Economical method of making high-strength glass fiber mats particularly useful for roofing products
Assignee: Building Materials Corp of America
•
Filing: 1979-05-16
•
Granted: 1980-04-29
•
Expires: 1999-05-16
Abstract
Abstract The glass mat made herein is comprised of two fibrous components, namely, individual filament glass fibers and extended glass fiber elements. These components are formed herein in situ in a wet-laid process from original bundles of glass fibers. The individual filaments appear by conventional filamentation of the bundles. The extended fiber elements, however, are formed by longitudinal extension of a given bundle whose fibers are connected longitudinally. Thereby the effective length of a fiber element is very much greater than the length of the fibers therein. The fiber elements are further characterized by a non-uniform diameter, as contrasted to the fibers themselves, being thicker in the midsection of the element where connection of fibers is maximized, and tapered towards its ends, where fiber connection is at a minimum. The extended fiber elements preferably predominate by weight of the fibrous content of the mat over the individual filaments. The desired ratio of the two components is achieved in the method of the invention by using bundles whose fibers have a long length, and by very gentle agitation of the dispersion slurry for a short period of time.
Inventors
- 👤 Alfredo A. Bondoc
- 👤 V. Robert Canfield
- 👤 B. Randall Ziegler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 09:10
CPC Classifications
D; D21; D21H; D21H13/00; D21H13/36; D21H13/38; D21H13/40; D21F; D21F11/00
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
206 words
A method of making high-strength glass fiber mats comprising a plurality of individual filament glass fibers comprising about 20% to 60% by weight of the fibrous material in said mat, and a plurality of extended glass fiber elements comprised of longitudinally connected fibers said elements there having a length which is greater than the length of the fibers in said element, and a diameter which is nonuniform, being greater in the mid-portion thereof than at its ends, said elements comprising about 40% to 80% by weight of the fibrous material in said mat, both said individual filament fibers and said extended fiber elements being substantially randomly oriented and uniformly dispersed throughout said material, and having a binder substance therein to hold said fibrous material together which comprises the steps of: (a) forming an aqueous slurry of bundles of glass fiber having a length of about 13/4 to 3 inches and a diameter of about 8 to 20 microns and a dispersant, (b) gently agitating said slurry to disperse said bundles into said individual filaments and extended fiber elements, (c) passing said thus agitated dispersion slurry onto a mat-forming screen to form said fibrous mat and removing water therefrom and, (d) applying a binder to said mat.
Claim 2
Independent Claim
206 words
A method of making high-strength glass fiber mats comprising a plurality of individual filament glass fibers comprising about 20% to 60% by weight of the fibrous material in said mat, and a plurality of extended glass fiber elements comprised of longitudinally connected fibers said elements there having a length which is greater than the length of the fibers in said element, and a diameter which is nonuniform, being greater in the mid-portion thereof than at its ends, said elements comprising about 40% to 80% by weight of the fibrous material in said mat, both said individual filament fibers and said extended fiber elements being substantially randomly oriented and uniformly dispersed throughout said material, and having a binder substance therein to hold said fibrous material together which comprises the steps of: (a) forming an aqueous slurry of bundles of glass fiber having a length of about 13/4 to 3 inches and a diameter of about 8 to 20 microns and a dispersant, (b) gently agitating said slurry to disperse said bundles into said individual filaments and extended fiber elements, (c) passing said thus agitated dispersion slurry onto a mat-forming screen to form said fibrous mat and removing water therefrom and, (d) applying a binder to said mat.
Claim 3
Dependent Claim
33 words
A method according to claim 1 wherein said individual filaments comprise about 30% to 50%, and said extended fiber elements about 50% to 70%, by weight of the fibrous material in said mat.
Claim 4
Dependent Claim
29 words
A method according to claim 1 wherein said individual filaments comprise about 40%, and said extended fiber elements about 60%, by weight of the fibrous material in said mat.
Claim 5
Dependent Claim
21 words
A method according to claim 1 wherein the fibers in said bundles have a length of about 2 to 21/2 inches.
Claim 6
Dependent Claim
22 words
A method according to claim 1 wherein a single source of bundles are used containing fibers having the same length and diameter.
Claim 7
Dependent Claim
23 words
A method according to claim 1 wherein said dispersant is present in an amount of about 2 to 100 ppm of said slurry.
Claim 8
Dependent Claim
20 words
A method according to claim 1 wherein said dispersant is present in an amount of about 5 to 30 ppm.
Claim 9
Dependent Claim
14 words
A method according to claim 1 wherein said dispersant is a tertiary amine oxide.
Claim 10
Dependent Claim
21 words
A method according to claim 1 wherein the fiber slurry consistency is about 0.1 to 2% by weight of the fibers.
Claim 11
Dependent Claim
15 words
A method according to claim 9 wherein said fiber consistency is about 0.2 to 1%.
Claim 12
Dependent Claim
47 words
A method according to claim 1 wherein said process is run continuously, with fiber bundles being fed at a uniform rate to form the fiber slurry, and water which is removed from said screen being recycled both for dilution water and for formation of the aqueous slurry.
Claim 13
Dependent Claim
15 words
A method according to claim 1 wherein the slurry is agitated for about 5 minutes.
Claim 14
Dependent Claim
26 words
A method according to claim 12 in which the energy input is about 0.6 kw-hr. for 5 minutes of agitation of an 80 cubic meter slurry.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-29 | 1983-10-29 | 1984-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-29 | 1987-10-29 | 1988-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-29 | 1991-10-29 | 1992-04-29 | $7700.00 | Window Closed / Lapsed |