Impact-resistant styrene resin composition
Assignee: Asahi Kasei Corp
•
Filing: 1978-09-25
•
Granted: 1980-03-25
•
Expires: 1998-09-25
Abstract
Abstract The disclosure relates to a resin composition comprising (A) 75-98 parts by weight of a block copolymer mixture of vinyl aromatic hydrocarbon and conjugated diolefin and (B) 25-2 parts by weight of an impact-resistant styrene resin, characterized in that said copolymer mixture (A) is a mixture of a copolymer (1) and a copolymer (2) (the weight ratio of the copolymer (1) to the copolymer (2) is 1.5 or more), the copolymer (1) being a copolymer which contains 55-85% by weight of vinyl aromatic hydrocarbon, consists of at least one vinyl aromatic hydrocarbon polymer block and at least one conjugated diene polymer block, and has a number average molecular weight of about 10,000 to about 500,000 and the copolymer (2) being a homopolymer of vinyl aromatic hydrocarbon or a copolymer which consists of at least one vinyl aromatic hydrocarbon polymer block and at least one conjugated diene polymer block, the vinyl aromatic hydrocarbon content of said copolymer being 75% by weight or more and at least 5% by weight higher than that of the copolymer (1), said homopolymer or copolymer having a number average molecular weight of about 500 to about 130,000, both of said copolymer (1) and said copolymer (2) being obtained by polymerization in an inert organic solvent with an organolithium compound as a catalyst; and that said impact-resistant styrene resin (B) is a polymer obtained by graft-polymerizing 3-12% by weight of a rubbery conjugated diene polymer and 97-88% by weight of a vinyl aromatic hydrocarbon. The said resin composition is far superior to conventional resin compositions of similar type in balance between impact resistance and transparency.
Inventors
- 👤 Yasushi Sato
- 👤 Toshio Ibaragi
- 👤 Masanobu Ishihara
- 👤 Makoto Honda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 12:07
CPC Classifications
C; C08; C08L; C08L53/00; C08L53/02
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
238 words
A resin composition comprising (A) 75-98 parts by weight of a block copolymer mixture of a vinyl aromatic hydrocarbon and a conjugated diene and (B) 25 - 2 parts by weight of an impact-resistant styrene resin, wherein said copolymer mixture (A) is a mixture of: (1) a copolymer consisting of at least one vinyl aromatic hydrocarbon polymer block and at least one conjugated diene polymer block, and having a vinyl aromatic hydrocarbon content of 55-85% by weight and a number average molecular weight of about 10,000 to about 500,000, and (2) a homopolymer of vinyl aromatic hydrocarbon or a copolymer consisting of at least one vinyl aromatic hydrocarbon polymer block and at least one conjugated diene polymer block, and having a vinyl aromatic hydrocarbon content of 75% by weight or more which is at least 5% by weight higher than that of the copolymer (1), said copolymer and said homopolymer both having a number average molecular weight of about 500 to about 130,000, the weight ratio of said copolymer (1) to said homopolymer or copolymer (2) in said mixture being 1.5/1 or more, said copolymer (1) and said copolymer (2) being both obtained by polymerization with an organolithium compound as a catalyst in an inert organic solvent, and wherein said impact-resistant styrene resin (B) is a graftcopolymer of 97 to 88% by weight of a vinyl aromatic hydrocarbon on 3-12% by weight of a rubbery conjugated diene polymer.
Claim 2
Dependent Claim
238 words
A resin composition comprising (A) 75-98 parts by weight of a block copolymer mixture of a vinyl aromatic hydrocarbon and a conjugated diene and (B) 25 - 2 parts by weight of an impact-resistant styrene resin, wherein said copolymer mixture (A) is a mixture of: (1) a copolymer consisting of at least one vinyl aromatic hydrocarbon polymer block and at least one conjugated diene polymer block, and having a vinyl aromatic hydrocarbon content of 55-85% by weight and a number average molecular weight of about 10,000 to about 500,000, and (2) a homopolymer of vinyl aromatic hydrocarbon or a copolymer consisting of at least one vinyl aromatic hydrocarbon polymer block and at least one conjugated diene polymer block, and having a vinyl aromatic hydrocarbon content of 75% by weight or more which is at least 5% by weight higher than that of the copolymer (1), said copolymer and said homopolymer both having a number average molecular weight of about 500 to about 130,000, the weight ratio of said copolymer (1) to said homopolymer or copolymer (2) in said mixture being 1.5/1 or more, said copolymer (1) and said copolymer (2) being both obtained by polymerization with an organolithium compound as a catalyst in an inert organic solvent, and wherein said impact-resistant styrene resin (B) is a graftcopolymer of 97 to 88% by weight of a vinyl aromatic hydrocarbon on 3-12% by weight of a rubbery conjugated diene polymer.
Claim 3
Dependent Claim
195 words
A resin composition according to claim 1, wherein said copolymer mixture is obtained in an inert organic solvent by (i) polymerizing with an organolithium compound catalyst the vinyl aromatic hydrocarbon and the conjugated diene in a weight ratio of 0/100 to 60/40 in an amount of 1 to 80% by weight based on the total weight of the monomers to be used in all the steps to prepare: (a) an active polymer of the conjugated diene, or (b) an active polymer consisting of a random copolymer of the conjugated diene and the vinyl aromatic hydrocarbon, or (c) an active polymer consisting of at least one vinyl aromatic hydrocarbon polymer block and at least one conjugated diene polymer block, and then (ii) adding the residual vinyl aromatic hydrocarbon and conjugated diene in a weight ratio of 100/0 to 75/25, and a fresh organolithium compound to the active polymer obtained in (i), and continuing the polymerization to prepare: (d) a homopolymer of vinyl aromatic hydrocarbon or (e) a copolymer consisting of at least one vinyl aromatic hydrocarbon polymer block and at least one conjugated diene polymer block, while prolonging the chain of the copolymer obtained in (i).
Claim 4
Dependent Claim
20 words
A resin composition according to claim 1 or 2, wherein said inert solvent is composed mainly of an aliphatic hydrocarbon.
Claim 5
Dependent Claim
16 words
A resin composition according to claim 3, wherein said aliphatic hydrocarbon is n-hexane, n-pentane or isopentane.
Claim 6
Dependent Claim
15 words
A resin composition according to claim 1 or 2, wherein said inert solvent is cyclohexane.
Claim 7
Dependent Claim
36 words
A resin composition according to claim 1 or 2, wherein said vinyl aromatic hydrocarbon is styrene, o-methylstyrene, m-methylstyrene, p-methylstyrene, α-methylstyrene, dimethylstyrene or a mixture thereof and said conjugated diene is 1,3-butadiene, isoprene or a mixture thereof.
Claim 8
Dependent Claim
93 words
A resin composition according to claim 1, wherein said copolymer (2) constituting the copolymer mixture (A) is a copolymer which is obtained by polymerization in an inert solvent with an organolithium compound as a catalyst; which consists of at least one vinyl aromatic hydrocarbon polymer block and at least one conjugated diene polymer block; which has a vinyl aromatic hydrocarbon content of 75% by weight which is at least 5% by weight higher than that of the copolymer (1); and which has a number average molecular weight of about 500 to about 130,000.
Claim 9
Dependent Claim
34 words
A resin composition according to claim 1, 2 or 7, wherein the vinyl aromatic hydrocarbon content of the copolymer (2) is 10% by weight higher than the vinyl aromatic hydrocarbon content of copolymer (1).
Claim 10
Dependent Claim
48 words
A resin composition according to claim 1, 2 or 7, wherein the copolymer (1) constituting the copolymer mixture (A) has a molecular weight of about 30,000 to about 300,000 and the copolymer (2) constituting the copolymer mixture (A) has a molecular weight of about 10,000 to about 100,000.
Claim 11
Dependent Claim
21 words
A resin composition according to claim 9, wherein the copolymer (2) has a number average molecular weight of 10,000 to 80,000.
Claim 12
Dependent Claim
33 words
A resin composition according to claim 1, 2 or 7, wherein at least 35% of the chain of the copolymer (1) is substantially identical with the chain of the copolymer (2) in structure.
Claim 13
Dependent Claim
17 words
A resin composition according to claim 1 or 2, wherein said organolithium compound is n-butyllithium or sec-butyllithium.
References Cited (Backward Citations)
GB726583A
Cited
US3907929A
Cited
DE2453110A1
Cited
US3907930A
Cited
US4073831A
Cited
US3936365A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-25 | 1983-09-24 | 1984-03-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-25 | 1987-09-24 | 1988-03-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-25 | 1991-09-24 | 1992-03-25 | $7700.00 | Window Closed / Lapsed |