Manufacture of carbon fibres
Assignee: BP PLC
•
Filing: 1978-05-04
•
Granted: 1980-04-08
•
Expires: 1998-05-04
Abstract
Abstract The invention relates to a process for the manufacture of carbon and/or graphite fibres from natural organic fibres, obtained particularly from the distillation residues of coal or petroleum, by irradiation by microwaves. The process according to the invention consists in subjecting the fibres to a preparatory thermal treatment up to a temperature of between 300° and 1500° C. in an inert atmosphere, for example of nitrogen, argon, helium or hydrogen and then irradiating them with microwaves. The microwaves may have frequencies between 900 and 30,000 MHz and preferably between 2000 and 15,000 MHz and use a power of between 10W and 30kW and preferably between 50W and 10kW. The irradiation is preferably also in an inert atmosphere, for a period ranging from 10 seconds to 15 minutes. The fibres may be oxidized for example in an atmosphere of oxygen, ozone or air up to a temperature of between 100° and 250° C. before the preparatory thermal treatment. The carbon and/or graphite fibres thus obtained, having an improved breaking strength, are used particularly for the reinforcement of plastic materials.
Inventors
- 👤 Jean-Francois G. Bailly-Lacresse
- 👤 Alain P. Crepaux
- 👤 Philippe G. J. Thomas
- 👤 Albert Bonzom
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:27
CPC Classifications
D; D01; D01F; D01F9/00; D01F9/08; D01F9/12; D01F9/14; D01F9/145
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
138 words
A process for the manufacture of carbon and/or graphite fibers which comprises subjecting fibers obtained by spinning a product chosen from coal tar pitches, pitches obtained from residues of the steam cracking of petroleum fractions or pitches obtained from petroleum crude oil residues to a preparatory thermal treatment comprising raising the temperature to at least 450° up to 1000° C. in an inert atmosphere and thereafter subjecting the fibers to irradiation with microwaves to effect carbonisation and/or graphitisation, the preparatory thermal treatment using a rate of increase of temperature of 0.5° and 1° C. per minute up to 420° C., 0.1° to 0.5° C. per minute from 420° to 450° C. and 1° to 5° C. per minute beyond 450° C., the duration of irradiation by microwaves in the irradiation treatment being between 10 seconds and 15 minutes.
Claim 2
Dependent Claim
138 words
A process for the manufacture of carbon and/or graphite fibers which comprises subjecting fibers obtained by spinning a product chosen from coal tar pitches, pitches obtained from residues of the steam cracking of petroleum fractions or pitches obtained from petroleum crude oil residues to a preparatory thermal treatment comprising raising the temperature to at least 450° up to 1000° C. in an inert atmosphere and thereafter subjecting the fibers to irradiation with microwaves to effect carbonisation and/or graphitisation, the preparatory thermal treatment using a rate of increase of temperature of 0.5° and 1° C. per minute up to 420° C., 0.1° to 0.5° C. per minute from 420° to 450° C. and 1° to 5° C. per minute beyond 450° C., the duration of irradiation by microwaves in the irradiation treatment being between 10 seconds and 15 minutes.
Claim 3
Dependent Claim
33 words
Process in accordance with claim 1, characterised in that the Conradson carbon content of the pre-treated fibres in greater than 83 percent by weight and is preferably at least 88 percent by weight.
Claim 4
Dependent Claim
29 words
Process in accordance with claim 1, characterised in that the preparatory thermal treatment is carried out in the presence of a gas which is nitrogen, argon, helium or hydrogen.
Claim 5
Dependent Claim
40 words
Process in accordance with claim 1, characterised in that the fibres have a Kraemer-Sarnow softening point of between 100° and 250° C., preferably between 180° and 250° C., and a Conradson carbon content of less than 80 percent by weight.
Claim 6
Dependent Claim
26 words
Process in accordance with claim 1, characterised in that the irradiation by microwaves uses an electromagnetic radiation of a frequency of between 900 and 30,000 MHz.
Claim 7
Dependent Claim
21 words
Process in accordance with claim 5, characterised in that the frequency of the electromagnetic radiation used is higher than 5000 MHz.
Claim 8
Dependent Claim
23 words
Process in accordance with claim 1, characterised in that the power of the electromagnetic radiation used is between 10 W and 30 kW.
Claim 9
Dependent Claim
23 words
Process in accordance with claim 1, characterised in that the temperature reached during the treatment by microwaves is between 400° and 2800° C.
Claim 10
Dependent Claim
20 words
Process in accordance with claim 1, characterised in that the irradiation by microwaves is carried out in an inert atmosphere.
Claim 11
Dependent Claim
25 words
Process in accordance with claim 9, characterised in that the irradiation by microwaves is carried out in an atmosphere of nitrogen, argon, helium or hydrogen.
Claim 12
Dependent Claim
30 words
Process in accordance with claim 1, characterised in that, prior to the preparatory thermal treatment there is an oxidation treatment up to a temperature ranging from 100° to 250° C.
Claim 13
Dependent Claim
25 words
Process in accordance with claim 11, characterised in that the oxidation treatment uses a rate of increase of temperature of 0.1° to 0.5° per minute.
Claim 14
Dependent Claim
52 words
Process in accordance with claim 11, characterised in that, when a fibre having a softening point lower than 150° C. is used, the oxidation treatment is carried out in the liquid phase in the presence of an oxidising agent chosen from nitric acid, sodium hypochlorite, hydrogen peroxide, potassium dichromate and, potassium permanganate.
Claim 15
Dependent Claim
40 words
Process in accordance with claim 11, characterised in that, when a fibre having a softening point higher than 150° C. is used, the oxidation treatment is carried out in the gaseous phase in the presence of oxygen, ozone or air.
References Cited (Backward Citations)
GB1261353A
Cited
US3595946A
Cited
US3607063A
Cited
US3702054A
Cited
JPS4724186U
Cited
US3919376A
Cited
US3974264A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-08 | 1983-10-08 | 1984-04-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-08 | 1987-10-08 | 1988-04-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-08 | 1991-10-08 | 1992-04-08 | $7700.00 | Window Closed / Lapsed |