05-27
•
Expires: 1998-04-18
Abstract
Abstract X-ray image intensifying screen including at least one fluorescent layer comprising phosphor particles dispersed in a binder and on top of such layer a protective layer containing a crosslinked polymer mass obtained by an acid-catalyzed reaction of a polymer or mixture of polymers containing reactive hydrogen atoms and a crosslinking agent, the crosslinking agent being an organic compound containing a plurality of etherified N-methylol groups.
Inventors
- 👤 Willy K. Van Landeghem
- 👤 Andre R. Suys
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:07
CPC Classifications
G; G21; G21K; G21K4/00; Y; Y10; Y10S; Y10S428/00; Y10S428/911; Y10S428/913; Y10S428/917; Y10T; Y10T428/00; Y10T428/31; Y10T428/31504; Y10T428/31786; Y10T428/31855; Y10T428/31909; Y10T428/31913; Y10T428/3192
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
65 words
X-ray image intensifying screen including at least one fluorescent layer comprising phosphor particles dispersed in a binder and on top of such layer a protective layer containing a crosslinked polymer mass obtained by an acid-catalyzed reaction of a polymer or mixture of polymers containing reactive hydrogen atoms and a crosslinking agent, the crosslinking agent being an organic compound containing a plurality of etherified N-methylol groups.
Claim 2
Dependent Claim
65 words
X-ray image intensifying screen including at least one fluorescent layer comprising phosphor particles dispersed in a binder and on top of such layer a protective layer containing a crosslinked polymer mass obtained by an acid-catalyzed reaction of a polymer or mixture of polymers containing reactive hydrogen atoms and a crosslinking agent, the crosslinking agent being an organic compound containing a plurality of etherified N-methylol groups.
Claim 3
Dependent Claim
36 words
A screen according to claim 1, wherein the polymer or mixture of polymers contains reactive hydrogen atoms forming part of one or more groups of the class consisting of free hydroxyl groups, ##STR7## and --COOH groups.
Claim 4
Dependent Claim
13 words
A screen according to claim 1, wherein the etherified N-methylol groups are ##STR8##
Claim 5
Dependent Claim
58 words
A screen according to any of the preceding claims, wherein the polymer is a polyester comprising free hydroxyl groups, a polyvinyl acetal in which part of the hydroxyl groups of the polyvinyl alcohol starting product has not been acetalized, a copolymer of vinyl alcohol and vinyl chloride or a copolymer of vinyl chloride, vinyl acetate and vinyl alcohol.
Claim 6
Dependent Claim
42 words
A screen according to claim 4, wherein the polymer is polyvinyl butyral with from 80 to 90% by weight of vinyl butyral units, 7 to 20% by weight of vinyl alcohol units and 0 to 3% by weight of vinyl ester units.
Claim 7
Dependent Claim
21 words
A screen according to claim 5, wherein the polyvinyl butyral has a molecular weight in the range of 45,000 to 55,000.
Claim 8
Dependent Claim
12 words
A screen according to claim 1, wherein the crosslinking agent is hexakis(methoxymethyl)-melamine.
Claim 9
Dependent Claim
17 words
A screen according to claim 1, wherein in the acid-catalyzed reaction p-toluene sulphonic acid has been used.
Claim 10
Dependent Claim
31 words
A screen according to claim 1, wherein the crosslinking agent has been used in an amount in the range of 5 to 20% by weight with respect to the crosslinkable polymer(s).
Claim 11
Dependent Claim
25 words
A screen according to claim 1, wherein the protective coating has in dry state a thickness in the range of 2 μm to 20 μm.
Claim 12
Dependent Claim
87 words
A screen according to claim 1, wherein the protective layer is light-diffusing, but does not bring about a reduction of fluorescent light emission by more than 50%, and wherein the light-diffusing layer is of such composition that when compared under identical X-ray exposure conditions with a radiographic combination of silver halide emulsion material and screen without said light-diffusing layer the image resolution in the silver halide emulsion material expressed in terms of modulation transfer at 1 line pair per mm is reduced by not more than 10%.
Claim 13
Dependent Claim
40 words
A screen according to claim 1, wherein the phosphor particles of the fluorescent layer include one or more rare-earth metal compounds containing as host metal and/or activator metal at least one element with atomic number 39 or 57 or 71.
Claim 14
Dependent Claim
28 words
A screen according to claim 12, wherein said phosphor particles are rare-earth oxysulfide or oxyhalide compounds of lanthanum or gadolinium activated with at least one other rare-earth metal.
References Cited (Backward Citations)
US1846515A
Cited
US2694153A
Cited
US2698991A
Cited
US2904689A
Cited
US2907882A
Cited
US3164719A
Cited
US3787238A
Cited
US4073777A
Cited
US4090085A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-05-27 | 1983-11-26 | 1984-05-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-05-27 | 1987-11-26 | 1988-05-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-05-27 | 1991-11-26 | 1992-05-27 | $7700.00 | Window Closed / Lapsed |