Self-extinguishing thermoplastic molding compositions
Assignee: BASF SE
•
Filing: 1978-06-05
•
Granted: 1980-04-29
•
Expires: 1998-06-05
Abstract
Abstract Thermoplastic molding compositions based on rubber-modified styrene-acrylonitrile copolymers containing a halogenated styrene oligomer as the effective flame-proofing agent which is sufficiently heat-stable, does not interfere with processing on conventional machinery, does not corrode or cause coatings on such machinery, and has virtually no adverse effect on the impact strength of the polymers. The flameproofing agent as a rule has a degree of polymerization of from 3 to 200 and can be incorporated into the polymer by conventional methods; the polymer may or may not contain additional synergistic agents and processing auxiliaries, which are incorporated in the conventional manner and in the conventional amounts.
Inventors
- 👤 Hermann Gausepohl
- 👤 Herbert Naarmann
- 👤 Klaus Penzien
- 👤 Rudolf Stephan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 07:09
CPC Classifications
C; C08; C08L; C08L25/00; C08L25/02; C08L25/04; C08L25/08; C08L25/12; C08L51/00; C08L51/04; C08L55/00; C08L55/02; C08L25/18
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
200 words
A thermoplastic molding composition comprising (A) from 6 to 100 percent by weight, based on (A+B), of a graft product manufactured by graft polymerization of 1. from 10 to 95 percent by weight, based on (A), of a mixture of styrene and acrylonitrile or an alkyl derivative thereof in the weight ratio of from 90:10 to 60:40, in the presence of 2. from 90 to 5 percent by weight, based on (A), of a rubbery polymer having a glass transition temperature of below 0° C., (B) from 0 to 94 percent by weight, based on (A+B), of a copolymer of styrene and acrylonitrile or an alkyl derivative thereof in the weight ratio of from 90:10 to 60:40, the content of the rubbery polymer (A 2) in the molding composition being from 5 to 40 percent by weight based on the sum of (A+B), (C) from 5 to 30 percent by weight, based on the sum of (A+B), of one or more heat-stable brominated styrene oligomers which contain 40 to 80 percent by weight of bromine and which have a mean degree of polymerization of from 3 to 200 to act as a flameproofing agent, with or without (D) further additives.
Claim 2
Dependent Claim
200 words
A thermoplastic molding composition comprising (A) from 6 to 100 percent by weight, based on (A+B), of a graft product manufactured by graft polymerization of 1. from 10 to 95 percent by weight, based on (A), of a mixture of styrene and acrylonitrile or an alkyl derivative thereof in the weight ratio of from 90:10 to 60:40, in the presence of 2. from 90 to 5 percent by weight, based on (A), of a rubbery polymer having a glass transition temperature of below 0° C., (B) from 0 to 94 percent by weight, based on (A+B), of a copolymer of styrene and acrylonitrile or an alkyl derivative thereof in the weight ratio of from 90:10 to 60:40, the content of the rubbery polymer (A 2) in the molding composition being from 5 to 40 percent by weight based on the sum of (A+B), (C) from 5 to 30 percent by weight, based on the sum of (A+B), of one or more heat-stable brominated styrene oligomers which contain 40 to 80 percent by weight of bromine and which have a mean degree of polymerization of from 3 to 200 to act as a flameproofing agent, with or without (D) further additives.
Claim 3
Dependent Claim
23 words
A thermoplastic molding composition as claimed in claim 1, wherein a synergistic flameproofing agent is present in addition to the halogenated styrene oligomers.
Claim 4
Dependent Claim
16 words
A thermoplastic molding composition as claimed in claim 2, wherein the synergistic agent is antimony trioxide.
References Cited (Backward Citations)
FR1101025A
Cited
GB874006A
Cited
DE1123823B
Cited
US3075944A
Cited
GB1345211A
Cited
US3830766A
Cited
DE2046795B2
Cited
US3962164B1
Cited
US3962164A
Cited
DE2328535B2
Cited
GB1412517A
Cited
GB1416585A
Cited
DE2358855C3
Cited
US3943195A
Cited
US4107231A
Cited
DE2515473B2
Cited
US4137212A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-29 | 1983-10-29 | 1984-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-29 | 1987-10-29 | 1988-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-29 | 1991-10-29 | 1992-04-29 | $7700.00 | Window Closed / Lapsed |