Hydrocracking of hydrocarbons
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1978-10-30
•
Granted: 1980-03-11
•
Expires: 1998-10-30
Abstract
Abstract A catalytic hydrocracking process for a hydrocarbonaceous oil is effected by dispersing a thermally decomposable metal compound in the oil, heating the compound in the presence of a hydrogen-containing gas to form a solid, non-colloidal catalyst within the oil and reacting the oil containing the catalyst with hydrogen. Preferred thermally decomposable compound are molybdenum compounds.
Inventors
- 👤 Clyde L. Aldridge
- 👤 Roby Bearden, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:21
CPC Classifications
B; B01; B01J; B01J37/00; C; C10; C10G; C10G47/00; C10G47/24; C10G47/26
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
173 words
A process for hydrocracking a hydrocarbon oil chargestock having a Conradson carbon content of less than about 5 weight percent, which comprises: (a) adding to said chargestock a thermally decomposable metal compound in an amount ranging from about 25 to about 950 weight parts per million, calculated as the elemental metal, based on said oil chargestock, said metal being selected from the group consisting of Groups IVB, VB, VIB, VIIB and VIII of the Periodic Table of Elements and mixtures thereof; (b) heating said thermally decomposable metal compound within said chargestock in the presence of a gas selected from the group consisting of a hydrogen-containing gas, a hydrogen sulfide-containing gas, and a gas comprising hydrogen and hydrogen sulfide, to produce a solid, non-colloidal catalyst within said chargestock, said solid catalyst comprising from about 25 to about 950 wppm of said metal, calculated as the elemental metal, based on said chargestock; (c) reacting the chargestock containing said catalyst with hydrogen under hydrocracking conditions, in a hydrocracking zone, and (d) recovering a hydrocracked hydrocarbon oil.
Claim 2
Dependent Claim
173 words
A process for hydrocracking a hydrocarbon oil chargestock having a Conradson carbon content of less than about 5 weight percent, which comprises: (a) adding to said chargestock a thermally decomposable metal compound in an amount ranging from about 25 to about 950 weight parts per million, calculated as the elemental metal, based on said oil chargestock, said metal being selected from the group consisting of Groups IVB, VB, VIB, VIIB and VIII of the Periodic Table of Elements and mixtures thereof; (b) heating said thermally decomposable metal compound within said chargestock in the presence of a gas selected from the group consisting of a hydrogen-containing gas, a hydrogen sulfide-containing gas, and a gas comprising hydrogen and hydrogen sulfide, to produce a solid, non-colloidal catalyst within said chargestock, said solid catalyst comprising from about 25 to about 950 wppm of said metal, calculated as the elemental metal, based on said chargestock; (c) reacting the chargestock containing said catalyst with hydrogen under hydrocracking conditions, in a hydrocracking zone, and (d) recovering a hydrocracked hydrocarbon oil.
Claim 3
Dependent Claim
32 words
The process of claim 1 wherein said thermally decomposable metal compound is selected from the group consisting of inorganic metal compounds, salts of organic acids, organometallic compounds and salts of organic amines.
Claim 4
Dependent Claim
31 words
The process of claim 1 wherein said thermally decomposable metal compound is selected from the group consisting of salts of acyclic aliphatic carboxylic acids and salts of alicyclic aliphatic carboxylic acids.
Claim 5
Dependent Claim
18 words
The process of claim 1 wherein said thermally decomposable metal compound is a salt of a naphthenic acid.
Claim 6
Dependent Claim
26 words
The process of claim 1 wherein the metal constituent of said thermally decomposable metal compound is selected from the group consisting of molybdenum, chromium and vanadium.
Claim 7
Dependent Claim
14 words
The process of claim 1 wherein said thermally decomposable metal compound is molybdenum naphthenate.
Claim 8
Dependent Claim
14 words
The process of claim 1 wherein said thermally decomposable metal compound is phosphomolybdic acid.
Claim 9
Dependent Claim
15 words
The process of claim 1 wherein said gas of step (b) is a hydrogen-containing gas.
Claim 10
Dependent Claim
16 words
The process of claim 1 wherein said gas of step (b) is a hydrogen sulfide-containing gas.
Claim 11
Dependent Claim
19 words
The process of claim 1 wherein said gas of step (b) is a gas comprising hydrogen and hydrogen sulfide.
Claim 12
Dependent Claim
21 words
The process of claim 10 wherein said gas of step (b) comprises from about 1 to 90 mole percent hydrogen sulfide.
Claim 13
Dependent Claim
22 words
The process of claim 10 wherein said hydrogen-containing gas of step (b) comprises from about 1 to 10 mole percent hydrogen sulfide.
Claim 14
Dependent Claim
70 words
The process of claim 1 wherein said thermally decomposable metal compound is converted to said solid non-colloidal catalyst by first heating the oil chargestock containing the added thermally decomposable metal compound to a temperature ranging from about 325° C. to about 415° C. in the presence of said gas to form a catalyst within said oil chargestock and subsequently reacting the oil containing said catalyst with hydrogen under hydrocracking conditions.
Claim 15
Dependent Claim
29 words
The process of claim 13 wherein said thermally decomposable metal compound is converted to said solid, non-colloidal catalyst in the presence of a gas comprising hydrogen and hydrogen sulfide.
Claim 16
Dependent Claim
46 words
The process of claim 1 wherein said thermally decomposable metal compound is converted to said solid non-colloidal catalyst in the presence of a hydrogen-containing gas under hydrocracking conditions thereby forming said catalyst in situ in said oil in said hydrocracking zone and producing a hydrocracked oil.
Claim 17
Dependent Claim
31 words
The process of claim 1 wherein said hydrocracking conditions include a temperature ranging from about 700° to 1000° F. and a total pressure ranging from about 500 to about 5000 psig.
Claim 18
Dependent Claim
52 words
The process of claim 1 wherein the reaction product resulting from step (c) comprises a hydrocracked oil containing solids, the additional steps which comprise separating at least a portion of said solids from said hydrocracked oil and recycling at least a portion of said solids to step (a) or to step (c).
Claim 19
Dependent Claim
16 words
The process of claim 1 wherein said catalyst is the sole catalyst in said hydrocracking zone.
Claim 20
Dependent Claim
26 words
The process of claim 1 wherein said hydrocarbon oil chargestock has an atmospheric pressure boiling point in the range of about 430° F. to 1100° F.
Claim 21
Dependent Claim
25 words
The process of claim 1 wherein said hydrocarbon oil chargestock has an atmospheric pressure boiling point ranging from about 650° F. to about 1050° F.
Claim 22
Dependent Claim
139 words
A process for hydrocracking a hydrocarbon oil chargestock having a Conradson carbon content of less than about 5 wt. %, which comprises: (a) adding to said oil chargestock a thermally decomposable molybdenum compound in an amount ranging from about 25 to about 950 weight parts per million, calculated as elemental molybdenum, based on said oil chargestock; (b) converting said molybdenum compound to a solid, non-colloidal catalyst in situ within said chargestock by reacting the resulting dispersion with a hydrogen-containing gas in a hydrocracking zone under hydrocracking conditions including a temperature ranging from about 800° to 900° F. and a total pressure ranging from about 500 psig to about 3000 psig, said solid catalyst comprising from about 25 to about 950 wppm of said molybdenum, calculated as the elemental metal, based on said chargestock; and (c) recovering a hydrocracked oil.
Claim 23
Dependent Claim
139 words
A process for hydrocracking a hydrocarbon oil chargestock having a Conradson carbon content of less than about 5 wt. %, which comprises: (a) adding to said oil chargestock a thermally decomposable molybdenum compound in an amount ranging from about 25 to about 950 weight parts per million, calculated as elemental molybdenum, based on said oil chargestock; (b) converting said molybdenum compound to a solid, non-colloidal catalyst in situ within said chargestock by reacting the resulting dispersion with a hydrogen-containing gas in a hydrocracking zone under hydrocracking conditions including a temperature ranging from about 800° to 900° F. and a total pressure ranging from about 500 psig to about 3000 psig, said solid catalyst comprising from about 25 to about 950 wppm of said molybdenum, calculated as the elemental metal, based on said chargestock; and (c) recovering a hydrocracked oil.
Claim 24
Dependent Claim
20 words
The process of claim 21 wherein said hydrogen-containing gas comprises from about 2 to about 7 mole percent hydrogen sulfide.
Claim 25
Dependent Claim
52 words
In the process of claim 21 wherein the effluent of said hydrocracking zone comprises a hydrocracked oil and solids, the improvement which comprises the additional steps of separating at least a portion of said solids from said effluent and recycling at least a portion of the separated solids to said hydrocracking zone.
Claim 26
Dependent Claim
23 words
The process of claim 1 or 21 wherein said hydrocarbon oil chargestock has a Conradson content of less than about 2 weight percent.
References Cited (Backward Citations)
US1876270A
Cited
US2091831A
Cited
US3131142A
Cited
US3161585A
Cited
US3338820A
Cited
US4125455A
Cited
US4134825A
Cited
US4090943A
Cited
US4136013A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-11 | 1983-09-10 | 1984-03-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-11 | 1987-09-10 | 1988-03-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-11 | 1991-09-10 | 1992-03-11 | $7700.00 | Window Closed / Lapsed |