Heat-resisting ceramic fibers and method for manufacture thereof
Assignee: Ibigawa Electric Industry Co Ltd
•
Filing: 1978-02-27
•
Granted: 1980-03-25
•
Expires: 1998-02-27
Abstract
Abstract Highly heat-resisting ceramic fibers are manufactured either by simply coating the surface of ceramic fibers with at least one phosphorus compound or by further subjecting the resultant coated ceramic fibers to a heat treatment. The ceramic fibers having the surface coated with said phosphorus compound or the ceramic fibers having the phosphorus compound contained therein at a gradually decreasing concentration in the direction of increasing depth from the surface which are manufactured by the aforesaid method are capable of high resistance to heat.
Inventors
- 👤 Yoshiro Moriya
- 👤 Kazuhito Ikai
- 👤 Makoto Tanaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 17:46
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B20/00; C04B20/10; C04B20/1055; C04B35/00; C04B35/622; C04B35/62227; C04B35/62231; C04B41/45; C04B41/50; C04B41/5076; C04B41/5092; C04B41/80; C04B41/81; C04B41/85; D; D01; D01F; D01F11/00; F; F27; F27D; F27D1/00; F27D1/0003; F27D1/0006; F27D1/0009; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294; Y10T428/2958; Y10T428/2964
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
135 words
Highly heat-resistant fibers possessing a thermal contraction under load of not more than 10% at a temperature of 1400° C., comprising: ceramic fibers composed predominantly of silica and alumina each present in the fibers in an amount of at least 25% wt.% and a combined amount of at least 80 wt.% and containing very small precipitated crystals of cristobalite and/or mullite close to the surface of the individual fibers, said precipitated crystals formed by heat treatment of said fibers coated with a phosphorus compound such that from 0.5 to 10% by weight based on P 2 O 5 of said phosphorus compound is incorporated into said ceramic fibers, the size and distribution of said precipitated crystals to the fibers being controlled by the introduction of the indicated quantity of said phosphorus compound into said fibers.
Claim 2
Dependent Claim
135 words
Highly heat-resistant fibers possessing a thermal contraction under load of not more than 10% at a temperature of 1400° C., comprising: ceramic fibers composed predominantly of silica and alumina each present in the fibers in an amount of at least 25% wt.% and a combined amount of at least 80 wt.% and containing very small precipitated crystals of cristobalite and/or mullite close to the surface of the individual fibers, said precipitated crystals formed by heat treatment of said fibers coated with a phosphorus compound such that from 0.5 to 10% by weight based on P 2 O 5 of said phosphorus compound is incorporated into said ceramic fibers, the size and distribution of said precipitated crystals to the fibers being controlled by the introduction of the indicated quantity of said phosphorus compound into said fibers.
Claim 3
Dependent Claim
30 words
The heat-resistant fibers of claim 1, wherein the ceramic fibers are composed predominately of silica and alumina in respective amounts ranging from 30 to 50% and from 50 to 70%.
Claim 4
Dependent Claim
60 words
The heat-resistant fibers of claim 1, wherein the phosphorous compound is at least one member selected from one group consisting of orthophosphoric acid, pyrophosphoric acid, metaphosphoric acid, triphosphoric acid, tetraphosphoric acid, and MH 2 PO 4 , M 2 HPO 4 and M 3 PO 4 wherein M is selected from the group consisting of alkali metals and ammonium ion.
Claim 5
Dependent Claim
56 words
The heat-resistant fibers of claim 1, wherein the amount of said phosphorous compound incorporated into said ceramic fibers is within the range of 1 to 6% by weight computed as P 2 O 5 and the thermal contraction under load of said fibers is not more than 5% by weight at a temperature of 1400° C.
Claim 6
Dependent Claim
105 words
Highly heat-resisting fibers possessing a thermal contraction under load of not more than 10% at a temperature of 1400° C., comprising: ceramic fibers composed predominately of silica and alumina each present in an amount of at least 25% by weight and in a combined amount of at least 80% by weight, and a phosphorous compound incorporated into the ceramic fibers in an amount of from 0.5 to 10% by weight computed as P 2 O 5 , said ceramic fibers having the phosphorus contained therein in such a way that the phosphorous concentration distribution gradually decreases from the surface to the core of each fiber.
Claim 7
Dependent Claim
105 words
Highly heat-resisting fibers possessing a thermal contraction under load of not more than 10% at a temperature of 1400° C., comprising: ceramic fibers composed predominately of silica and alumina each present in an amount of at least 25% by weight and in a combined amount of at least 80% by weight, and a phosphorous compound incorporated into the ceramic fibers in an amount of from 0.5 to 10% by weight computed as P 2 O 5 , said ceramic fibers having the phosphorus contained therein in such a way that the phosphorous concentration distribution gradually decreases from the surface to the core of each fiber.
Claim 8
Dependent Claim
30 words
The highly heat-resistant fibers of claim 5, wherein said ceramic fibers contain silica and alumina in respective amounts ranging from 30 to 50% and from 50 to 70% by weight.
Claim 9
Dependent Claim
62 words
The highly heat-resistant fibers of claim 5, wherein said phosphorous compound is at least one member selected from the group consisting of orthophosphoric acid, pyrophosphoric acid, metaphosphoric acid, triphosphoric acid, tetraphosphoric acid, and MH 2 PO 4 , M 2 HPO 4 , and M 3 PO 4 wherein M is selected from the group consisting of alkali metals and ammonium ion.
Claim 10
Dependent Claim
54 words
The highly heat-resistant fibers of claim 5, wherein the amount of said phosphorous compound incorporated in said ceramic fibers is within the range of 1 to 6% by weight computed as P 2 O 5 and the thermal contraction under load is not more than 5% by weight at a temperature of 1400° C.
Claim 11
Dependent Claim
116 words
Highly heat-resistant fibers possessing a thermal contraction under load of not more than 10% at a temperature of 1400° C., comprising: ceramic fibers composed predominately of silica and alumina each present in the fibers in an amount of at least 25% by weight and a combined amount of at least 80% by weight, and a phosphorous compound incorporated into the ceramic fibers in an amount of from 0.5 to 10% by weight computed as P 2 O 5 , said ceramic fibers having a structure such that they are formed of crystals of a substantially uniform diameter of not more than 500 A throughout the entire depth of each fiber from the surface to the core.
Claim 12
Dependent Claim
116 words
Highly heat-resistant fibers possessing a thermal contraction under load of not more than 10% at a temperature of 1400° C., comprising: ceramic fibers composed predominately of silica and alumina each present in the fibers in an amount of at least 25% by weight and a combined amount of at least 80% by weight, and a phosphorous compound incorporated into the ceramic fibers in an amount of from 0.5 to 10% by weight computed as P 2 O 5 , said ceramic fibers having a structure such that they are formed of crystals of a substantially uniform diameter of not more than 500 A throughout the entire depth of each fiber from the surface to the core.
Claim 13
Dependent Claim
31 words
The heat-resistance fibers of claim 9, wherein said ceramic fibers are composed predominantly of silica and alumina in respective amounts of 30 to 50% and from 50 to 70% by weight.
Claim 14
Dependent Claim
60 words
The heat-resistant fibers of claim 9, wherein said phosphorous compound is at least one member selected from the group consisting of orthophosphoric acid, pyrophosphoric acid, metaphosphoric acid, triphosphoric acid, tetraphosphoric acid, and MH 2 PO 4 , M 2 HPO 4 and M 3 PO 4 wherein M is selected from the group consisting of alkali metals and ammonium ion.
Claim 15
Dependent Claim
50 words
The heat-resistant fibers of claim 9, wherein the amount of said phosphorous compound incorporated in the ceramic fibers ranges from 1 to 6% by weight computed as P 2 O 5 and the thermal contraction under load is not more than 5% by weight at a temperature of 1400° C.
Claim 16
Independent Claim
82 words
A method for preparing highly heat-resistant fibers possessing a thermal contraction under load of not more than 10% at a temperature of 1400° C., comprising: coating the surface of ceramic fibers containing silica and alumina each in an amount of at least 25 wt.% with a phosphorous-containing compound such that said fibers are coated with from 0.5 to 10% by weight of said phosphorous-containing compound; drying said coated fibers; and heat-treating said coated fibers to a temperature of at least 600° C.
Claim 17
Independent Claim
82 words
A method for preparing highly heat-resistant fibers possessing a thermal contraction under load of not more than 10% at a temperature of 1400° C., comprising: coating the surface of ceramic fibers containing silica and alumina each in an amount of at least 25 wt.% with a phosphorous-containing compound such that said fibers are coated with from 0.5 to 10% by weight of said phosphorous-containing compound; drying said coated fibers; and heat-treating said coated fibers to a temperature of at least 600° C.
Claim 18
Dependent Claim
19 words
The method of claim 1, wherein said heat treatment is conducted at a temperature of at least 1000° C.
Claim 19
Dependent Claim
26 words
The method of claim 13, wherein the ceramic fibers are composed predominately of silica and alumina in a combined amount of at least 80% by weight.
Claim 20
Dependent Claim
32 words
The method of claim 13, wherein the ceramic fibers are composed predominately of silica and alumina in substantially equal amounts and in a combined amount of not less than 80% by weight.
Claim 21
Dependent Claim
42 words
The method of claim 13, wherein the ceramic fibers are composed predominately of silica and alumina in respective amounts ranging from 30 to 50% and from 50 to 70% by weight and in a combined amount of at least 80% by weight.
Claim 22
Dependent Claim
59 words
The method of claim 13, wherein the phosphorous compound is at least one member selected from the group consisting of orthophosphoric acid, pyrophosphoric acid, metaphosphoric acid, triphosphoric acid, tetraphosphoric acid, and MH 2 PO 4 , M 2 HPO 4 and M 3 PO 4 wherein M is selected from the group consisting of alkali metals and ammonium ion.
Claim 23
Dependent Claim
47 words
The method of claim 13, wherein the amount of the phosphorous compound incorporated into the ceramic fibers ranges from 0.5 to 10% by weight computed as P 2 O 5 and the thermal contraction under load is not more than 10% at a temperature of 1400° C.
Claim 24
Dependent Claim
49 words
The method of claim 13, wherein the amount of the phosphorous compound incorporated into the ceramic fibers ranges from 1 to 6% by weight computed as P 2 O 5 and the thermal contraction under load is not more than 5% by weight at a temperature of 1400° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-25 | 1983-09-24 | 1984-03-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-25 | 1987-09-24 | 1988-03-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-25 | 1991-09-24 | 1992-03-25 | $7700.00 | Window Closed / Lapsed |