Polyolefin resin composition
Assignee: Idemitsu Kosan Co Ltd
•
Filing: 1978-12-04
•
Granted: 1980-04-22
•
Expires: 1998-12-04
Abstract
Abstract Since their surfaces are inactive, polyolefin resins are difficult to plate. A plating method utilizing sensitizing-activation of the surface has been used for plating polyolefin resins. Many attempts have been made to improve the plating properties of the surfaces of polyolefin resins, for example, a mechanical method, a method employing a solvent, a method of coating other types of resins on the surface, etc. As methods modifying the plastics themselves, there are several; a method of introducing polar radicals by graft polymerization, etc., a method of introducing atactic polypropylene or block copolymer of polypropylene and polyethylene, a method of mixing rubber or a copolymer of ethylene and vinyl acetate, a method of mixing in an inorganic filler, etc. Recently, it was attempted to apply a high chrome etching-catalyst method for plating polyolefin resin, said method being mainly used in the automatic process of plating although the plating adhesion is poorer than that obtained with the plating method of sensitizing-activation. However, there was found no polyolefin resin composition having plating properties that can compare with ABS resin for applying the plating method of a high chrome etching-catalyst method. We have developed a polyolefin resin composition which can be plated by a high-chrome etching-catalyst method. As a result, we have found that the object of the invention can be attained by blending a compound containing a cyano group with a mixture consisting of polyolefin resin and inorganic filler, and kneading and melting them.
Inventors
- 👤 Akio Inayoshi
- 👤 Hitomi Tomari
- 👤 Kikuo Nagatoshi
- 👤 Yasuo Hata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:54
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08K; C08K3/00; C08K3/01; C08K3/013; C08K3/34; C08K5/00; C08K5/16; C08K5/315; C08L23/10; C08L33/00; C08L33/18; C08L33/20; C08L51/00; C08L51/06; C08L55/00; C08L55/02; C08L71/00; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/0353; H05K1/0373; H05K3/00; H05K3/10; H05K3/18; H05K3/181
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
239 words
A polyolefin resin composition having excellent plating properties which comprises: (A) 100 parts by weight of a mixture consisting of from 20 to 80 weight percent of polyolefin resin and from 80 to 20 weight percent of inorganic filler, (B) from 3 to 60 parts by weight of a compound containing a cyano group, said compound containing a cyano group is at least one member selected from the group consisting of acrylonitrile-styrene resin, acrylonitrile-butadiene-styrene resin, acrylonitrile-methyl-acrylate resin, acrylonitrile-indene resin, acrylonitrile-itaconic acid resin, acrylonitrile-methyl-methacrylate-styrene resin, acrylonitrile-cyclopentadiene resin, terephthalodinitrile and β-naphthonitrile, (C) from 0 to 20 parts by weight of rubber, said rubber being at least one rubber selected from (1) solid diene rubber selected from the group consisting of isoprene rubber, butadiene rubber, styrene-butadiene rubber, and acrylonitrile-butadiene rubber, (2) liquid rubber having an average molecular weight of from about 500 to about 10,000, which is at least one member selected from the group consisting of 1,2-polybutadiene, 1,4-polybutadiene, styrene-butadiene copolymer, acrylonitrile-butadiene copolymer, polyisoprene, polychloroprene, 1,2-polypentadiene, acrylonitrile-butadiene copolymer, butadiene-isoprene copolymer and butadiene-pentadiene copolymer, and such polymers containing functional groups selected from carboxyl, hydroxy, mercapto, halogen, amino, aziridino, and epoxy, (3) unsaturated dicarboxylic acid half esters, (4) heat-decomposed rubber, and (5) ozone-decomposed rubber, (D) from 0 to 50 parts by weight of an unsaturated carboxylic acid added polyolefin resin, and (E) from 0 to 20 parts by weight of at least one surfactant selected from the group consisting of nonionic surfactant and polyethyleneglycol.
Claim 2
Dependent Claim
239 words
A polyolefin resin composition having excellent plating properties which comprises: (A) 100 parts by weight of a mixture consisting of from 20 to 80 weight percent of polyolefin resin and from 80 to 20 weight percent of inorganic filler, (B) from 3 to 60 parts by weight of a compound containing a cyano group, said compound containing a cyano group is at least one member selected from the group consisting of acrylonitrile-styrene resin, acrylonitrile-butadiene-styrene resin, acrylonitrile-methyl-acrylate resin, acrylonitrile-indene resin, acrylonitrile-itaconic acid resin, acrylonitrile-methyl-methacrylate-styrene resin, acrylonitrile-cyclopentadiene resin, terephthalodinitrile and β-naphthonitrile, (C) from 0 to 20 parts by weight of rubber, said rubber being at least one rubber selected from (1) solid diene rubber selected from the group consisting of isoprene rubber, butadiene rubber, styrene-butadiene rubber, and acrylonitrile-butadiene rubber, (2) liquid rubber having an average molecular weight of from about 500 to about 10,000, which is at least one member selected from the group consisting of 1,2-polybutadiene, 1,4-polybutadiene, styrene-butadiene copolymer, acrylonitrile-butadiene copolymer, polyisoprene, polychloroprene, 1,2-polypentadiene, acrylonitrile-butadiene copolymer, butadiene-isoprene copolymer and butadiene-pentadiene copolymer, and such polymers containing functional groups selected from carboxyl, hydroxy, mercapto, halogen, amino, aziridino, and epoxy, (3) unsaturated dicarboxylic acid half esters, (4) heat-decomposed rubber, and (5) ozone-decomposed rubber, (D) from 0 to 50 parts by weight of an unsaturated carboxylic acid added polyolefin resin, and (E) from 0 to 20 parts by weight of at least one surfactant selected from the group consisting of nonionic surfactant and polyethyleneglycol.
Claim 3
Dependent Claim
106 words
A polyolefin resin composition according to claim 1, which comprises: (A) 100 parts by weight of a mixture consisting of from 40 to 80 weight percent of said polyolefin and from 60 to 20 weight percent of said inorganic filler, (B) from 5 to 40 parts by weight of said compound containing a cyano group, (C) from 1 to 10 parts by weight of said rubber, (D) from 0.5 to 30 parts by weight of said unsaturated carboxylic acid added polyolefin resin, and (E) from 0.3 to 15 parts by weight of at least one surfactant selected from the group consisting of nonionic surfactant and polyethyleneglycol.
Claim 4
Dependent Claim
40 words
The polyolefin resin composition of claim 1 or claim 2 wherein said polyolefin resin is a member selected from the group consisting of low density polyethylene, medium density polyethylene, high density polyethylene, polypropylene, polybutene-1, poly-4-methylpentene-1, ethylenepropylene copolymer and ethylene-butene copolymer.
Claim 5
Dependent Claim
54 words
The polyolefin resin composition of claims 1 or 2, wherein the inorganic filler comprises at least one member selected from the group consisting of alumina, zinc white, magnesium oxide, calcium carbonate, talc, clay, silica, kieselguhr, mica, calcium sulfite, calcium sulfate, barium sulfate, titanium oxide, calcium silicate, glass powder, glass fiber, asbestos and gypsum fiber.
Claim 6
Dependent Claim
20 words
The polyolefin resin composition of claim 4, wherein the particle size of said inorganic filler is up to 10 microns.
Claim 7
Dependent Claim
32 words
The polyolefin resin composition of claim 1 or claim 2, wherein said rubber is a solid rubber selected from the group consisting of isoprene rubber, butadiene rubber, styrene-butadiene rubber and acrylonitrile-butadiene rubber.
Claim 8
Dependent Claim
56 words
The polyolefin resin composition of claim 1 or claim 2, wherein said rubber is liquid rubber having an average molecular weight of from about 500 to about 10,000, which is at least one member selected from the group consisting of 1,2-polybutadiene, 1,4-polybutadiene, styrene-butadiene copolymer, acrylonitrile-butadiene copolymer, polyisoprene, polychloroprene, 1,2-polypentadiene, acrylonitrile-butadiene copolymer, butadiene-isoprene copolymer and butadiene-pentadiene copolymer.
Claim 9
Dependent Claim
101 words
The polyolefin resin composition of claims 1 or 2, wherein said unsaturated carboxylic acid added polyolefin resin comprises a polyolefin resin containing an unsaturated carboxylic acid polar radical, and wherein said unsaturated carboxylic acid is at least one member of the group consisting of maleic acid, maleic anhydride, nudic anhydride, citraconic acid, crotonic acid, isocrotonic acid, mesaconic acid, itaconic acid, angelic acid, sorbic acid, methacrylic acid, itaconic anhydride, citraconic anhydride and acrylic acid, and said polyolefin resin is at least one member selected from the group consisting of low density polyethylene, medium density polyethylene, high density polyethylene, polypropylene, polybutene-1 and poly-4-methylpentene-1.
Claim 10
Dependent Claim
37 words
The polyolefin resin composition of claim 1 or claim 2, wherein said surfactant is at least one member selected from the group consisting of polyoxyethylene alkylether, polyoxyethylene alkylphenolether, polyoxyethylene alkylester, polyoxyethylene sorbitanalkylester, polyoxyethylene alkylamine and polyethylene glycol.
Claim 11
Dependent Claim
17 words
The polyolefin resin composition of claim 4, wherein said compound containing a cyano group is acrylonitrile-butadiene-styrene resin.
Claim 12
Dependent Claim
17 words
The polyolefin resin composition of claim 4, wherein said compound containing a cyano group is acrylonitrile-styrene resin.
Claim 13
Dependent Claim
17 words
The polyolefin resin composition of claim 4, wherein said compound containing a cyano group is acrylonitrile-methyl-acrylate resin.
References Cited (Backward Citations)
US3953655A
Cited
US4063004A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-22 | 1983-10-22 | 1984-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-22 | 1987-10-22 | 1988-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-22 | 1991-10-22 | 1992-04-22 | $7700.00 | Window Closed / Lapsed |