Powder intended for powder metallurgical manufacturing of soft magnetic components
Assignee: Hoganas AB
•
Filing: 1978-03-02
•
Granted: 1980-02-26
•
Expires: 1998-03-02
Abstract
Abstract An improved composition, for the powder metallurgical manufacture by sintering of soft magnetic components which consists essentially of powdered iron and phosphorus. Phosphorus is present in an amount of up to about 1.5% by weight of the composition. The improvement comprises powdered iron at least about 99.8% pure and containing less than about 5% by weight of particles exceeding 35 Tyler mesh (417 μm) and less than about 20% by weight of particles less than 100 Tyler mesh (147 μm), the remainder of the particles being in the range between about 35 and 100 Tyler mesh (417 and 147 μm). The phosphorus content and iron particle size distribution is such that on sintering the composition provides components of satisfactory mechanical strength and having soft magnetic properties about as good as or better than the soft magnetic properties of components made of solid iron of comparable purity.
Inventors
- 👤 Jan R. Tengzelius
- 👤 Robert R. Fayles
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:38
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0207; C22C33/0214; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/20
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
151 words
In an improved composition, for the powder metallurgical manufacture by sintering of soft magnetic components which consists essentially of powdered iron and phosphorus, the latter being present in an amount of up to about 1.5% by weight of said composition, the improvement which comprises: said powdered iron being at least about 99.8% pure and containing less than about 5% by weight of particles exceeding 35 Tyler mesh (417 μm) and less than about 20% by weight of particles less than 100 Tyler mesh (147 μm), the remainder of the particles being in the range between about 35 and 100 Tyler mesh (417 and 147 μm), said phosphorus content and iron particle size distribution being such that on sintering said composition provides components of satisfactory mechanical strength and having soft magnetic properties about as good as or better than the soft magnetic properties of components made of solid iron of comparable purity.
Claim 2
Dependent Claim
151 words
In an improved composition, for the powder metallurgical manufacture by sintering of soft magnetic components which consists essentially of powdered iron and phosphorus, the latter being present in an amount of up to about 1.5% by weight of said composition, the improvement which comprises: said powdered iron being at least about 99.8% pure and containing less than about 5% by weight of particles exceeding 35 Tyler mesh (417 μm) and less than about 20% by weight of particles less than 100 Tyler mesh (147 μm), the remainder of the particles being in the range between about 35 and 100 Tyler mesh (417 and 147 μm), said phosphorus content and iron particle size distribution being such that on sintering said composition provides components of satisfactory mechanical strength and having soft magnetic properties about as good as or better than the soft magnetic properties of components made of solid iron of comparable purity.
Claim 3
Dependent Claim
28 words
A composition according to claim 1 wherein the iron contains less than about 0.01% carbon, less than about 0.1% oxygen, and less than about 0.005% nitrogen, by weight.
Claim 4
Dependent Claim
25 words
A composition according to claim 2 wherein the phosphorus content is in the range from about 0.15 to about 1.5% by weight of the composition.
Claim 5
Dependent Claim
26 words
A composition according to claim 3 wherein the iron powder contains less than about 10% by weight of particles less than 100 Tyler mesh (147 μm).
Claim 6
Dependent Claim
18 words
A composition according to claim 4 wherein the phosphorus content is about 1% by weight of the composition.
Claim 7
Dependent Claim
33 words
A composition according to claim 1 wherein the phosphorus is added in the form of ferrophosphorus powder containing about 15% phosphorus by weight and having a particle size less than about 45 μm.
Claim 8
Dependent Claim
28 words
A composition according to claim 6 wherein the iron contains less than about 0.01% carbon, less than about 0.1% oxygen, and less than about 0.005% nitrogen, by weight.
Claim 9
Dependent Claim
25 words
A composition according to claim 7 wherein the phosphorus content is in the range from about 0.15% to about 1.5% by weight of the composition.
Claim 10
Dependent Claim
26 words
A composition according to claim 8 wherein the iron powder contains less than about 10% by weight of particles less than 100 Tyler mesh (147 μm).
Claim 11
Dependent Claim
18 words
A composition according to claim 9 wherein the phosphorus content is about 1% by weight of the composition.
References Cited (Backward Citations)
US3836355A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-25 | 1983-08-27 | 1984-02-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-25 | 1987-08-27 | 1988-02-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-25 | 1991-08-27 | 1992-02-26 | $7700.00 | Window Closed / Lapsed |