Method of manufacturing a semiconductor device and semiconductor device manufactured while using such a method
Assignee: US Philips Corp
•
Filing: 1978-08-18
•
Granted: 1980-04-22
•
Expires: 1998-08-18
Abstract
Abstract A method of manufacturing LOCOS transistors in which base doping, emitter doping and emitter metallization are provided via the same aperture. Problems at the edge of the sunken oxide are eliminated by a two-stage doping technique so that the channel stopper diffusion in the epitaxial layer may be omitted, which presents particular advantages in the manufacture of I 2 L devices.
Inventors
- 👤 Johannes A. A. van Gils
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 03:42
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/61; H10D; H10D62/00; H10D62/10; H10D62/17; H10D62/177; H10D84/00; H10D84/01; H10D84/0112; H10D84/0116; H10D84/02; H10D84/03; H10D84/038; H10D84/60; H10D84/65; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/0121; H10W10/0124; H10W10/0125; H10W10/0126; H10W10/10; H10W10/13
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
274 words
A method of manufacturing a semiconductor device having a semiconductor body comprising a circuit element having at least three zones of alternating conductivity type situated on top of one other and a sunken oxide pattern at the upper surface of said semiconductor body which bounds a surface-adjoining region containing said zones of alternating conductivity type, including upper and lower zones of a first type conductivity and an intermediate zone of a second type conductivity opposite to that of the first, said intermediate zone forming p-n junctions with said upper and lower zones, which zones extend to said sunken oxide pattern, the method comprising the steps of: providing the surface-adjoining region of a first type conductivity semiconductor material in said semiconductor body; providing the sunken oxide pattern at the upper surface of said semiconductor body and surrounding said surface-adjoining region; providing said intermediate zone of the second type conductivity in said surface-adjoining region in a first doping step; masking the surface of said intermediate zone to form a window which, together with the sunken oxide pattern, defines a surface part of the intermediate zone which adjoins the sunken oxide pattern; doping said intermediate zone at least through said window in a second doping step to increase the doping level of an upper portion of at least that part of the intermediate zone which adjoins the sunken oxide pattern; providing said upper zone of the first type conductivity through said window, in said upper portion of the intermediate zone which adjoins the sunken oxide pattern and down to a depth of less than that of said upper portion; and contacting said upper zone through said window.
Claim 2
Independent Claim
274 words
A method of manufacturing a semiconductor device having a semiconductor body comprising a circuit element having at least three zones of alternating conductivity type situated on top of one other and a sunken oxide pattern at the upper surface of said semiconductor body which bounds a surface-adjoining region containing said zones of alternating conductivity type, including upper and lower zones of a first type conductivity and an intermediate zone of a second type conductivity opposite to that of the first, said intermediate zone forming p-n junctions with said upper and lower zones, which zones extend to said sunken oxide pattern, the method comprising the steps of: providing the surface-adjoining region of a first type conductivity semiconductor material in said semiconductor body; providing the sunken oxide pattern at the upper surface of said semiconductor body and surrounding said surface-adjoining region; providing said intermediate zone of the second type conductivity in said surface-adjoining region in a first doping step; masking the surface of said intermediate zone to form a window which, together with the sunken oxide pattern, defines a surface part of the intermediate zone which adjoins the sunken oxide pattern; doping said intermediate zone at least through said window in a second doping step to increase the doping level of an upper portion of at least that part of the intermediate zone which adjoins the sunken oxide pattern; providing said upper zone of the first type conductivity through said window, in said upper portion of the intermediate zone which adjoins the sunken oxide pattern and down to a depth of less than that of said upper portion; and contacting said upper zone through said window.
Claim 3
Dependent Claim
54 words
A method of manufacturing a semiconductor device as in claim 1, wherein said circuit element comprises a transistor, the lower zone of said circuit element comprises the collector region of said transistor, the intermediate zone thereof comprises the base region of said transistor and the upper zone comprises the emitter zone of said transistor.
Claim 4
Dependent Claim
54 words
A method of manufacturing a semiconductor device as in claim 1, wherein said circuit element comprises a transistor, the lower zone of said circuit element comprises the emitter region of said transistor, the intermediate zone thereof comprises the base region of said transistor and the upper zone comprises the collector zone of said transistor.
Claim 5
Dependent Claim
22 words
A method as claimed in claim 1, wherein the upper zone is provided in the semiconductor body by means of ion implantation.
Claim 6
Dependent Claim
20 words
A method as claimed in claim 1, wherein the second doping step is carried out by means of ion implantation.
Claim 7
Dependent Claim
32 words
A method as claimed in claim 1, wherein the concentration of impurities in the second doping step is increased over the whole surface of the intermediate zone of the second conductivity type.
Claim 8
Dependent Claim
105 words
A method as claimed in claim 2, wherein said mask, in addition to forming the window through which the upper zone of the first type conductivity is provided, constitutes, together with the sunken oxide pattern, a second window which forms a contact window for the base region and leaves unmasked a second surface part of the intermediate zone of the second type conductivity adjoining the sunken oxide, which second window is covered, during the provision of the upper zone of the first type conductivity, with a masking layer of a material which can be removed selectively with respect to the mask and the sunken oxide.
Claim 9
Dependent Claim
27 words
A method as claimed in claim 1, wherein the mask comprises a layer of a material which can be removed selectively with respect to the sunken oxide.
Claim 10
Dependent Claim
16 words
A method as claimed in claim 8, wherein the mask comprises a layer of silicon nitride.
Claim 11
Dependent Claim
35 words
A method as claimed in claim 1, wherein the starting material in which the surface-adjoining material is provided is a substrate of the second type conductivity having a surface layer of the first type conductivity.
Claim 12
Dependent Claim
15 words
A method as claimed in claim 10, wherein the surface layer is an epitaxial layer.
Claim 13
Dependent Claim
91 words
A method as claimed in claim 1, wherein a mask masking the semiconductor body against oxidation is provided on the surface of the body, after which the body is subjected to an etching treatment in which said mask masking against oxidation forms an etching mask, recesses are formed at the area of the exposed parts of the semiconductor body not covered by the mask masking against oxidation, and the oxidation treatment to obtain the sunken oxide pattern is then carried out, said recesses being filled at least substantially entirely with oxide.
Claim 14
Dependent Claim
107 words
A method as claimed in claim 12, wherein the recesses extend down to below the mask masking against oxidation and, after providing said recesses, impurities of the second type conductivity are provided by means of ion implantation in parts of the recesses which are defined by the parts of the mask masking against oxidation which project over the edge of the recesses, and said impurities, during the subsequent oxidation treatment to obtain the sunken oxide pattern, diffuse deeper into the body and, below the sunken oxide pattern, form zones of the second type conductivity which, viewed on the surface, are situated entirely below the sunken oxide pattern.
Claim 15
Dependent Claim
83 words
A method as claimed in claim 13, wherein the sunken oxide pattern is provided over at least substantially the whole thickness of the surface layer and below the sunken oxide pattern a zone of the second type conductivity is formed which is situated entirely below the sunken oxide pattern and in the substrate of the second type conductivity and which has a sufficiently high doping level such that formation of channels of the first type conductivity below the sunken oxide pattern is prevented.
Claim 16
Dependent Claim
13 words
A semiconductor device manufactured by using a method as claimed in claim 1.
References Cited (Backward Citations)
US3928091A
Cited
US3992232A
Cited
US4008107A
Cited
US3996077A
Cited
US4029527A
Cited
US4045249A
Cited
GB1530010A
Cited
US4066473A
Cited
US4111720A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-22 | 1983-10-22 | 1984-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-22 | 1987-10-22 | 1988-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-22 | 1991-10-22 | 1992-04-22 | $7700.00 | Window Closed / Lapsed |