Controlled permeation process for fireproofing wood
Assignee: KORNDORFFER JAMES R
•
Filing: 1978-08-22
•
Granted: 1980-02-05
•
Expires: 1998-08-22
Abstract
Abstract Fireproofing of wood and the variety of hardwoods typically utilized in the manufacture of furniture is provided by a process of controlled permeation of a solution composed of a combination of a halide salt of a Group I or Group II metal of the Periodic Table of Elements and an ammonium salt which upon impregnation precipitates in the cellular structure of the treated wood. Controlled permeation of furniture wood to a depth of about 1/8 of an inch to 3 inches is provided by evacuating and expanding the cellular structure of the wood by utilizing a vacuum chamber, or a heat chamber for heating the wood to temperatures of about 220° F. or a combination thereof to activate the surface and a portion of the subsurface of the cellular structure of the wood for absorption and adsorption of the solution of fire retardant compounds providing a controlled impregnation of the furniture hardwood. Fire retardant compounds drawn into the surface and subsurface structure of the wood may then be sealed into the furniture wood by utilizing traditional furniture finishing procedures.
Inventors
- 👤 George W. Jarrett
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 01:01
CPC Classifications
B; B27; B27K; B27K3/00; B27K3/16; B27K3/32; B27K3/02; B27K3/0207; B27K3/0214; B27K5/00; B27K5/001; B27K2240/00; B27K2240/30; B27K3/08; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10S428/921; Y10T; Y10T428/00; Y10T428/27; Y10T428/273; Y10T428/277; Y10T428/31504; Y10T428/31971; Y10T428/31989
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
220 words
A process for fireproofing and strengthening wood by employing controlled permeation of a fire retardant compound in the cellular structure of a wood comprising: (a) evacuating and expanding the cellular structure of a wood by utilizing a sufficient amount of dry heat, vacuum or a combination thereof to activate the cellular structure of said wood for receiving a fire retardant solution to a depth of about 1% to 40% of the thickness of the treated wood; (b) immersing said evacuated and expanded cellular structure of said wood in a fire retardant solution composed of a combination of a halide salt of a Group I or Group II metal and an ammonium salt to provide a reaction between said halide salt and said ammonium salt and deposit a reaction product in said cellular structure of said wood; (c) dissipating said dry heat, vacuum or combination thereof after said evacuated and expanded cellular structure of said wood is immersed in said fire retardant solution to draw said fire retardant solution into said wood and deposit said reaction product; and (d) drying said wood by exposing said wood to the atmosphere or drying in a kiln for about 15 minutes to 72 hours at a temperature of from about 100° F. to 175° F. or a combination of said atmospheric and kiln drying.
Claim 2
Dependent Claim
220 words
A process for fireproofing and strengthening wood by employing controlled permeation of a fire retardant compound in the cellular structure of a wood comprising: (a) evacuating and expanding the cellular structure of a wood by utilizing a sufficient amount of dry heat, vacuum or a combination thereof to activate the cellular structure of said wood for receiving a fire retardant solution to a depth of about 1% to 40% of the thickness of the treated wood; (b) immersing said evacuated and expanded cellular structure of said wood in a fire retardant solution composed of a combination of a halide salt of a Group I or Group II metal and an ammonium salt to provide a reaction between said halide salt and said ammonium salt and deposit a reaction product in said cellular structure of said wood; (c) dissipating said dry heat, vacuum or combination thereof after said evacuated and expanded cellular structure of said wood is immersed in said fire retardant solution to draw said fire retardant solution into said wood and deposit said reaction product; and (d) drying said wood by exposing said wood to the atmosphere or drying in a kiln for about 15 minutes to 72 hours at a temperature of from about 100° F. to 175° F. or a combination of said atmospheric and kiln drying.
Claim 3
Dependent Claim
44 words
The process of claim 1 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood additionally comprising the step of sealing said fire retardant compound into said wood utilizing furniture finishing techniques.
Claim 4
Dependent Claim
54 words
The process of claim 1 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said evacuating and expanding of said cellular structure of said wood is accomplished by utilizing a vacuum pressure of about 20 to 30 inches of mercury.
Claim 5
Dependent Claim
54 words
The process of claim 3 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said vacuum is maintained for a period of about 1 to 4 hours prior to immersing said wood in a solution of said fire retardant compound.
Claim 6
Dependent Claim
56 words
The process of claim 4 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said evacuated and expanded cellular structure of said wood is covered with said treating solution at a temperature in the range of about 80° F. to 200° F.
Claim 7
Dependent Claim
51 words
The process of claim 5 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said vacuum is maintained for a period of about 5 to 10 minutes after said wood is immersed in said fire retardant solution.
Claim 8
Dependent Claim
49 words
The process of claim 3 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said halide salt of a Group I or Group II metal is sodium chloride and said ammonium salt is ammonium sulfate.
Claim 9
Dependent Claim
57 words
The process of claim 7 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said cellular structure of said wood is activated for receiving said fire retardant solution to a depth of about 2% to 30% of the thickness of the treated wood.
Claim 10
Dependent Claim
61 words
The process of claim 8 for fireproofing and strengthening wood by controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said wood is a softwood and said cellular structure of said softwood is activated for receiving said fire retardant solution to a depth of about 10% to 35% of the thickness of the treated wood.
Claim 11
Dependent Claim
61 words
The process of claim 8 for fireproofing and strengthening wood by controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said wood is a hardwood and said cellular structure of said hardwood is activated for receiving said fire retardant solution to a depth of about 1% to 25% of the thickness of the treated wood.
Claim 12
Dependent Claim
53 words
The process of claim 8 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood further comprising the step of sealing said fire retardant compound in said cellular structure of the wood by immersing said treated wood in furniture finishing compounds.
Claim 13
Dependent Claim
69 words
The process of claim 1 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said controlled permeation is achieved by utilizing dry heat to heat said wood to a temperature of about 200° F. to 250° F. for a period of about 1 to 5 hours before immersing said wood in said fire retardant solution.
Claim 14
Dependent Claim
49 words
The process of claim 12 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said halide salt of a Group I or Group II metal is sodium chloride and said ammonium salt is ammonium sulfate.
Claim 15
Dependent Claim
55 words
The process of claim 13 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said evacuated and expanded cellular structure of said wood is immersed in said fire retardant solution maintained at a temperature of about 50° F. to 100° F.
Claim 16
Dependent Claim
43 words
The process of claim 14 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said salt solution of sodium chloride and ammonium sulfate is dissolved in furniture finishing oil.
Claim 17
Dependent Claim
46 words
The process of claim 14 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said combined salt solution is about 7% by weight sodium chloride and about 15% by weight ammonium sulfate.
Claim 18
Dependent Claim
40 words
The process of claim 12 for fireproofing and strengthening wood by employing a controlled permeation of a fire retardant compound into the cellular structure of a wood further comprising the step of finishing said wood by employing furniture finishing techniques.
Claim 19
Dependent Claim
9 words
The product produced by the process of claim 1.
Claim 20
Dependent Claim
216 words
A process for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood comprising: (a) evacuating and expanding the cellular structure of a wood by utilizing a vacuum in the range of about 20 to 30 inches of mercury for a period of about 30 minutes to 4 hours to activate the surface and a portion of the subsurface of said wood to receive a fire retardant solution to a depth of less than to the core of the wood and in the range of about 1/16 to 4 inches; (b) covering said evacuated and expanded cellular structure of said wood with a fire retardant solution wherein said fire retardant solution comprises a combination of ammonium sulfate and a halide of a Group I or Group II metal of the Periodic Table of Elements; (c) releasing said vacuum after said wood is covered with said treating solution; (d) drying said wood by exposure to the atmosphere or drying said wood in a kiln for about 15 minutes to 72 hours at a temperature of from about 100° F. to 175° F. or a combination of said atmospheric and kiln drying; and (e) sealing said fire retardant compound into the cellular structure of the wood by employing furniture finishing techniques.
Claim 21
Dependent Claim
216 words
A process for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood comprising: (a) evacuating and expanding the cellular structure of a wood by utilizing a vacuum in the range of about 20 to 30 inches of mercury for a period of about 30 minutes to 4 hours to activate the surface and a portion of the subsurface of said wood to receive a fire retardant solution to a depth of less than to the core of the wood and in the range of about 1/16 to 4 inches; (b) covering said evacuated and expanded cellular structure of said wood with a fire retardant solution wherein said fire retardant solution comprises a combination of ammonium sulfate and a halide of a Group I or Group II metal of the Periodic Table of Elements; (c) releasing said vacuum after said wood is covered with said treating solution; (d) drying said wood by exposure to the atmosphere or drying said wood in a kiln for about 15 minutes to 72 hours at a temperature of from about 100° F. to 175° F. or a combination of said atmospheric and kiln drying; and (e) sealing said fire retardant compound into the cellular structure of the wood by employing furniture finishing techniques.
Claim 22
Dependent Claim
53 words
The process of claim 19 for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said fire retardant solution comprises a combination of ammonium sulfate and a chloride salt of a metal selected from the group of metals consisting of sodium, calcium and potassium.
Claim 23
Dependent Claim
39 words
The process of claim 20 for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said fire retardant solution has furniture oil as at least a part of the solvent.
Claim 24
Dependent Claim
37 words
The process of claim 19 for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said fire retardant solution is a combination of sodium chloride and ammonium sulfate.
Claim 25
Dependent Claim
41 words
The process of claim 21 for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of the wood wherein said fire retardant solution is introduced into the vacuum chamber at about 100° F. to 200° F.
Claim 26
Dependent Claim
49 words
The process of claim 23 for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said wood is a softwood having a thickness of about 6 to 10 inches and said depth of penetration is about 2 to 3 inches.
Claim 27
Dependent Claim
49 words
The process of claim 23 for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said wood is a hardwood having a thickness of about 1 to 4 inches and said depth of penetration is about 1/16 to 1 inch.
Claim 28
Dependent Claim
50 words
The process of claim 19 for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood further comprises the step of utilizing a second vacuum pressure of about 16 to 18 inches of mercury to remove excessive fire retardant solution from treated parts.
Claim 29
Dependent Claim
9 words
The product produced by the process of claim 19.
Claim 30
Dependent Claim
218 words
A process for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood comprising: (a) evacuating and expanding the cellular structure of a wood by utilizing dry heat in the temperature range of about 200° F. to 260° F. for a period of about 1 to 4 hours to activate the surface and a portion of the subsurface of said wood to receive a fire retardant solution to a depth of less than to the core of the wood and in a range of about 1/16 to 4 inches; (b) covering said evacuated and expanded cellular structure of said wood with a fire retardant solution wherein said fire retardant solution comprises a combination of ammonium sulfate and a halide of a Group I or Group II metal of the Periodic Table of Elements; (c) dissipating said dry heat as said wood is immersed in said fire retardant solution; (d) drying said wood by exposure to the atmosphere or drying said wood in a kiln for about 15 minutes to 72 hours at a temperature of from about 100° F. to 175° F. or a combination of said atmospheric and kiln drying; and (e) sealing said fire retardant compound into the cellular structure of the wood by employing ordinary furniture finishing techniques.
Claim 31
Dependent Claim
218 words
A process for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood comprising: (a) evacuating and expanding the cellular structure of a wood by utilizing dry heat in the temperature range of about 200° F. to 260° F. for a period of about 1 to 4 hours to activate the surface and a portion of the subsurface of said wood to receive a fire retardant solution to a depth of less than to the core of the wood and in a range of about 1/16 to 4 inches; (b) covering said evacuated and expanded cellular structure of said wood with a fire retardant solution wherein said fire retardant solution comprises a combination of ammonium sulfate and a halide of a Group I or Group II metal of the Periodic Table of Elements; (c) dissipating said dry heat as said wood is immersed in said fire retardant solution; (d) drying said wood by exposure to the atmosphere or drying said wood in a kiln for about 15 minutes to 72 hours at a temperature of from about 100° F. to 175° F. or a combination of said atmospheric and kiln drying; and (e) sealing said fire retardant compound into the cellular structure of the wood by employing ordinary furniture finishing techniques.
Claim 32
Dependent Claim
53 words
The process of claim 28 for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said fire retardant solution comprises a combination of ammonium sulfate and a chloride salt of a metal selected from the group of metals consisting of sodium calcium and potassium.
Claim 33
Dependent Claim
39 words
The process of claim 29 for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said fire retardant solution has furniture oil as at least a part of the solvent.
Claim 34
Dependent Claim
37 words
The process of claim 28 for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said fire retardant solution is a combination of sodium chloride and ammonium sulfate.
Claim 35
Dependent Claim
52 words
The process of claim 28 for fireproofing wood by controlled permeation of a fire retardant compound into the cellular structure of a wood wherein said fire retardant solution is in a temperature range of about 50° F. to 100° F. prior to covering said evacuated and expanded cellular structure of said wood.
Claim 36
Dependent Claim
9 words
The product produced by the process of claim 29.
References Cited (Backward Citations)
US1702285A
Cited
US691812A
Cited
US2838424A
Cited
US3968276A
Cited
US4062991A
Cited
DE2363097A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-04 | 1983-08-06 | 1984-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-04 | 1987-08-06 | 1988-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-04 | 1991-08-06 | 1992-02-05 | $7700.00 | Window Closed / Lapsed |