US4205033A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing compact silicon nitride ceramics
Assignee: Niterra Co Ltd
•
Filing: 1978-08-22
•
Granted: 1980-05-27
•
Expires: 1998-08-22
Abstract
Abstract A process for producing a compact silicon nitride ceramic product which comprises molding a powder mixture of Si 3 N 4 , Ta 2 O 5 and Al 2 O 3 in proportions defined by the region A, B, C, D in the FIGURE within the ranges of 65.0 to 96.0% by volume Si 3 N 4 , 1.0 to 32.0% by volume Ta 2 O 5 and 3.0 to 20.0% by volume Al 2 O 3 , and then firing the powder mixture in a non-oxidizing atmosphere containing a carbon compound; or hot-pressing the powder mixture; in a graphite mold.
Inventors
- 👤 Yoshinori Hattori
- 👤 Tamotu Miyachi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 04:23
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/597; C04B35/584; C04B35/593
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
113 words
A process for producing a compact silicon nitride ceramic product which comprises molding a powder mixture of Si 3 N 4 , Ta 2 O 5 and Al 2 O 3 in the volume proportions defined by the region A, B, C and D in the FIGURE, the points A, B, C and D representing powder mixtures of the compositions, in volume percent, indicated below: ______________________________________
Si.sub.3 N.sub.4
Ta.sub.2 O.sub.5
Al.sub.2 O.sub.3
______________________________________
A 65.0% 32.0% 3.0%
B 65.0% 15.0% 20.0%
C 79.0% 1.0% 20.0%
D 96.0% 1.0% 3.0%
______________________________________ and then firing the powder mixture in a non-oxidizing atmosphere containing a carbon compound; or hot-pressing the powder mixture; in a graphite mold.
Claim 2
Dependent Claim
113 words
A process for producing a compact silicon nitride ceramic product which comprises molding a powder mixture of Si 3 N 4 , Ta 2 O 5 and Al 2 O 3 in the volume proportions defined by the region A, B, C and D in the FIGURE, the points A, B, C and D representing powder mixtures of the compositions, in volume percent, indicated below: ______________________________________
Si.sub.3 N.sub.4
Ta.sub.2 O.sub.5
Al.sub.2 O.sub.3
______________________________________
A 65.0% 32.0% 3.0%
B 65.0% 15.0% 20.0%
C 79.0% 1.0% 20.0%
D 96.0% 1.0% 3.0%
______________________________________ and then firing the powder mixture in a non-oxidizing atmosphere containing a carbon compound; or hot-pressing the powder mixture; in a graphite mold.
Claim 3
Dependent Claim
58 words
The process of claim 1, wherein at least one alkaline earth metal oxide or an alkaline earth metal compound convertible to said oxide in an amount of 5 parts by weight or less as the alkaline earth metal oxide, per 100 parts by weight of the powder mixture is further added to the powder mixture prior to molding.
Claim 4
Dependent Claim
52 words
The process of claim 1, wherein said Si 3 N 4 has an average particle size of about 3μ or less, said Ta 2 O 5 has an average particle size of about 2μ or less and said Al 2 O 3 has an average particle size of about 2μ or less.
Claim 5
Dependent Claim
21 words
The process of claim 1, wherein said firing temperature is in the range of about 1600° C. to about 1850° C.
Claim 6
Dependent Claim
22 words
The process of claim 1, wherein said non-oxidizing atmosphere has oxygen present in an amount of about 5 volume percent or less.
Claim 7
Dependent Claim
36 words
The process of claim 1, wherein said hot-pressing is at a temperature in the range of about 1550° C. to about 1850° C. and is at a pressure of more than about 100 kg/cm 2 .
Claim 8
Dependent Claim
30 words
The process of claim 1, wherein said compact silicon nitride ceramic product has increased thermal stability and modulus of rupture strength in combination with a reduced coefficient of thermal expansion.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-05-27 | 1983-11-26 | 1984-05-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-05-27 | 1987-11-26 | 1988-05-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-05-27 | 1991-11-26 | 1992-05-27 | $7700.00 | Window Closed / Lapsed |