US4189332A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Vapor treatment of metal tire cord
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1978-10-10
•
Granted: 1980-02-19
•
Expires: 1998-10-10
Abstract
Abstract Brass coated steel tire cord is treated with vaporized benzotriazole and/or other treatment agents to promote corrosion resistance and cord to rubber adhesion retention.
Inventors
- 👤 Grover W. Rye
- 👤 Karol Marencak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 18:48
CPC Classifications
C; C23; C23C; C23C8/00; C23C8/80; C23C8/06; C23C8/08; C23C8/10; D; D07; D07B; D07B1/00; D07B1/06; D07B1/0606; D07B1/0666; D07B2201/00; D07B2201/20; D07B2201/2001; D07B2201/201; D07B2201/2011; D07B2201/2012; D07B2201/2013; D07B2205/00; D07B2205/30; D07B2205/3021; D07B2205/3085; D07B2205/3089; Y; Y10; Y10S; Y10S156/00; Y10S156/91; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294; Y10T428/2942; Y10T428/2944; Y10T428/2945
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
114 words
In a process of treating a filament of steel having a brass coating thereon with a reagent reactive with the brass and/or any exposed surface of the steel filament, the improvement characterized by (A) continuously passing a steel filament having a microscopically porous brass coating thereon through the vapors of molten benzotriazole and (B) subjecting the treated filament to a water vapor treatment; wherein said benzotriazole vapor is heated to a temperature of up to about 180° C., to form primarily a monomolecular coating on said filament so as to promote both corrosion resistance to said filament and aged adhesion between a cord thereof of such stranded filaments and adjacent, adherent sulfur vulcanized rubber.
Claim 2
Dependent Claim
114 words
In a process of treating a filament of steel having a brass coating thereon with a reagent reactive with the brass and/or any exposed surface of the steel filament, the improvement characterized by (A) continuously passing a steel filament having a microscopically porous brass coating thereon through the vapors of molten benzotriazole and (B) subjecting the treated filament to a water vapor treatment; wherein said benzotriazole vapor is heated to a temperature of up to about 180° C., to form primarily a monomolecular coating on said filament so as to promote both corrosion resistance to said filament and aged adhesion between a cord thereof of such stranded filaments and adjacent, adherent sulfur vulcanized rubber.
Claim 3
Dependent Claim
117 words
In a process of treating a stranded cord comprised of filaments of steel having a brass coating thereon with a reagent reactive with the brass and/or exposed surface of the steel filaments, the improvement characterized by (A) continually passing a cord of stranded steel filaments having a microscopically porous brass coating thereon through the vapors of molten benzothiazole and (B) subjecting the treated stranded cord to a water vapor treatment; wherein said benzotriazole vapor is heated to a temperature of up to about 180° C., to form primarily a monomolecular coating on the filaments of said cord so as to promote both corrosion resistance thereto and aged adhesion between said cord and an adherent sulfur vulcanized rubber.
Claim 4
Dependent Claim
117 words
In a process of treating a stranded cord comprised of filaments of steel having a brass coating thereon with a reagent reactive with the brass and/or exposed surface of the steel filaments, the improvement characterized by (A) continually passing a cord of stranded steel filaments having a microscopically porous brass coating thereon through the vapors of molten benzothiazole and (B) subjecting the treated stranded cord to a water vapor treatment; wherein said benzotriazole vapor is heated to a temperature of up to about 180° C., to form primarily a monomolecular coating on the filaments of said cord so as to promote both corrosion resistance thereto and aged adhesion between said cord and an adherent sulfur vulcanized rubber.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-18 | 1983-08-20 | 1984-02-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-18 | 1987-08-20 | 1988-02-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-18 | 1991-08-20 | 1992-02-19 | $7700.00 | Window Closed / Lapsed |