Batch method for making solid-electrolyte capacitors
Assignee: Vishay Sprague Inc
•
Filing: 1978-07-17
•
Granted: 1980-05-20
•
Expires: 1998-07-17
Abstract
Abstract A plurality of porous valve-metal pellets are suspended by their anode riser wires from a holding bar. After the conventional steps of anodically forming an oxide film over the surfaces of the pellets and depositing a solid electrolyte and a metallic counterelectrode over the film, an insulative resin layer is applied over the pellets by an electrostatic fluidized powder-bed coating step, selective air-stream powder-removal steps and heat curing steps. Anode and cathode end cap terminals are subsequently formed over opposite ends of each pellet, preferably by applying and curing a silver loaded paint, curing the paint, nickel immersion plating over the silver and cladding the nickel film with solder.
Inventors
- 👤 N. Christian McGrath
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 08:08
CPC Classifications
H; H01; H01G; H01G9/00; H01G9/0029; H01G9/004; H01G9/008; H01G9/012
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
256 words
A batch method for making solid-electrolyte capacitors including providing a plurality of porous valve-metal pellets each having one end face from which a wire of said valve-metal extends, an opposite end face and at least one side face being contiguous with said two end faces; suspending said pellets by their respective wires from a holding bar; anodically forming an oxide film over the surfaces of each said porous pellet; disposing a solid electrolyte over said film of said each pellet; and depositing a conductive counterelectrode layer overlying said solid electrolyte of said each pellet in a region over said at least one side face and extending over said opposite end face thereof; wherein the improvement comprises: (a) bringing said suspended pellets to a fluidized bed of a fusible insulative resin powder and applying a high d.c. voltage to said holding bar with respect to said fluidized bed to electrostatically form a powder coating on said suspended pellets and on said wires; (b) selectively removing said powder coating from said opposite end face of said each pellet to expose said counterelectrode layer; (c) heating said suspended pellets to fuse and cure the remaining portions of said powder coatings; (d) subsequently forming an anode terminal over said one end face of each said pellet in contact with the corresponding of said wires, and forming a cathode terminal spaced from said anode terminal over said opposite end face of each said pellet in contact with said counterelectrode; and (e) severing said wires to separate said pellets from said bar.
Claim 2
Dependent Claim
256 words
A batch method for making solid-electrolyte capacitors including providing a plurality of porous valve-metal pellets each having one end face from which a wire of said valve-metal extends, an opposite end face and at least one side face being contiguous with said two end faces; suspending said pellets by their respective wires from a holding bar; anodically forming an oxide film over the surfaces of each said porous pellet; disposing a solid electrolyte over said film of said each pellet; and depositing a conductive counterelectrode layer overlying said solid electrolyte of said each pellet in a region over said at least one side face and extending over said opposite end face thereof; wherein the improvement comprises: (a) bringing said suspended pellets to a fluidized bed of a fusible insulative resin powder and applying a high d.c. voltage to said holding bar with respect to said fluidized bed to electrostatically form a powder coating on said suspended pellets and on said wires; (b) selectively removing said powder coating from said opposite end face of said each pellet to expose said counterelectrode layer; (c) heating said suspended pellets to fuse and cure the remaining portions of said powder coatings; (d) subsequently forming an anode terminal over said one end face of each said pellet in contact with the corresponding of said wires, and forming a cathode terminal spaced from said anode terminal over said opposite end face of each said pellet in contact with said counterelectrode; and (e) severing said wires to separate said pellets from said bar.
Claim 3
Dependent Claim
29 words
The method of claim 1 wherein said removing is accomplished by directing a sharply defined gas stream at said opposite end faces to selectively blow away said powder therefrom.
Claim 4
Dependent Claim
26 words
The method of claim 2 wherein said directing is in a plane corresponding essentially to the plane of said opposite end face of said each pellet.
Claim 5
Dependent Claim
32 words
The method of claim 1 additionally comprising directing a sharply defined gas stream at a middle region of said each wire to selectively remove said powder coating from said middle wire regions.
Claim 6
Independent Claim
12 words
The method of claims 2 or 4 wherein said gas is air.
Claim 7
Dependent Claim
20 words
The method of claim 1 wherein said bringing and applying is accomplished simultaneously with respect to said plurality of pellets.
Claim 8
Dependent Claim
13 words
The method of claim 1 wherein said resin powder is fusible epoxy resin.
Claim 9
Dependent Claim
60 words
The method of claim 7 wherein said heating is accomplished by first holding and heating at one temperature said suspended pellets by said bar in a vaccum type oven to fuse and transform each of said powder coatings to a gel coating, and subsequently curing said gel coating to a hard coating at a higher temperature than said one temperature.
Claim 10
Dependent Claim
33 words
The method of claim 8 wherein said heating in said vacuum oven is for about 15 minutes in a reduced pressure atmosphere less than 600 mmHg, said one temperature being about 85° C.
Claim 11
Dependent Claim
50 words
The method of claim 1 wherein said terminal forming steps are accomplished prior to said severing and comprise spraying a conductive paint at said pellet ends to form two spaced cup-shaped layers over said one and said opposite end faces of said each pellet, respectively, and curing said paint layers.
Claim 12
Dependent Claim
33 words
The method of claim 1 wherein said forming of said terminals includes applying a silver containing paint, heating to cure said paint, and selectively plating a nickel film over said cured silver paint.
Claim 13
Dependent Claim
35 words
The method of claim 11 additionally comprising baring a portion of said each wire prior to said plating so that said nickel film extends from over said one end face and contacts said bared portion.
Claim 14
Dependent Claim
22 words
The method of claim 11 wherein said plating is accomplished by submersing said plurality of pellets into a nickel immersion plating solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-05-20 | 1983-11-19 | 1984-05-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-05-20 | 1987-11-19 | 1988-05-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-05-20 | 1991-11-19 | 1992-05-20 | $7700.00 | Window Closed / Lapsed |