Method for producing shaped glass fiber reinforced gypsum articles
Assignee: ROBERTSON-CECO Corp A DE CORP
•
Filing: 1976-02-27
•
Granted: 1980-02-05
•
Expires: 1996-02-27
Abstract
Abstract A method for forming shaped articles from glass fiber reinforced gypsum. An aqueous slurry of calcium sulfate hemihydrate, water and glass fibers contains between 22 and 45 parts by weight water, 100 parts by weight calcium sulfate hemihydrate and 3 to 10 parts by weight glass fiber. The slurry is provided as a continuous ribbon on a moving, water-impermeable first membrane. A water-impermeable second membrane is applied above the continuous ribbon and sealed along its side edges to the side edges of the first membrane to form a sandwich consisting of the two membranes and the slurry ribbon. The sandwich is shaped prior to the setting of the gypsum and is retained in the desired shape until initial setting occurs. Thereafter at least a portion of one of the two membranes is removed and substantially all of the uncombined water is removed from the shaped ribbon.
Inventors
- 👤 Glenn E. Kautz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 17:28
CPC Classifications
B; B28; B28B; B28B1/00; B28B1/52; B28B1/526
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
97 words
A method for forming glass fiber reinforced gypsum products comprising: 1. forming on a water impervious bottom membrane a ribbon comprising: 3-10 parts by weight glass fibers having an average length of 1/2 to 4 inches; 100 parts by weight calcium sulfate hemihydrate; 22-45 parts by weight water; 2. covering the said ribbon with a water impervious top membrane to form a sandwich consisting of two said membranes and the said ribbon; 3. removing entrapped gases from the space between the two said membranes; 4. shaping the said sandwich prior to the setting of the said ribbon;
Claim 2
Independent Claim
97 words
A method for forming glass fiber reinforced gypsum products comprising: 1. forming on a water impervious bottom membrane a ribbon comprising: 3-10 parts by weight glass fibers having an average length of 1/2 to 4 inches; 100 parts by weight calcium sulfate hemihydrate; 22-45 parts by weight water; 2. covering the said ribbon with a water impervious top membrane to form a sandwich consisting of two said membranes and the said ribbon; 3. removing entrapped gases from the space between the two said membranes; 4. shaping the said sandwich prior to the setting of the said ribbon;
Claim 3
Dependent Claim
37 words
setting the said ribbon prior to any deliberate water removal; 6. removing at least a portion of at least one said membrane after the ribbon has set and removing substantially all uncombined water from the said ribbon.
Claim 4
Dependent Claim
37 words
setting the said ribbon prior to any deliberate water removal; 6. removing at least a portion of at least one said membrane after the ribbon has set and removing substantially all uncombined water from the said ribbon.
Claim 5
Independent Claim
164 words
A method for forming glass fiber reinforced gypsum products comprising: 1. developing a spray of aqueous calcium sulfate hemihydrate slurry having a weight ratio of water to hemihydrate from 0.22 to 0.45; 2. developing a moving stream of glass fibers having an average length of 0.5 to 4.0 inches; 3. impinging said spray and said stream against each other to produce a slurry-wetted stream of glass fibers; 4. collecting said slurry-wetted stream as a ribbon on a water impervious bottom membrane; 5. covering said ribbon with a water impervious top membrane; 6. removing entrapped gases from the space between the two said membranes to produce a sandwich consisting of the two said membranes and the said ribbon; 7. shaping the said sandwich prior to setting of said ribbon; 8. setting the said ribbon prior to any deliberate water removal; 9. removing at least a portion of one said membrane after the ribbon has set and removing substantially all uncombined water from the said ribbon.
Claim 6
Independent Claim
164 words
A method for forming glass fiber reinforced gypsum products comprising: 1. developing a spray of aqueous calcium sulfate hemihydrate slurry having a weight ratio of water to hemihydrate from 0.22 to 0.45; 2. developing a moving stream of glass fibers having an average length of 0.5 to 4.0 inches; 3. impinging said spray and said stream against each other to produce a slurry-wetted stream of glass fibers; 4. collecting said slurry-wetted stream as a ribbon on a water impervious bottom membrane; 5. covering said ribbon with a water impervious top membrane; 6. removing entrapped gases from the space between the two said membranes to produce a sandwich consisting of the two said membranes and the said ribbon; 7. shaping the said sandwich prior to setting of said ribbon; 8. setting the said ribbon prior to any deliberate water removal; 9. removing at least a portion of one said membrane after the ribbon has set and removing substantially all uncombined water from the said ribbon.
Claim 7
Dependent Claim
28 words
The method of claim 1 including the additional step of continuously sealing the two membranes along each side of the said ribbon prior to shaping the said sandwich.
Claim 8
Dependent Claim
24 words
The method according to claim 1 wherein the said glass fibers comprise at least in part a preformed mat of randomly oriented glass fibers.
Claim 9
Dependent Claim
25 words
The method of claim 1 wherein the said ribbon has along at least one side edge a preformed ribbon mat of randomly oriented glass fibers.
Claim 10
Dependent Claim
23 words
The method of claim 1 wherein the said ribbon has along each side edge a ribbon mat of preformed randomly oriented glass fibers.
Claim 11
Dependent Claim
42 words
The method according to claim 1 wherein the said glass fibers are provided in part in the form of ribbon mats of randomly oriented glass fibers and at least in part of glass fibers randomly deposited on said water impervious bottom membrane.
References Cited (Backward Citations)
CA519920A
Cited
US2871134A
Cited
US2991824A
Cited
US3047447A
Cited
US3062670A
Cited
GB1204541A
Cited
US3616173A
Cited
US3964944A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-04 | 1983-08-06 | 1984-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-04 | 1987-08-06 | 1988-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-04 | 1991-08-06 | 1992-02-05 | $7700.00 | Window Closed / Lapsed |