Method of forming a sintered ceramic product
Assignee: ZF International UK Ltd
•
Filing: 1974-12-23
•
Granted: 1976-11-02
•
Expires: 1994-12-23
Abstract
Abstract In a method of forming a sintered, ceramic product, aluminium nitride is reacted with silica at a temperature of between 1200° and 2000° C to form a single phase silicon aluminium oxynitride ceramic material, the reaction mixture at said temperature containing not more than 60% by weight of the aluminium nitride and also containing first and second metal oxides other than silica. The metal oxides are arranged so that they do not introduce into the mixture a combination of magnesium oxide and alumina alone and further are arranged so that during the reaction they combine with part of said silica to form a silicate glass having a liquidus temperature below that of the silicate glass which would be formed from silica with either of said metal oxides alone. The silicate glass formed then aids densification of the ceramic material during sintering.
Inventors
- 👤 Roland John Lumby
- 👤 Bernard North
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 19:29
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/597; C04B35/01; C04B35/10; C04B35/111
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
190 words
In a method of forming a sintered ceramic product wherein a mixture consisting essentially of an effective amount of aluminum nitride, silica, alumina and silicon nitride is provided and the relative proportions of said aluminum nitride, silica, alumina and silicon nitride are such that there is formed, after surrounding with a protective medium and sintering at a temperature between 1200°-2000° C, a ceramic material consisting of at least 95% by weight of a single phase compound obeying the formula Si.sub.6.sub.-z Al.sub.z N.sub.8.sub.-z O.sub.z where z is greater than zero and less than or equal to 5, the improvement being the step of introducing into said mixture at least two metal oxides, each being of a different metal, selected from the group consisting of magnesium oxide, a manganese oxide, lithium oxide, titanium dioxide, a boron oxide, and ferric oxide, wherein said at least two metal oxides react with part of the silica present in said mixture to form a silicate glass having a liquidus temperature below that of the silicate which would be formed from silica and either of the metal oxides alone, said glass aiding densification of the ceramic material.
Claim 2
Dependent Claim
190 words
In a method of forming a sintered ceramic product wherein a mixture consisting essentially of an effective amount of aluminum nitride, silica, alumina and silicon nitride is provided and the relative proportions of said aluminum nitride, silica, alumina and silicon nitride are such that there is formed, after surrounding with a protective medium and sintering at a temperature between 1200°-2000° C, a ceramic material consisting of at least 95% by weight of a single phase compound obeying the formula Si.sub.6.sub.-z Al.sub.z N.sub.8.sub.-z O.sub.z where z is greater than zero and less than or equal to 5, the improvement being the step of introducing into said mixture at least two metal oxides, each being of a different metal, selected from the group consisting of magnesium oxide, a manganese oxide, lithium oxide, titanium dioxide, a boron oxide, and ferric oxide, wherein said at least two metal oxides react with part of the silica present in said mixture to form a silicate glass having a liquidus temperature below that of the silicate which would be formed from silica and either of the metal oxides alone, said glass aiding densification of the ceramic material.
Claim 3
Dependent Claim
185 words
In a method of forming a sintered ceramic product wherein a mixture consisting essentially of an effective amount of aluminum nitride, silica, and alumina is provided and the relative proportions of said aluminum nitride, silica and alumina are such that there is formed, after surrounding with a protective medium and sintering at a temperature between 1200°-2000° C, a ceramic material consisting of at least 95% by weight of a single phase compound obeying the formula: Si.sub.6.sub.-z Al.sub.z N.sub.8.sub.-z O.sub.z where z is greater than 4 and less than or equal to 5, the improvement being the step of introducing into said mixture at least two metal oxides, each being of a different metal, selected from the group consisting of magnesium oxide, a manganese oxide, lithium oxide, titanium dioxide, a boron oxide, and ferric oxide, wherein said at least two metal oxides react with part of the silica present in the mixture to form a silicate glass having a liquidus below that of a silicate which would be formed from silica with either of the metal oxides alone, said glass aiding densification of the ceramic material.
Claim 4
Dependent Claim
185 words
In a method of forming a sintered ceramic product wherein a mixture consisting essentially of an effective amount of aluminum nitride, silica, and alumina is provided and the relative proportions of said aluminum nitride, silica and alumina are such that there is formed, after surrounding with a protective medium and sintering at a temperature between 1200°-2000° C, a ceramic material consisting of at least 95% by weight of a single phase compound obeying the formula: Si.sub.6.sub.-z Al.sub.z N.sub.8.sub.-z O.sub.z where z is greater than 4 and less than or equal to 5, the improvement being the step of introducing into said mixture at least two metal oxides, each being of a different metal, selected from the group consisting of magnesium oxide, a manganese oxide, lithium oxide, titanium dioxide, a boron oxide, and ferric oxide, wherein said at least two metal oxides react with part of the silica present in the mixture to form a silicate glass having a liquidus below that of a silicate which would be formed from silica with either of the metal oxides alone, said glass aiding densification of the ceramic material.
Claim 5
Dependent Claim
27 words
The method as claimed in claim 1, wherein at least part of the silica in said mixture is introduced as an impurity contained by the silicon nitride.
Claim 6
Dependent Claim
27 words
The method as claimed in claim 1 wherein, at least part of the alumina in the mixture is introduced as an impurity contained by the aluminum nitride.
Claim 7
Dependent Claim
44 words
The method as claimed in claim 1 wherein the liquidus temperature of the silicate formed from silica with the metal oxides together is at least a 100° C below that of the silicate which would be formed from silica with each metal oxide alone.
Claim 8
Dependent Claim
15 words
The method as claimed in claim 1, wherein the heating step is accompanied by pressure.
Claim 9
Dependent Claim
44 words
The method as claimed in claim 6, wherein the metal oxides are each pressing aids for said ceramic material and their total quantity in the mixture is less than the quantity which would be required if each metal oxide were present on its own.
Claim 10
Dependent Claim
42 words
The method as claimed in claim 1, wherein at least one of the constituents present in said mixture is introduced into the starting materials used to produce the mixture as a compound which provides the required constituent or constituents at said temperature.
Claim 11
Dependent Claim
40 words
The method as claimed in claim 1, wherein prior to reaction to produce the silicate glass, at least one of the metal oxides is present in said mixture in combination with a portion of said silica as a metal silicate.
Claim 12
Dependent Claim
20 words
The method as claimed in claim 1, wherein said at least two metal oxides are magnesium oxide and trimanganese tetroxide.
Claim 13
Dependent Claim
29 words
The method as claimed in claim 10, wherein said magnesium oxide and trimanganese tetroxide are present in said mixture in a weight ratio of the order of 1:4 respectively.
Claim 14
Dependent Claim
18 words
The method as claimed in claim 10, wherein said at least two metal oxides also includes ferric oxide.
Claim 15
Dependent Claim
29 words
The method as claimed in claim 1, wherein said at least two metal oxides are magnesium oxide and lithium oxide present in said mixture in substantially equal weight proportions.
Claim 16
Dependent Claim
20 words
The method as claimed in claim 13, wherein said at least two metal oxides also include an oxide or boron.
Claim 17
Dependent Claim
31 words
The method as claimed in claim 1, wherein said at least two metal oxides are magnesium oxide and titanium dioxide and are present in said mixture in substantially equal weight proportions.
Claim 18
Dependent Claim
40 words
The method as claimed in claim 1, wherein the amount of said at least two metal oxides present in said mixture at said temperature is such that said silicate glass constitutes up to 5% by weight of the sintered product.
References Cited (Backward Citations)
US3108887A
Cited
GB970639A
Cited
US3262761A
Cited
US3262763A
Cited
US3409417A
Cited
US3833389A
Cited
US3903230A
Cited
US3836374A
Cited
US3837871A
Cited
US3950464A
Cited
DE2354024A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-02 | 1980-05-03 | 1980-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-02 | 1984-05-03 | 1984-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-02 | 1988-05-03 | 1988-11-02 | $7700.00 | Window Closed / Lapsed |