Process for preparing water-soluble alkyd resins
Assignee: Daicel Corp
•
Filing: 1978-04-12
•
Granted: 1980-04-29
•
Expires: 1998-04-12
Abstract
Abstract A process for preparing a water-soluble alkyd resin, which comprises (1) reacting (i) at least one of (a) a 1,2-epoxyalkane containing 6 to 28 carbon atoms, (b) a straight-chain internal epoxyalkane containing 6 to 20 carbon atoms, (c) a mixture of one or more of the 1,2-epoxyalkane (a) and/or the internal epoxyalkane (b), or (d) a mixture of one or more of the 1,2-epoxyalkane (a) and/or the internal epoxyalkane (b) and an unsaturated fatty acid containing 12 to 18 carbon atoms in a molar ratio of about 4:1 to about 2:1 of the 1,2-epoxyalkane (a) and/or the internal epoxyalkane (b) to the unsaturated fatty acid; with (ii) at least one of (a') an aromatic carboxyl compound selected from the group consisting essentially of phthalic anhydride, isophthalic acid, terephthalic acid, an ester of isophthalic acid and an ester of terephthalic acid, (b') a mixture of two or more of the aromatic carboxyl compounds (a'), or (c') a mixture of one or more of the aromatic carboxylic compounds (a') and an aliphatic dicarboxylic acid having 3 or more carbon atoms or an anhydride thereof; and (iii) a polyhydric alcohol containing 2 to 10 carbon atoms to form a polyester containing hydroxyl groups and having an acid value of about 5 or less, a hydroxyl value of about 40 to about 200 and an average molecular weight of about 600 to about 2,500; (2) reacting the hydroxyl groups of the polyester with an aromatic polycarboxylic acid anhydride to adjust the acid value of the polyester to about 25 to about 80 and form a carboxyl group-containing alkyd resin; and (3) neutralizing the carboxyl group-containing alkyd resin with a base.
Inventors
- 👤 Masyoshi Kubo
- 👤 Michio Nakanishi
- 👤 Shoji Watanabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:09
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/02; C08G63/12; C08G63/40; C08G63/42; C08G63/46; C08G63/48; C08K; C08K5/00; C08K5/16; C08K5/34; C09; C09D; C09D167/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31786; Y10T428/31794
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
283 words
A process for preparing a water-soluble alkyd resin, which comprises (1) reacting (i) at least one of (a) a 1,2-epoxyalkane containing 6 to 28 carbon atoms, (b) a straight-chain internal epoxyalkane containing 6 to 20 carbon atoms, (c) a mixture of one or more of the 1,2-epoxyalkane (a) and/or the internal epoxyalkane (b), or (d) a mixture of one or more of the 1,2-epoxyalkane (a) and/or the internal epoxyalkane (b) and an unsaturated fatty acid containing 12 to 18 carbon atoms in a molar ratio of about 4:1 to about 2:1 of the 1,2-epoxyalkane (a) and/or the internal epoxyalkane (b) to the unsaturated fatty acid; with (ii) at least one of a mixture of one or more aromatic carboxylic compounds selected from the group consisting of phthalic anhydride, isophthalic acid, terephthalic acid, an ester of isophthalic acid and an ester of terephthalic acid and an aliphatic dicarboxylic acid having 3 or more carbon atoms or an anhydride thereof and (iii) a polyhydric alcohol containing 2 to 10 carbon atoms, wherein said at least one of reactants (i)(a), (i)(b), (i)(c) or (i)(d) is added to a mixture of said reactants (ii) and (iii) while heating to thus form a polyester containing hydroxyl groups and having an acid value of about 5 or less, a hydroxyl value of about 40 to about 200 and an average molecular weight of about 600 to about 2,500, said reacting resulting in dehydroesterification; (2) reacting the hydroxyl groups of the polyester with an aromatic polycarboxylic acid anhydride to adjust the acid value of the polyester to about 25 to about 80 and form a carboxyl group-containing alkyd resin; and (3) neutralizing the carboxyl group-containing alkyd resin with a base.
Claim 2
Dependent Claim
283 words
A process for preparing a water-soluble alkyd resin, which comprises (1) reacting (i) at least one of (a) a 1,2-epoxyalkane containing 6 to 28 carbon atoms, (b) a straight-chain internal epoxyalkane containing 6 to 20 carbon atoms, (c) a mixture of one or more of the 1,2-epoxyalkane (a) and/or the internal epoxyalkane (b), or (d) a mixture of one or more of the 1,2-epoxyalkane (a) and/or the internal epoxyalkane (b) and an unsaturated fatty acid containing 12 to 18 carbon atoms in a molar ratio of about 4:1 to about 2:1 of the 1,2-epoxyalkane (a) and/or the internal epoxyalkane (b) to the unsaturated fatty acid; with (ii) at least one of a mixture of one or more aromatic carboxylic compounds selected from the group consisting of phthalic anhydride, isophthalic acid, terephthalic acid, an ester of isophthalic acid and an ester of terephthalic acid and an aliphatic dicarboxylic acid having 3 or more carbon atoms or an anhydride thereof and (iii) a polyhydric alcohol containing 2 to 10 carbon atoms, wherein said at least one of reactants (i)(a), (i)(b), (i)(c) or (i)(d) is added to a mixture of said reactants (ii) and (iii) while heating to thus form a polyester containing hydroxyl groups and having an acid value of about 5 or less, a hydroxyl value of about 40 to about 200 and an average molecular weight of about 600 to about 2,500, said reacting resulting in dehydroesterification; (2) reacting the hydroxyl groups of the polyester with an aromatic polycarboxylic acid anhydride to adjust the acid value of the polyester to about 25 to about 80 and form a carboxyl group-containing alkyd resin; and (3) neutralizing the carboxyl group-containing alkyd resin with a base.
Claim 3
Dependent Claim
14 words
The process of claim 1, wherein the 1,2-epoxyalkane contains 10 to 18 carbon atoms.
Claim 4
Dependent Claim
24 words
The process of claim 1 or 2, wherein the unsaturated fatty acid is oleic acid, ricinoleic acid, linoleic acid, linolenic acid or eleosteric acid.
Claim 5
Dependent Claim
15 words
The process of claim 1 or 2, wherein the aliphatic dicarboxylic acid is adipic acid.
Claim 6
Dependent Claim
30 words
The process of claim 1 or 2, wherein the polyhydric alcohol is at least one member selected from the group consisting of neopentyl glycol, trimethylolpropane, glycerol and a mixture thereof.
Claim 7
Dependent Claim
28 words
The process of claim 3, wherein the polyhydric alcohol is at least one member selected from the group consisting of neopentyl glycol, trimethylolpropane, glycerol and a mixture thereof.
Claim 8
Dependent Claim
28 words
The process of claim 4, wherein the polyhydric alcohol is at least one member selected from the group consisting of neopentyl glycol, trimethylolpropane, glycerol and a mixture thereof.
Claim 9
Dependent Claim
24 words
The process of claim 1, wherein said 1,2-epoxyalkane has the general formula (I): ##STR3## wherein n is an integer of from 3 to 25.
Claim 10
Dependent Claim
25 words
The process of claim 8, wherein said 1,2-epoxyalkane of the general formula (I) is 1,2-epoxyhexane, 1,2-epoxyheptane, 1,2-epoxyoctane, 1,2-epoxynonane, 1,2-epoxydecane, 1,2-epoxyundecane, 1,2-epoxydodecane, 1,2-epoxytetradecane, 1,2-epoxyhexadecane and 1,2-epoxyoctadecane.
Claim 11
Dependent Claim
16 words
The process of claim 1, wherein the straight-chain internal epoxyalkane contains 8 to 14 carbon atoms.
Claim 12
Dependent Claim
35 words
The process of claim 1, wherein the straight-chain internal epoxyalkane has the general formula (II): ##STR4## wherein p and m each represents 0 or a positive integer and p and m satisfy the relationship 2≦m+p≦16.
Claim 13
Dependent Claim
22 words
The process of claim 1, wherein the aliphatic dicarboxylic acid or anhydride thereof is adipic acid, maleic acid or an anhydride thereof.
Claim 14
Dependent Claim
20 words
The process of claim 1, wherein said polyhydric alcohol is a dihydric alcohol, a trihydric alcohol or a tetrahydric alcohol.
Claim 15
Dependent Claim
24 words
The process of claim 1, wherein said polyhydric alcohol is ethylene glycol, propylene glycol, diethylene glycol, neopentyl glycol, glycerol, trimethylolethane, trimethylolpropane, pentaerythritol or diglycerol.
Claim 16
Dependent Claim
43 words
The process of claim 1, wherein the amount of the 1,2-epoxyalkane or straight-chain internal epoxyalkane or mixture thereof with the unsaturated fatty acid ranges from about 20 to about 50% by weight based on the weight of the water-soluble alkyd resin ultimately obtained.
Claim 17
Dependent Claim
32 words
The process of claim 1, wherein the reacting in step (1) is at a temperature of about 100° to about 250° C. and in the presence of a catalyst promoting the reaction.
Claim 18
Dependent Claim
58 words
The process of claim 16, wherein said catalyst is an amine, a quaternary ammonium salt, a phosphine compound or a complex of boron trifluoride and an ether or an amine and said catalyst is present in an amount of about 0.01 to about 5% by weight based on the weight of the 1,2-epoxyalkane or the straight-chain internal epoxyalkane.
Claim 19
Dependent Claim
21 words
The process of claim 1, wherein the reacting in step (2) is at a temperature of about 100° to 150° C.
Claim 20
Dependent Claim
32 words
The process of claim 1, wherein the neutralizing in step (3) is with a base selected from the group consisting of an alkylamine, an alcoholamine, a cyclic amine or an inorganic base.
Claim 21
Dependent Claim
21 words
The process of claim 19, wherein the neutralizing in step (3) is to a pH of about 7 to about 9.
Claim 22
Dependent Claim
13 words
A water-soluble alkyd resin produced in accordance with the process of claim 1.
Claim 23
Dependent Claim
17 words
A coating composition comprising the water-soluble alkyd resin of claim 21, an amino resin and a solvent.
Claim 24
Dependent Claim
46 words
The process of claim 1, wherein reacting to form the polyester of step (1) is performed by adding a solvent azeotroping with water and, while heating at about 150° to about 250° C. with stirring, water is removed from the reaction system, whereby said dehydroesterification proceeds.
Claim 25
Dependent Claim
23 words
The process of claim 23, wherein said solvent azeotroping with water is added in an amount of about 5 to 20% by weight.
Claim 26
Dependent Claim
10 words
The process of claim 24, wherein said solvent is xylene.
References Cited (Backward Citations)
CA728716A
Cited
US3397255A
Cited
US3427266A
Cited
GB1298773A
Cited
DE2620726A1
Cited
US4054614A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-29 | 1983-10-29 | 1984-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-29 | 1987-10-29 | 1988-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-29 | 1991-10-29 | 1992-04-29 | $7700.00 | Window Closed / Lapsed |